The Domain and Structural Characteristics of Ferroelectric Copolymers Based on Vinylidene Fluoride Copolymer with Tetrafluoroethylene Composition (94/6).

This paper presents data on the macroscopic polarization of copolymer films of vinylidene fluoride with tetrafluoroethylene obtained with a modified apparatus assembled according to the Sawyer-Tower Circuit. The kinetics of the polarization process were analyzed taking into consideration the contributions of both bound and quasi-free (impurity) charges. It was shown that an "abnormal" decrease in conductivity was observed in fields near the coercive fields. This could be associated with the appearance of deep traps of the impurity charge carriers formed by the polar planes of ß-phase crystals. The conductivity data obtained from the charge and current responses differed. It was concluded that chain segments contributing to polarization with sufficiently low fields were present in the amorphous phase. A comparison showed that the average size of ß-phase crystals (crystals of X-ray diffraction reflection width) was almost one order of magnitude lower than the domain size obtained using piezoresponse force microscopy (PFM). The analysis of the fast-stage dielectric response before and after polarization indicated that as the external polarizing field increased in the ferroelectric polymer chains, conformational transitions occurred according to the T3GT3G- → (-TT-)n и TGTG → (-TT-)n types. This was accompanied by an increase in the effective dipole moment in the amorphous phase chains. The analysis of the IR spectroscopy data obtained in transmission and ATR modes revealed a difference in the conformational states of the chains in the core and surface parts of the film.

Low Cost Embedded Copper Mesh Based on Cracked Template for Highly Durability Transparent EMI Shielding Films.

Embedded copper mesh coatings with low sheet resistance and high transparency were formed using a low-cost Cu seed mesh obtained with a magnetron sputtering on a cracked template, and subsequent operations electroplating and embedding in a photocurable resin layer. The influence of the mesh size on the optoelectric characteristics and the electromagnetic shielding efficiency in a wide frequency range is considered. In optimizing the coating properties, a shielding efficiency of 49.38 dB at a frequency of 1 GHz, with integral optical transparency in the visible range of 84.3%, was obtained. Embedded Cu meshes have been shown to be highly bending stable and have excellent adhesion strength. The combination of properties and economic costs for the formation of coatings indicates their high prospects for practical use in shielding transparent objects, such as windows and computer monitors.