NMR measurements of gaseous sulfur hexafluoride (SF6) to probe the cross-linking of EPDM rubber.

The effects of embedding gaseous SF6 into EPDM rubber were investigated using NMR methods. It was found that observed sorption and desorption processes follow the behavior of the dual mode sorption model. A strong correlation was found between EPDM cross-linking and transversal relaxation time of embedded SF6. EPDM samples with different cross-link densities, preliminarily determined by 1H transversal relaxation using the Gotlib model and Litvinov's method, were investigated using embedded SF6. The sensitivity of the 19F transversal relaxation rate of SF6 to the EPDM cross-link density variation was found to be at least 10 times higher than for 1H in the polymer chain. First experiments on probing the swelling effects in EPDM due to its contact with polar liquids have been performed.

Application of magnetic resonance imaging to the investigation of the diffusivity of 1,1,1,2-tetrafluorethane in two polymers.

In order to evaluate the suitability of a polymer as a sealing material for certain working fluids used in process plants, information about the fluid diffusivity into the polymer or the polymer permeability to the fluid is a prerequisite. The fluid of interest in the present work is 1,1,1,2-tetrafluorethane, CH(2)FCF(3), a partly fluorinated hydrocarbon (HFC) commonly known as refrigerant R134a. HFCs are increasingly used in refrigeration, air conditioning, and heat pump applications as substitutes for the chlorofluorocarbons (CFCs) or hydrochlorofluorocarbons (HCFCs) that are believed to be responsible for ozone depletion in the stratosphere. The polymers studied were FPM, a perfluoroelastomer, and EPDM, an ethylene-propylene-diene rubber. The study was carried out using magnetic resonance imaging (MRI). The contact time dependence of diffusion of the fluid into the polymer, as well as the spatial distributions of spin-lattice, T(1), and spin-spin, T(2), relaxation times, were used as indicators of the influence of the EPDM matrix on the mobility of R134a molecules.