Influence of Protic Ionic Liquid-Based Flame Retardant on the Flammability and Water Sorption of Alkalized Hemp Fiber-Reinforced PLA Composites.

This article investigates the effects of combining a novel protic ionic liquid-based fire retardant (FR) with alkalized hemp fiber. A pivotal importance of this study refers to the hydrophilic properties and limits regarding poor thermal resistance of green composites where standard guidelines for fire risks are crucial. Although it is well-studied that alkalization is essential for green composite's moisture and mechanical durability, research on the flammability of such a combined treatment for natural fiber-reinforced biopolymer composites is lacking. The alkaline treatment used in the current study follows a process already studied as optimal, particularly for the selected hemp fiber. The fire performance was examined using a bench scale approach based on self and piloted ignition from cone calorimeter tests. The result from the Fourier-transform infrared analysis of the hemp fiber confirms phosphorylation following the fire-retardant treatment, which was visible from the morphological examination with scanning electron microscope. The presence of FR in the composites led to impactful moisture sorption. However, the FR composites demonstrated an enhanced response to fire, indicating potential use as a Class B standard for building construction, and hazard level 3 (HL3) classification as an interior material in vehicles, provided the problem of high emission of smoke is mitigated.

Investigation of Efficient Alkali Treatment and the Effect of Flame Retardant on the Mechanical and Fire Performance of Frost-Retted Hemp Fiber Reinforced PLA.

This research investigates an effective alkali (NaOH) treatment and fire-retardant coating to produce biocomposites from frost-retted hemp fiber and PLA. The fiber surface treatment with various NaOH concentrations was investigated throughout a range of soaking times. The results show that the extracted non-cellulosic fiber content increases with treatment duration and NaOH concentration, while the fraction of targeted components removed remains nearly unchanged after soaking for 1, 2, and 4 h with a 5 wt.% NaOH solution. At the composite level, the treatment with 5 wt.% NaOH solution for 1 h emerged as the most efficient, with tensile strength, Young's modulus, flexural strength, and flexural modulus of 89.6 MPa, 9.1 GPa, 121.6 MPa, and 9.6 GPa, respectively, using 30 wt.% fibrous reinforcement. The fire performance of the examined batches of biocomposites improved significantly with the novel fire-retardant (Palonot F1) coating. However, the tensile strength notably decreased, while the flexural properties showed only a slight reduction. In most cases, the biocomposites with the alkali-treated hemp fiber had delayed ignition during the 5 min exposure to the cone heater. The findings in this work contribute to studies that will be required to give design guidelines for sustainable building options.