Critical-sized marginal defects around implants in the rabbit mandible.

BACKGROUND: The mandible of the rabbit is considered a reliable model to be used to study bone regeneration in defects. The aim of the present study was to evaluate the formation of new bone around implants installed in defects of either 5 or 10 mm in the mandible of rabbits. MATERIALS AND METHODS: In 12 rabbits, 3 mm deep circumferential defect, either 5 or 10 mm in diameter, were prepared bilaterally and an implant was placed in the center. A collagen membrane was placed to close the entrance. After 10 weeks, biopsies were taken, histological slides were prepared, and different regions of the defects were analyzed. RESULTS: Similar amounts of new bone were found in both defects. However, most of the 5 mm defects were filled with new bone. New bone was observed closing the entrance of the defect and laid onto the implant surface. Only in a few cases the healing was incomplete. Despite a similar percentage of new bone found within the 10 mm defects, the healing was incomplete in most of the cases, presenting a low rate of bone formation onto the implant surface within the defect. Only one case presented the closure of the entrance. CONCLUSIONS: The dimensions of the defect strongly influenced the healing so that a circumferential marginal defect of 10 mm around an implant in the mandible body should be considered a critical-sized defect. The presence of the implant and of residues of teeth might have strongly influenced the healing.

Argon Bioactivation of Implants Installed Simultaneously to Maxillary Sinus Lifting without Graft. An Experimental Study in Rabbits.

BACKGROUND: The treatment of the surface of titanium implants with argon plasma improved its hydrophilicity and cell adhesion, resulting in higher bone apposition on implant and graft surfaces. The spontaneous perforation over time of the sinus mucosa after sinus augmentation has been documented in experimental studies at both implants and graft particles. The aim of the present study was to evaluate the influence of plasma argon treatment of the implant surface on bone apposition and on the rate of sinus mucosa perforations. METHODS: A sinus lifting procedure was performed bilaterally in sixteen rabbits, and implants, either treated with argon plasma or left without treatment (control), were placed simultaneously without grafts. After 8 weeks, histological analyses were carried out. RESULTS: A collapse of the sinus mucosa was observed at all implants. Twenty-four out of thirty-two implants presented sinus mucosa perforations at the apex. Several perforations were also found at the threads. Thinned mucosa sites (width < 40 µm) were found around almost all implants. About 2.6-2.9 mm of the apical regions of the implant did not present signs of osseointegration and about 1.3 mm were exposed to the sinus cavity. No statistically significant differences were found between plasma and control sites. CONCLUSIONS: In conclusion, the sinus mucosa was damaged and perforated by direct contact with treated and non-treated implant surfaces. The treatment of the implant surface with argon plasma did not affect the outcomes.