Analysis of pH, calcium ion release, and energy dispersive spectroscopy of a bioceramic root canal dressing.

This study compared the pH and calcium ion release of calcium silicate- (Bio-C Temp) and calcium hydroxide-based (Ultracal XS) medications. Intracanal remnants of both medications were also evaluated using SEM-EDS after the removal protocol. Thirty-five bovine teeth were prepared. Fifteen were filled with Bio-C Temp and 15 with Ultracal XS. Five remained without intracanal medication (control group). Five samples from each experimental time (i.e.. 24, 72, and 168 hours) were used to measure pH and calcium ions release using a digital pH meter and microplate reader, respectively. Afterward, the peaks of the chemical elements composing both medications were analyzed in SEM-EDS. One-way ANOVA and Tukey's post hoc test analyzed the pH and calcium ion release data. Student's t-test compared the medications in each experimental time. SEM-EDS described the percentage of chemical elements in the samples. Bio-C Temp and Ultracal XS showed a significant pH increase from 24 to 168 hours (p<0.05). Ultracal XS showed a higher pH value at 24 hours than Bio-C Temp (p<0.05) but were similar at 72 and 168h (p > 0.05). Calcium ion release did not depend on the experimental period (p > 0.05). Bio-C Temp showed lower calcium ions release than Ultracal XS at 24 hours (p<0.05). SEM-EDS analyses showed the remains of both medications, but the concentration of Si, Al, and W ions was present only in the calcium silicate-based medication. Bio-C Temp presented alkaline pH and a satisfactory calcium ion release over the time. The remaining of both medications were present after the protocols for paste removal.

Analysis of pH, calcium ion release, and energy dispersive spectroscopy of a bioceramic root canal dressing

Abstract This study compared the pH and calcium ion release of calcium silicate- (Bio-C Temp) and calcium hydroxide-based (Ultracal XS) medications. Intracanal remnants of both medications were also evaluated using SEM-EDS after the removal protocol. Thirty-five bovine teeth were prepared. Fifteen were filled with Bio-C Temp and 15 with Ultracal XS. Five remained without intracanal medication (control group). Five samples from each experimental time (i.e.. 24, 72, and 168 hours) were used to measure pH and calcium ions release using a digital pH meter and microplate reader, respectively. Afterward, the peaks of the chemical elements composing both medications were analyzed in SEM-EDS. One-way ANOVA and Tukey's post hoc test analyzed the pH and calcium ion release data. Student's t-test compared the medications in each experimental time. SEM-EDS described the percentage of chemical elements in the samples. Bio-C Temp and Ultracal XS showed a significant pH increase from 24 to 168 hours (p<0.05). Ultracal XS showed a higher pH value at 24 hours than Bio-C Temp (p<0.05) but were similar at 72 and 168h (p > 0.05). Calcium ion release did not depend on the experimental period (p > 0.05). Bio-C Temp showed lower calcium ions release than Ultracal XS at 24 hours (p<0.05). SEM-EDS analyses showed the remains of both medications, but the concentration of Si, Al, and W ions was present only in the calcium silicate-based medication. Bio-C Temp presented alkaline pH and a satisfactory calcium ion release over the time. The remaining of both medications were present after the protocols for paste removal.

Resumo Este estudo comparou o pH e a liberação de íons cálcio de medicações intracanais a à base de silicato de cálcio (Bio-C Temp) e à base de hidróxido de cálcio (Ultracal XS). Remanescentes de ambas as medicações também foram avaliados usando microscopia eletrônica de varredura e espectroscopia de dispersão de energia após o protocolo de remoção. Trinta e cinco dentes bovinos foram preparados. Quinze dentes foram preenchidos com Bio-C Temp e 15 com Ultracal XS. Cinco permaneceram sem medicação intracanal (grupo controle). Cinco amostras de cada tempo experimental (ou seja, 24, 72 e 168 horas) foram usadas para medir o pH e a liberação de íons de cálcio usando um medidor de pH digital e um leitor de microplacas, respectivamente. Em seguida, os picos dos elementos químicos que compõem os dois medicamentos foram analisados ​​em microscopia eletrônica de varredura e por espectroscopia de dispersão de energia. Os testes One-way ANOVA e post hoc de Tukey analisaram os dados de pH e liberação de íons cálcio. O teste t de Student comparou as medicações em cada tempo experimental. A microscopia eletrônica de varredura e a espectroscopia de dispersão de energia descreveu a porcentagem de elementos químicos nas amostras. O Bio-C Temp e o Ultracal XS mostraram um aumento significativo de pH de 24 a 168 horas (p<0,05). O Ultracal XS apresentou um valor de pH mais alto em 24 horas do que o Bio-C Temp (p<0,05), mas foi semelhante em 72 e 168h (p > 0,05). A liberação de íons cálcio não dependeu do período experimental (p> 0,05). O Bio-C Temp apresentou menor liberação de íons de cálcio do que Ultracal XS em 24 horas (p<0,05). As análises de microscopia eletrônica de varredura e espectroscopia de dispersão de energia mostraram remanescentes de ambas as medicações, mas a concentração de íons Si, Al e W estavam presentes apenas na medicação à base de silicato de cálcio. O Bio-C Temp apresentou pH alcalino e maior liberação de íons cálcio. Remanescentes de ambas as medicações estiveram presentes após os protocolos de remoção da pasta.

