RESUMO
BACKGROUND: Chemical surface treatment increases the shear bond strength (SBS) between hard reline resins (HRRs) and denture base resin. OBJECTIVE: To evaluate the effect of methyl formate-methyl acetate (MF-MA), when used as a surface treatment agent, on the SBS between denture base resin and different HRRs. MATERIALS AND METHODS: One hundred and twenty specimens of heat-polymerised acrylic resin denture base (Meliodent(®) ) were divided into 12 groups. These groups comprised denture base relined with three self-polymerised HRRs [Unifast trad(®) (UT), Tokuyama(®) RebaseII Fast (TR), Ufi gel hard(®) (UG)], and treated with their respective Bonding Agent (BA) or by MF:MA solutions at ratios of 35:65, 25:75, and 15:85 for 15 s. The SBS was measured using a Universal Testing Machine. The data were analysed using two-way anova and post hoc Tukey's analysis at p < 0.05. RESULTS: The highest SBS was in the UT treated with MF:MA at a ratio of 25:75 group, followed by UT treated with MF:MA at ratios of 15:85, 35:65, UT treated with BA, and all UG treated with MF:MA groups. The SBS of the UT treated with MF:MA at a ratio of 25:75 group was significantly higher than those of the groups treated with BA. The SBS of the UG treated with MF:MA groups was significantly higher than control. The TR groups treated with BA or MF:MA groups showed no significant difference in SBS. CONCLUSION: Surface treatment with MF-MA significantly enhanced the SBS of denture base resin and UT and UG compared to that of the groups treated with BA.