Thermal Degradation Processes of Aromatic Poly(Ether Sulfone) Random Copolymers Bearing Pendant Carboxyl Groups.

Thermal degradation processes of poly(ether sulfone) random copolymers having different molar amount of diphenolic acid (DPA) units were studied by direct-pyrolysis/mass spectrometry, stepwise pyrolysis-gas chromatography/mass spectrometry and thermogravimetric techniques. Results highlighted that thermal degradation processes occur in the temperature range from 370 to 650 °C, yielding a char residue of 32-35 wt%, which decreases as the mol% of DPA units rises. The pyrolysis/mass spectra data allowed us to identify the thermal decomposition products and to deduce the possible thermal degradation mechanisms. Thermal degradation data suggest that the decarboxylation process of the pendant acid moiety mainly occurs in the initial step of the pyrolysis of the copolymers studied. Successively, the scission of the generated isobutyl groups occurs in the temperature range between 420 and 480 °C. Known processes involving the main chain random scission of the diphenyl sulfone and diphenyl ether groups were also observed.

Synthesis and Characterization of Copoly(Ether Sulfone)s with Different Percentages of Diphenolic Acid Units.

New functionalized Poly(ether sulfone)s having different molar ratio (10, 20, 30, 50, 70, 100 mol%) of 4,4-bis phenoxy pentanoic acid unit (diphenolic acid; DPA) units were synthesized and characterized by (1H and 13C)-NMR, MALDI-TOF MS, FT-IR, DSC and DMA analyses. The microstructural analysis of the copolymers, obtained by 13C-NMR using an appropriate statistical model, shows a random distribution of copolymer sequences, as expected. The presence of different amount of DPA units along the polymer chains affects the chemical and physical properties of the copolymers. The Tg and the contact angle values decrease as the molar fraction of DPA units increases, whereas the hydrophilicity increases. NMR and MALDI-TOF MS analyses show that all polymer chains are almost terminated with hydroxyl and chlorine as end groups. The presence of cyclic oligomers was also observed by MALDI-TOF MS analysis.

Design, Preparation and Thermal Characterization of Polystyrene Composites Reinforced with Novel Three-Cages POSS Molecules.

Novel polystyrene (PS)/polyhedral oligomeric silsequioxanes (POSSs) nanocomposites were designed and prepared by in situ polymerization, using, for the first time, three-cage POSS molecules. The synthesized compounds were first characterized by Fourier transform infrared spectroscopy (FTIR) and 1H NMR spectroscopy to verify the obtaining of the designed products before their thermal performance was evaluated and compared with those of pristine PS and the corresponding single-cage POSSs nanocomposites. The thermal behaviour was checked by the means of the differential scanning calorimetry (DSC) and thermogravimetric analysis (TGA). Scanning electron microscopy (SEM) was also used to confirm the hypothesis about the dispersion/aggregation of the POSS molecules into the polymer matrix. The parameters chosen to evaluate the thermal stability of the investigated compounds, namely temperature at 5% of mass loss (T5%) and solid residue at 700 °C, showed a significant increase in the stability of the polymers reinforced with the three-cages POSS, in comparison to both PS and single-cage POSS reinforced PSs, which therefore turn out to be promising molecular fillers for nanocomposite production.

Optimization of ZnO Nanorods Growth on Polyetheresulfone Electrospun Mats to Promote Antibacterial Properties.

Zinc oxide (ZnO) nanorods grown by chemical bath deposition (CBD) on the surface of polyetheresulfone (PES) electrospun fibers confer antimicrobial properties to the obtained hybrid inorganic-polymeric PES/ZnO mats. In particular, a decrement of bacteria colony forming units (CFU) is observed for both negative (Escherichia coli) and positive (Staphylococcus aureus and Staphylococcus epidermidis) Grams. Since antimicrobial action is strictly related to the quantity of ZnO present on surface, a CBD process optimization is performed to achieve the best results in terms of coverage uniformity and reproducibility. Scanning electron microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) provide morphological and compositional analysis of PES/ZnO mats while thermogravimetric analysis (TGA) is useful to assess the best process conditions to guarantee the higher amount of ZnO with respect to PES scaffold. Biocidal action is associated to Zn2+ ion leaching in solution, easily indicated by UV-Vis measurement of metallation of free porphyrin layers deposited on glass.

Polystyrene Nanocomposites Reinforced with Novel Dumbbell-Shaped Phenyl-POSSs: Synthesis and Thermal Characterization.

Two series of novel dumbbell-shaped polyhedral oligomeric silsesquioxanes (POSSs), fully functionalized with phenyl groups at the corner of the silicon cages, were used to prepare polystyrene (PS) nanocomposites through the method of in situ polymerization. The percentage of the molecular filler reinforcement was set as 5% w/w of POSS and was checked by 1H-NMR spectroscopy. The obtained nanocomposites were characterized by thermogravimetric analysis (TGA), differential scanning calorimetry (DSC), Fourier transform infrared spectroscopy (FTIR) and scanning electron microscopy (SEM). Thermal and morphological properties were evaluated and compared among the nanocomposites obtained using the two different series of dumbbell-shaped POSSs and with the net PS. The thermal parameters for the prepared nanocomposites were very high when compared with those of neat PS, and they evidenced significant differences when an aliphatic or aromatic bridge was used to link the silicon cages. SEM analysis results allow us to hypothesize a justification for the different resistance to thermal degradation showed by the two series of molecular reinforcement.

Interlaminar Toughening of Epoxy Carbon Fiber Reinforced Laminates: Soluble Versus Non-Soluble Veils.

