A new method of adhesive system application improves the bond strength between fiber post and root dentin.

This study evaluated a new method of adhesive system application on the bond strength between fiber post and root dentin using two adhesive systems. The canals of sixty bovine incisors were prepared and obturated. The roots were divided into six groups (n=10) according to the adhesive system (Clearfil SE - CSE and Single Bond Universal - SBU) and the application strategy (microbrush - MB; rotary brush - RB; and ultrasonic tip - US). The glass fiber posts were cemented with resin cement (RelyX ARC). The roots were sectioned perpendicularly to their long axis, and three slices per root were obtained. Previously to the push-out test, confocal laser scanning microscopy (CLSM) was performed to illustrate the interfacial adaptation of the cement to the root canal walls. Failure patterns were analyzed with 40x magnification. Shapiro-Wilk indicated a normal distribution of the data. The bond strength values were compared using one-way ANOVA and Tukey's tests. Student's T test analyzed the differences between the adhesive systems within each third and protocol. A significance level of 5% was used. CSE with RB showed higher mean bond strength values compared to MB (conventional technique) (P < 0.05). US application resulted in intermediate bond strength values for CSE (P > 0.05). The application of SBU using RB generated higher mean bond strength values compared to MB and US (P < 0.05). Adhesive failures were predominant (65.5%). CSE and SBU application with the new rotary brush improved the bond strength of fiber posts to root dentin compared to the conventional strategy.

A new method of adhesive system application improves the bond strength between fiber post and root dentin

Abstract This study evaluated a new method of adhesive system application on the bond strength between fiber post and root dentin using two adhesive systems. The canals of sixty bovine incisors were prepared and obturated. The roots were divided into six groups (n=10) according to the adhesive system (Clearfil SE - CSE and Single Bond Universal - SBU) and the application strategy (microbrush - MB; rotary brush - RB; and ultrasonic tip - US). The glass fiber posts were cemented with resin cement (RelyX ARC). The roots were sectioned perpendicularly to their long axis, and three slices per root were obtained. Previously to the push-out test, confocal laser scanning microscopy (CLSM) was performed to illustrate the interfacial adaptation of the cement to the root canal walls. Failure patterns were analyzed with 40x magnification. Shapiro-Wilk indicated a normal distribution of the data. The bond strength values were compared using one-way ANOVA and Tukey's tests. Student's T test analyzed the differences between the adhesive systems within each third and protocol. A significance level of 5% was used. CSE with RB showed higher mean bond strength values compared to MB (conventional technique) (P < 0.05). US application resulted in intermediate bond strength values for CSE (P > 0.05). The application of SBU using RB generated higher mean bond strength values compared to MB and US (P < 0.05). Adhesive failures were predominant (65.5%). CSE and SBU application with the new rotary brush improved the bond strength of fiber posts to root dentin compared to the conventional strategy.

Resumo Este estudo avaliou o efeito de um novo método para aplicação do sistema adesivo na resistência de união entre pino de fibra e dentina radicular usando dois sistemas adesivos. Os canais de sessenta incisivos bovinos foram preparados e obturados. As raízes foram divididas em seis grupos (n=10) de acordo com o sistema adesivo (Clearfil SE - CSE e Single Bond Universal - SBU) e com a estratégia de aplicação (microbrush - MB, escova rotatória - RB e inserto ultrassônico - US). Os pinos de fibra foram cimentados utilizando cimento resinoso (RelyX ARC). As raízes foram seccionadas perpendicularmente ao seu longo eixo e três fatias foram obtidas. Previamente ao teste de push-out, foi realizada microscopia de varredura confocal a laser para ilustrar a adaptação interfacial do cimento às paredes do canal radicular. Os padrões de falha foram analisados com magnificação de 40x. O teste de Shapiro-Wilk indicou distribuição normal dos dados. Os valores de resistência de união foram comparados usando o teste ANOVA de uma via e post hoc de Tukey. As diferenças entre os sistemas adesivos em cada terço e de acordo com cada protocolo foram analisadas pelo teste T de Student. O nível de significância foi de 5%. CSE aplicado com RB apresentou maiores valores médios de resistência de união do que quando aplicado com MB (técnica convencional) (P<0,05). Aplicação com US apresentou valores intermediários de resistência de união para o CSE (P>0,05). A aplicação do SBU utilizando RB gerou maiores valores médios de resistência de união comparados com MB e US (P<0,05). Falhas adesivas foram predominantes (65,5%). A aplicação do CSE e SBU com a nova escova rotatória melhorou a resistência de união dos pinos de fibra à dentina radicular comparados com a estratégia convencional.

Effect of bioceramic root canal sealers on the bond strength of fiber posts cemented with resin cements.

