A New Photocatalyst Bismuth Oxo Citrate: Synthesis, Characterization, and Photocatalytic Performance.

A new photocatalyst bismuth oxo citrate was synthesized by facile precipitation process with calcination at 200 °C. The photocatalyst was characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), Fourier-transform infrared (FTIR) spectroscopy, N2 sorptometry, and elemental analysis. Morphologically, it is composed of polyhedral particles with different, irregular shapes and sizes. The specific surface area (SSA) of the photocatalyst was 8.92 m2 g-1. It showed very good photocatalytic performance and reusability. Total decolorization of Reactive Blue 19 (RB19) was achieved in less than 10 minutes, which is much faster in comparison with TiO2 P25. Also, bismuth oxo citrate showed higher photocatalytic activity than other photocatalysts based on bismuth compounds reported by other authors. Optimal photocatalysis parameters were pH 2 and photocatalyst dose of 250 mg dm-3. The decolorization rate was found to decrease as initial dye concentration increased. The photocatalytic data best fitted to L-H kinetic model with pseudo-first order reaction rate. Chrastil diffusion model showed that diffusion has not influence on the process.

Suppression of inherent ferromagnetism in Pr-doped CeO2 nanocrystals.

Ce(1-x)Pr(x)O(2-δ) (0 ≤ x ≤ 0.4) nanocrystals were synthesized by self-propagating method and thoroughly characterized using X-ray diffraction, Raman and X-ray photoelectron spectroscopy and magnetic measurements. Undoped CeO2 nanocrystals exhibited intrinsic ferromagnetism at room temperature. Despite the increased concentration of oxygen vacancies in doped samples, our results showed that ferromagnetic ordering rapidly degrades with Pr doping. The suppression of ferromagnetism can be explained in terms of the different dopant valence state, the different nature of the vacancies formed in Pr-doped samples and their ability/disability to establish the ferromagnetic ordering.