RSC Adv ; 12(31): 20074-20079, 2022 Jul 06.
Artigo em Inglês | MEDLINE | ID: mdl-35919588

RESUMO

Up-conversion nanoparticles have garnered lots of attention due to their ability to transform low energy light (near-infrared) into high-energy (visible) light, enabling their potential use as remote visible light nano-transducers. However, their low efficiency restricts their full potential. To overcome this disadvantage, fluoroindate glasses (InF3) doped at different molar concentrations of Yb3+ and Er3+ were obtained using the melting-quenching technique, reaching the highest green emission at 1.4Yb and 1.75Er (mol%), which corresponds to the 4S3/2 → 4I15/2 (540-552 nm) transition. The particles possess the amorphous nature of the glass and have a high thermostability, as corroborated by thermogravimetric assay. Furthermore, the spectral decay curve analysis showed efficient energy transfer as the rare-earth ions varied. This was corroborated with the absolute quantum yield (QY) obtained (85%) upon excitation at 385 nm with QYEr = 17% and QYYb = 68%. Additionally, InF3-1.4Yb-1.75Er was milled and functionalized using poly(ethylene glycol) to impart biocompatibility, which is essential for biomedical applications. Such functionalization was verified using FTIR, TG/DSC, and XRD.

SELEÇÃO DE REFERÊNCIAS
DETALHE DA PESQUISA