This study aimed to evaluate the influence of calcium silicate-based sealers on the bond strength of fiber posts using conventional and self-adhesive resin cement. Sixty single-rooted teeth were selected. The canals were prepared with a reciprocating instrument 40.06. The roots were randomly distributed in six groups (n = 10) according to the strategies for root canal filling and fiber posts cementation: AH Plus/RelyX ARC; AH Plus/RelyX U200; Bio C Sealer/RelyX ARC; Bio C Sealer/RealyX U200; Sealer Plus BC/RelyX ARC; and Sealer Plus BC/RelyX U200. The roots were transversally sectioned, and one slice per post-third was obtained. The push-out test was performed at a crosshead speed of 1mm/min. The failure patterns were described after assessment with a stereomicroscope with a 10× magnification. Bond strength was calculated and analyzed using the ANOVA and Tukey test. AH Plus did not influence the bond strength of fiber posts cemented with conventional (RelyX ARC) or with self-adhesive resin cement (RelyX U200). The lowest bond strength values were obtained when calcium silicate-based sealers were associated with conventional resin cement (Bio C Sealer/RelyX ARC and Sealer Plus BC/RelyX ARC). Except for Sealer Plus BC/RelyX ARC, all groups presented lower bond strength at the apical portion compared to the cervical portion of the post. Adhesive failures between cement and post and cement and dentin were predominant (55.3%). Calcium silicate-based sealers decreased the bond strength of fiber posts cemented with conventional resin cement.

Effect of bioceramic root canal sealers on the bond strength of fiber posts cemented with resin cements

Abstract This study aimed to evaluate the influence of calcium silicate-based sealers on the bond strength of fiber posts using conventional and self-adhesive resin cement. Sixty single-rooted teeth were selected. The canals were prepared with a reciprocating instrument 40.06. The roots were randomly distributed in six groups (n = 10) according to the strategies for root canal filling and fiber posts cementation: AH Plus/RelyX ARC; AH Plus/RelyX U200; Bio C Sealer/RelyX ARC; Bio C Sealer/RealyX U200; Sealer Plus BC/RelyX ARC; and Sealer Plus BC/RelyX U200. The roots were transversally sectioned, and one slice per post-third was obtained. The push-out test was performed at a crosshead speed of 1mm/min. The failure patterns were described after assessment with a stereomicroscope with a 10× magnification. Bond strength was calculated and analyzed using the ANOVA and Tukey test. AH Plus did not influence the bond strength of fiber posts cemented with conventional (RelyX ARC) or with self-adhesive resin cement (RelyX U200). The lowest bond strength values were obtained when calcium silicate-based sealers were associated with conventional resin cement (Bio C Sealer/RelyX ARC and Sealer Plus BC/RelyX ARC). Except for Sealer Plus BC/RelyX ARC, all groups presented lower bond strength at the apical portion compared to the cervical portion of the post. Adhesive failures between cement and post and cement and dentin were predominant (55.3%). Calcium silicate-based sealers decreased the bond strength of fiber posts cemented with conventional resin cement.

Resumo Este estudo teve como objetivo avaliar a influência de cimentos à base de silicato de cálcio na resistência de união de pinos de fibra utilizando cimentos resinosos convencionais e autoadesivos. Sessenta dentes humanos monorradiculares foram selecionados. Os canais foram preparados um instrumento reciprocante 40.06. As raízes foram distribuídas aleatoriamente em seis grupos (n = 10) de acordo com as estratégias de obturação do canal e cimentação dos pinos de fibra: AH Plus/RelyX ARC; AH Plus/RelyX U200; Bio C Sealer/RelyX ARC; Bio C Sealer/RealyX U200; Sealer Plus BC/RelyX ARC; e Sealer Plus BC/RelyX U200. As raízes foram seccionadas transversalmente e foi obtido um espécime por terço. O teste de push-out foi realizado em uma velocidade de 1mm/min. Os padrões de falha foram descritos após avaliação em estereomicroscópio com aumento de 10×. A resistência de união foi calculada e analisada por ANOVA e teste de Tukey. AH Plus não influenciou na resistência de união dos pinos de fibra cimentados com cimento resinoso convencional (RelyX ARC) ou autoadesivo (RelyX U200) (p > 0,05). Os menores valores de resistência de união foram obtidos quando os cimentos à base de silicato de cálcio foram associados ao cimento resinoso convencional (Bio C Sealer/RelyX ARC e Sealer Plus BC/RelyX ARC) (p < 0,05). Com exceção do Sealer Plus BC/RelyX ARC, todos os grupos apresentaram menor resistência de união na porção apical em comparação com a porção cervical do pino (p < 0,05). Falhas adesivas entre cimento e pino e cimento e dentina foram predominantes (55,3%). Cimentos a base de silicato de cálcio diminuíram a resistência de união de pinos de fibra cimentados com cimento resinoso convencional.