RESUMO
The objective of this study was to introduce a functionally graded (FG) polymer-infiltrated ceramic network (PICN) block, characterized by a gradient of mechanical properties, as a biomimetic material for computer-aided design and manufacturing (CAD-CAM) prostheses. FG-PICN blocks were manufactured from a slurry of glass-ceramic powder, which was subsequently centrifuged and sintered. The ceramic network was infiltrated with urethane dimethacrylate and polymerized under high temperature-pressure. Blocks were sectioned into 9 layers, and each layer was subsequently cut into 3 samples. Samples were loaded into a 3-point bending device and tested for flexural strength, flexural load energy, and flexural modulus. The volume percentage of glass-ceramic, hardness, and brittleness index were also measured and scanning electron microscopy (SEM) observations were performed. Katana translucent zirconia (HT-ZIR) and e.max-CAD (EMX) were tested for comparison. Flexural strength, flexural load energy, and Weibull modulus of FG-PICN were shown to increase from the first (enamel-like zone) to the ninth layer (dentin-like zone), while, on the contrary, flexural modulus, hardness, brittleness index, and ceramic volume percentage decreased. SEM characterization highlighted a higher porosity in layer 9 than in layer 1. Flexural strength of the dentin-like zone (372.7 ± 27.8 MPa) was similar to EMX and lower than HT-ZIR. Flexural modulus was shown to vary from 41.9 ± 5.1 to 28.6 ± 2.0 GPa from surface to depth. Flexural load energy in the dentin-like zone (27.1 ± 4.9 mJ) was significantly superior to EMX and HT-ZIR. Hardness gradient was shown to be close to tooth tissues. This work introduces FG-PICN blocks, with a gradient of mechanical and optical properties through the entire thickness of the block designed to mimic dental tissues. FG-PICN demonstrated a favorable gradient of flexural strength, elastic modulus, and, most of all, flexural load energy and hardness compared to other CAD-CAM materials, which can promote the biomechanical behavior of single-unit restorations on teeth and implants.
Assuntos
Biomimética , Cerâmica/química , Desenho Assistido por Computador , Planejamento de Prótese Dentária , Polímeros/química , Módulo de Elasticidade , Resistência à Flexão , Dureza , Teste de Materiais , Metacrilatos/química , Microscopia Eletrônica de Varredura , Poliuretanos/química , Porosidade , Propriedades de SuperfícieRESUMO
The objective of this study was to evaluate the interfacial fracture toughness (IFT) of composite cement with dispersed filler (DF) versus polymer-infiltrated ceramic network (PICN) computer-aided design and computer-aided manufacturing (CAD-CAM) composite blocks after 2 different surface pretreatments using the notchless triangular prism (NTP) test. Two DFs (Cerasmart [CRT] and Lava Ultimate [LVA]), 2 PICNs (Enamic [ENA] and experimental PICN [EXP]), and e.max CAD lithium disilicate glass-ceramic (EMX, control) prism samples were bonded to their counterparts with Variolink Esthetic DC composite cement after either hydrofluoric acid etching (HF) or gritblasting (GR). Both procedures were followed by silanization. All samples ( n = 30 per group) were thermocycled (10,000 cycles) and tested for their IFT in a water bath at 36°C. Moreover, representative samples from each group were subjected to a developed interfacial area ratio (Sdr) measurement by profilometry and scanning electron microscopy (SEM) characterization. EXP-HF gave the highest IFT (1.85 ± 0.39 MPa·m1/2), followed by EMX-HF and ENA-HF, while CRT-HF gave the lowest (0.15 ± 0.22 MPa·m1/2). PICNs gave significantly better results with HF, and DF showed better results with GR. A 2-way analysis of variance indicated that there were significantly higher IFT and Sdr for PICNs than for DF. A positive correlation ( r² = 0.872) was found between IFT and Sdr. SEM characterization showed the specific microstructure of the surface of etched PICNs, indicating the presence of a retentive polymer-based honeycomb structure. Etching of the typical double-network microstructure of PICNs causes an important increase in the Sdr and IFT, while DF should be gritblasted. DF exhibited significantly lower Sdr and IFT values than PICNs. The present results show the important influence of the material class and surface texture, and consequently the micromechanical bond, on the adhesive interface performance of CAD-CAM composites.
Assuntos
Desenho Assistido por Computador , Colagem Dentária , Cimentos Dentários/uso terapêutico , Planejamento de Prótese Dentária , Falha de Restauração Dentária , Colagem Dentária/métodos , Planejamento de Prótese Dentária/métodos , Análise do Estresse Dentário , Humanos , Microscopia Eletrônica de Varredura , Propriedades de SuperfícieRESUMO
The aim of this study was to produce composite blocks (CB) for CAD/CAM applications by high-temperature-pressure (HT/HP) polymerization of resin-infiltrated glass-ceramic networks. The effect of network sintering and the absence/presence of initiator was investigated. Mechanical properties were determined and compared with those of Paradigm MZ100 (3M ESPE) blocks and HT/HP polymerized experimental "classic" CB, in which the filler had been incorporated by conventional mixing. The networks were made from glass-ceramic powder (VITA Zahnfabrik) formed by slip casting and were either sintered or not. They were silanized, infiltrated by urethane dimethacrylate, with or without initiator, and polymerized under HT/HP (300 MPa, 180°C) to obtain resin-infiltrated glass-ceramic network (RIGCN) CB. HT/HP polymerized CB were also made from an experimental "classic" composite. Flexural strength (σf), fracture toughness (KIC), and Vickers hardness were determined and analyzed by one- or two-way analysis of variance (ANOVA), Scheffé multiple-means comparisons (α = 0.05), and Weibull statistics (for σf). Fractured surfaces were characterized with scanning electron microscopy. The mechanical properties of RIGCN CB were significantly higher. Sintering induced significant increases in σf and hardness, while the initiator significantly decreased hardness. The results suggested that RIGCN and HT/HP polymerization could be used to obtain CB with superior mechanical properties, suitable for CAD/CAM applications.