Dynamics of native oxide growth on CdTe and CdZnTe X-ray and gamma-ray detectors.

We studied the growth of the surface oxide layer on four different CdTe and CdZnTe X-ray and gamma-ray detector-grade samples using spectroscopic ellipsometry. We observed gradual oxidization of CdTe and CdZnTe after chemical etching in bromine solutions. From X-ray photoelectron spectroscopy measurements, we found that the oxide consists only of oxygen bound to tellurium. We applied a refined theoretical model of the surface layer to evaluate the spectroscopic ellipsometry measurements. In this way we studied the dynamics and growth rate of the oxide layer within a month after chemical etching of the samples. We observed two phases in the evolution of the oxide layer on all studied samples. A rapid growth was visible within five days after the chemical treatment followed by semi-saturation and a decrease in the growth rate after the first week. After one month all the samples showed an oxide layer about 3 nm thick. The oxide thickness was correlated with leakage current degradation with time after surface preparation.

Infrared LED Enhanced Spectroscopic CdZnTe Detector Working under High Fluxes of X-rays.

This paper describes an application of infrared light-induced de-polarization applied on a polarized CdZnTe detector working under high radiation fluxes. We newly demonstrate the influence of a high flux of X-rays and simultaneous 1200-nm LED illumination on the spectroscopic properties of a CdZnTe detector. CdZnTe detectors operating under high radiation fluxes usually suffer from the polarization effect, which occurs due to a screening of the internal electric field by a positive space charge caused by photogenerated holes trapped at a deep level. Polarization results in the degradation of detector charge collection efficiency. We studied the spectroscopic behavior of CdZnTe under various X-ray fluxes ranging between 5 × 10 5 and 8 × 10 6 photons per mm 2 per second. It was observed that polarization occurs at an X-ray flux higher than 3 × 10 6 mm - 2 ·s - 1 . Using simultaneous illumination of the detector by a de-polarizing LED at 1200 nm, it was possible to recover X-ray spectra originally deformed by the polarization effect.