This work describes the evaluation of different interlaminar veils to improve the toughening of epoxy/carbon fiber composites manufactured by resin infusion. Three commercial veils have been used in the study: two electro spun thermoplastic nanofiber (Xantulayr® from Revolution Fibres) with different areal weight, and one micro carbon fibers veil (Optiveil® from TFP). Two laboratory made veils were also manufactured by electrospinning commercial polyethersulfone (PES) tougheners (Virantage by Solvay). The veils were selected to be either soluble or non-soluble in the epoxy resin matrix during curing. The solubility was analyzed by scanning electron microscopy and dynamic mechanical analysis testing on the cured laminates. The fracture energy was evaluated by double cantilever bending (DCB) testing under Mode I loading. The insoluble thermoplastic nanofibers showed the highest toughening efficiency, followed by the soluble nanofiber veils. The carbon fiber based veil showed no toughness improvement.

Trifunctional Epoxy Resin Composites Modified by Soluble Electrospun Veils: Effect on the Viscoelastic and Morphological Properties.

Electrospun veils from copolyethersulfones (coPES) were prepared as soluble interlaminar veils for carbon fiber/epoxy composites. Neat, resin samples were impregnated into coPES veils with unmodified resin, while dry carbon fabrics were covered with electrospun veils and then infused with the unmodified epoxy resin to prepare reinforced laminates. The thermoplastic content varied from 10 wt% to 20 wt%. TGAP epoxy monomer showed improved and fast dissolution for all the temperatures tested. The unreinforced samples were cured first at 180 °C for 2 h and then were post-cured at 220 °C for 3 h. These sample showed a high dependence on the curing cycle. Carbon reinforced samples showed significant differences compared to the neat resin samples in terms of both viscoelastic and morphological properties.

Comparison of Ultem 9085 Used in Fused Deposition Modelling (FDM) with Polytherimide Blends.

Polyetherimide (PEI) blends modified by either polycarbonate (PC) or polyethylene terephthalate glycol-modified (PETG) were prepared. The latter modifier (PETG) was an industrial grade widely used for fused deposition modelling (FDM) printing. PEI blends were compared to Ultem 9085, which is the standard PEI grade for FDM printing in advanced applications. All the blends were thoroughly characterized in terms of their rheological, morphological, thermomechanical and tensile properties. Ultem 9085 showed improved rheology for processing over standard PEI. PEI/PC blends with 10 wt % of modifier developed here closely matched the viscosity behavior of Ultem 9085. On the other hand, the blends with low PC content (i.e., less than 20 wt %) outperformed Ultem 9085 in terms of thermal and tensile properties. When PETG was added, similar tensile properties to Ultem 9085 were found. The immiscibility for PC contents higher than 20 wt % deteriorated the tensile properties, making it less attractive for applications, although melt viscosity decreased further for increasing PC contents.

Combined Approach To Remove and Fast Detect Heavy Metals in Water Based on PES-TiO2 Electrospun Mats and Porphyrin Chemosensors.

Hybrid poly(ether sulfones) (PES)-TiO2 electrospun mats are used as selective filters to remove lead and zinc ions from water. Presence of TiO2 is functional to trigger fiber's surface charge that allows for better performances in terms of ionic adsorption with respect to bare PES mats. Temperature increase promotes a speed up of ion removal. Ability of electrospun mats to retain adsorbed ions is proven by washing procedures, which confirm the lack of released Pb2+ in solution, even after sonication. To detect presence of metal ions in aqueous solutions, water-soluble porphyrins are used as chemosensors, which are able to provide fast, in-field, and real-time analysis. In particular, cationic H2T4 metalation, occurring both in solution or at transparent glass surface, allows for a straightforward spectrophotometric (UV-vis) detection of metal ions in solution.

PES/POSS Soluble Veils as Advanced Modifiers for Multifunctional Fiber Reinforced Composites.

Novel polyhedral oligomeric silsesquioxanes (POSS)-filled thermoplastic electrospun veils were used to tailor the properties of the interlaminar region of epoxy-based composites. The veils were designed to be soluble upon curing in the epoxy matrix, so that POSS could be released within the interlaminar region. Three different POSS contents, varying from 1 to 10 wt %, were tested while the percentage of coPolyethersulphone (coPES) dissolved in the epoxy resin was kept to a fixed value of 10 wt %. Good quality veils could be obtained at up to 10 wt % of POSS addition, with the nanofibers' diameters varying from 861 nm for the coPES to 428 nm upon POSS addition. The feasibility of the soluble veils to disperse POSS in the interlaminar region was proved, and the effect of POSS on phase morphology and viscoelastic properties studied. POSS was demonstrated to significantly affect the morphology and viscoelastic properties of epoxy composites, especially for the percentages 1% and 5%, which enabled the composites to avoid POSS segregates occurring. A dynamic mechanical analysis showed a significant improvement to the storage modulus, and a shift of more than 30 °C due to the POSS cages hindering the motion of the molecular chains and network junctions.

Poly-paper: a sustainable material for packaging, based on recycled paper and recyclable with paper.

BACKGROUND: Until now, environmental sustainability issues are almost entirely unsolved for packaging materials. With the final aim of finding materials with a single recycling channel, cellulose fiber/poly(vinyl)alcohol composites were investigated. METHODS: After extrusion and injection molding, samples of composite with different cellulose fiber content (30%, 50% and 70% w/w) were tested. RESULTS: Tensile mechanical tests exhibited an improvement in composite stiffness when the reinforcement content was increased together with a decrease in composite elongation. Solubility tests performed at room temperature and 45°C showed different behavior depending on the water-resistant film applied on the composite (50% cellulose fiber content). In particular, the uncoated composite showed complete solubility after 2 hours, whereas at the same time point, no solubility occurred when a non-water-soluble varnish was used. CONCLUSIONS: The proposed composites, named Poly-paper, appear to warrant further investigation as highly sustainable packaging.