Optical properties of zirconia-reinforced lithium silicate veneers obtained with CAD/CAM milling and hot-pressing techniques: a comparative in vitro study.

Background and aims: Dental veneers have become increasingly required among patients, but little is known about the optical properties of veneers obtained from the same ceramic material through different processing techniques. Methods: In this study we compared the translucency and the opalescence parameters of zirconia-reinforced lithium silicate (ZLS) veneers restorations fabricated through CAD/CAM milling and hot-pressing techniques on the upper central incisor. Eighty specimens divided into 8 groups (n=10) were sectioned (Celtra Duo) and heat pressed (Celtra Press) to obtain 0.8 mm thickness. The optical parameters were calculated from the color difference against different backgrounds. Analysis of variance, one way ANOVA and post-hoc multiple comparison tests were used to evaluate and compare the optical properties of the same material, with a significance level of p < 0.05. Results: The processing method had significant effect on optical parameters. Celtra Duo HT proved to be the material with the highest transparency degree. The hot-pressing technique led to higher opacity than CAD/CAM milling technique. Conclusions: For a bio-mimetic aesthetic prosthetic restoration, the ceramic materials must have the same translucency and opacity as the real tooth. The results of this study revealed that high translucency ZLS obtained through hot pressing technique was the material of choice, as it fulfilled these requirements.

Compressive strength evaluation of thin occlusal veneers from different CAD/CAM materials, before and after acidic saliva exposure.

In the present study are depicted valuable observations for practitioners, obtained from an in vitro study which aims to evaluate the compressive strength of occlusal veneers fabricated from 3 type of restorative materials, before and after 1 month of acidic artificial saliva exposure (pH = 2.939). In this context, 90 extracted human molars were prepared to receive computer-aided design/computer-aided manufacturing (CAD/CAM) occlusal veneers. The restorative materials considered in this study were: Cerasmart; Straumann Nice and Tetric CAD. The occlusal veneers were designed, milled and cemented with an adhesive dual-cure resin cement. From all the extracted human molars, only sixty specimens were immersed in acidic artificial saliva, for 1 month, at 37 °C ± 1 °C and part of this specimens were also thermo-cycled, between 5 and 55 °C ± 2 °C, before compressive strength test. The results showed a lower compressive strength for both the samples exposed to acidic artificial saliva as well as for the samples exposed to acidic artificial saliva and thermo-cycled. Scanning electron microscopy (SEM) showed that after compressive strength, all the specimens non-exposed to acidic artificial saliva, present extensive cracks formation at the surface of the restorations, and after exposure to acidic artificial saliva for 1 month, the surface damage was characterized by longitudinal and profound fractures of the restoration, as well as the fracture of the tooth structure. Between CAD/CAM materials tested, nanoceramic resin shows more favorable fracture patterns, both before and after acidic artificial saliva exposure.