Effect of Curing Modes on the Mechanical Properties of Commercial Dental Resin-Based Composites: Comparison between Different LEDs and Microwave Units.

Resin-based composites (RBCs) have transformed restorative dentistry and its procedures. However, the characteristics of RBCs have been modified over the years to enhance the physical and chemical properties of the materials. This context raises the need for studies that evaluate whether the properties of the RBCs that are commercially available are clinically adequate with different curing modes. This study aimed to evaluate the mechanical behavior of commercial RBCs after undergoing different curing modes. Twenty-three RBCs of different classes were evaluated. For curing the specimens, a microwave (BMS45, Brastemp) (for 3 min at 450 W) and three LED units were used: an Emitter A Fit (Schuster (second generation)) (light-curing for 15 s with an irradiance of 1250 mW/cm2), VALO (Ultradent (third generation)) (light-curing for 15 s with an irradiance of 1100 mW/cm2), and Emitter Now Duo (Schuster (second generation)) (light-curing for 15 s with an irradiance of 1100 mW/cm2). A total of 670 RBC specimens of 8 mm in diameter and 1 mm in depth were obtained. Afterward, a biaxial flexure strength test was performed until the failure of the specimens, using a universal testing machine set at a speed of 0.5 mm/min. The same specimens were subjected to infrared spectroscopy for evaluating the degree of conversion. Tukey's test was used for multiple comparisons at a significance level of 5%. The light-curing mode did not affect the flexure strength of the RBCs (p > 0.05), but the type and shade of RBCs did so (p < 0.05). In conclusion, the type of RBC directly interferes with the mechanical behavior of the material. However, the curing modes within the same RBC did not change the mechanical properties.

Avaliação clínica do desempenho do sistema rotatório RaCe® / Clinical assessment of the performance of the RaCe® rotary sytem

O objetivo do tratamento endodôntico é possibilitar sua limpeza, modelagem e desinfecção do sistema de canais radiculares para seu posterior selamento. Sistemas rotatórios de níquel-titânio têm sido empregados, principalmente devido a sua grande flexibilidade e baixo módulo de elasticidade. Vários estudos buscam equacionar a rapidez e facilidade da instrumentação rotatória com sua eficiência e segurança. Assim, o objetivo deste estudo foi divulgar a técnica e avaliar o desempenho clínico da instrumentação rotatória com o sistema RaCe. Estes instrumentos foram introduzidos recentemente no mercado pela FKG apresentando um desenho inovador de suas lâminas cortantes. Cinco molares foram tratados no curso de Especialização em Endodontia da Universidade do Sagrado Coração, por um mesmo operador. Os tratamentos foram analisados radiograficamente, fatores como dilatação dos canais, manutenção da trajetória, desvio apical e manutenção do comprimento de trabalho, além de fraturas ou deformação de instrumentos. O novo sistema mostrou bons resultados em relação a todos os quesitos. Concluiu-se que todos os canais biomecanizados com o sistema RaCe resultaram num tratamento endodôntico adequado tanto clínica quanto radiograficamente, obtendo-se eficiência e facilidade no preparo.

