RESUMO
Polypropylene (PP)-based composites have attracted numerous attention as a replacement of prevailing cross-linked polyethylene (XLPE) for high-voltage insulation due to their ease of processing, recyclability, and excellent electrical performance. However, the poor resistances against high-temperature creep and thermal aging are obstacles to practical applications of PP-based thermoplastic high-voltage insulation. To address these problems, in this Letter, we synthesized an impact polypropylene copolymer (IPC) containing multifold long-chain branched (LCB) structures in phases, especially the interfaces between the PP matrix and the rubber phase. The results indicated that the structural stability of LCBIPC was significantly enhanced under extreme conditions. In comparison to IPC (without LCB structures), 24.1% less creep strain and 75.2% less unrecoverable deformation are achieved in LCBIPC at 90 °C. In addition, the thermal aging experiments were performed at 135 °C for 48 and 88 days for IPC and LCBIPC, respectively. The results show that the resistance against thermal aging was also enhanced in LCBIPC, which showed a 133% longer thermal aging life compared to IPC. Further results revealed that the interfacial layer between the PP matrix and the rubber phase was constructed in LCBIPC. The two phases are tightly linked by chemical bonds in LCB structures, leading to enforced constraints of the rubber phase at the micro level and better resistance performance against creep and thermal aging at the macro level. Evidently, the reported eco-friendly LCBIPC thermoplastic insulation shows great potential for applications in high-voltage cable insulation.
RESUMO
Insulation fails quickly under high-frequency AC high voltage, especially bipolar square-wave voltage with a high dV/dt. It is of great significance to study the failure mechanism of epoxy casting insulation under such kind of voltage. In this paper, pin-plane epoxy casting insulation samples with air gaps were prepared, and the relation between the electrical trees under the high frequency bipolar square-wave voltage and the air gap conditions and voltage frequencies (1~20 kHz) were studied. Results indicated that, with the presence of air gaps, the electrical trees were bush-type and had a relatively slow growth rate, which was different from the fast-growing branch-type trees in the samples without air gap. The electrical tree characteristics related with the size of air gap and voltage frequency were also studied. The electrical tree grew faster under higher voltage frequency or with a smaller air gap. Results proved that discharge introduced a lot of defects for the surface layer of the epoxy resin samples and hence induced the possibility of multi-directional expansion of electrical trees. In addition, the resulting heat accumulation and unique charge transport synergistically affected the electrical tree characteristics under the high frequency bipolar square-wave voltage.