Aspectos associados à amamentação e desmame em crianças atendidas no programa bebê-clínica em Bandeirantes-PR / Breastfeeding and weaning related aspects in children attended at the “bebê-clinica” program in Bandeirantes–PR

O aleitamento materno, alimento natural, de fundamental importância para a saúde materno-infantil e para o espaçamento das gestações, encontra dificuldades em sua prática. O presente estudo propõe avaliar as razões e analisar quais são os mitos e fatos que contribuem para o desmame antes dos seis meses de idade. O objeto de estudo foi composto por crianças que participam do Programa Preventivo- Educativo Bebê-Clínica, realizando o levantamento do prontuário de cada criança, que foram amamentados no peito no período de zero a seis meses de idade totalizando uma amostragem de 143 prontuários. O questionário buscava informações relacionadas a progenitora tais como: idade, paridade, estado civil, atuação profissional, escolaridade, raça, renda familiar, inclusão em programa social e histórico da gestação. A promoção do aleitamento materno deve ser vista como uma ação prioritária para a melhoria da saúde e da qualidade de vida das crianças e de suas famílias. As estratégias de promoção da amamentação devem variar de acordo com a população, sua cultura, seus hábitos, suas crenças, sua posição sócio-econômica, entre outras características. No entanto, é de fundamental importância em qualquer estratégia a conscientização da importância do aleitamento materno.

Avaliação in vitro da infiltração marginal de alguns materiais seladores provisórios / In vitro evaluation of marginal microleakage of remoroary sealing materials

Estudou-se, in vitro, a infiltração marginal de 7 materiais seladores provisórios. Instrumentaram-se 82 dentes caninos unirradiculares humanos, obtidos de Banco de Dentes. No interior de cada canal radicular, foi colocado um cone de papel absorvente com a solução alcooólica de dimetilglioxina a 1 por cento e, na câmara pulpar, uma bolinha de algodão também impregnada em solução alcoólica de dimetilglioxima a 1 por cento, e os materiais seladores provisórios foram testados. Os dentes foram imersos em solução de sulfato de níquel a 5 por cento e submetidos à ciclagem térmica durante 72h. Os resultados demosntraram que não houve infiltração coronária quando se usou guta-percha mais Super Bonder, e os materiais foram agrupados na ordem decrescente de infiltraçãod: Cimpat W, Citodur, Dentalville, guta-percha mais Super Bonder.

Avaliação in vitro da infiltração marginal de alguns materiais seladores provisórios submetidos à ciclagem térmica / Evaluation in vitro of marginal microleakage of the temporay seling materials submetted to thermal cycling

Estudou-se in vitro a microinfiltração coronária de quatro seladores temporários usados em Endodontia: Dentatalville, IRM, Bioplic, Vitremer. Quarenta e dois dentes humanos, obtidos do banco de dentes da Universidade do Sagrado Coração - Bauru, foram usados. Feita a cavidade de acesso endodôntico, os dentes foram então divididos em seis grupos de sete dentes. No interior de cada câmara pulpar, foram colocadas três bolinhas de algodão impregnadas com solução alcoólica de dimetilglioxima a 1 por cento e os materiais seladores provisórios testados. Em seguida, os dentes foram impermeabilizados, imersos em solução de sulfato de níquel a 5 por cento, submetidos à ciclagem térmica (5 grau centígrados, 37 grau centígrados e 55 grau centígrados) durante sete dias e seccionados no sentido mésio-distal. A infiltração do sulfato de níquel como identificador da infiltração marginal foi revelada pela formação do complexo Ni-dimetliglioxima, de coloração vermelha. A análise de infiltração foi possível em função da profundidade em que ocorreu a coloração vermelha nas bolinhas de algodão, medidas em escores. Com base no testo estatístico Kruskal Wallis, o IRM apresentou a maior microinfiltração coronária, sendo estatisticamente diferente do Biolic do Dentalville e Vitremer. Agrupando-se os materiais na ordem decrescente de infiltração, tem-se: IRM, Vitremer, Dentalville, Bioplic com ataque ácido e adesivo dentinário, Dentaville + Super Bonder e Bioplic somente

Descompressão gradual de lesões ósseas parendodônticas: técnica conservadora / Gradual descompression of large periradicular lesions: a conservative treatment

Descrição de técnica conservadora de descompressão de grandes lesões radiolúcidas ósseas, previamente à cirurgia radical. Discute-se as vantagens, indicações e pecularidades da modalidade cirúrgica