RESUMO
The sulfur curing system, peroxide curing system and their combinations were applied for the cross-linking of unfilled and carbon black-filled rubber formulations based on ethylene-propylenediene-monomer rubber. The results demonstrated that the type of curing system influenced the course and shape of curing isotherms. This resulted in the change of curing kinetics of rubber compounds. The cross-link density of materials cured with combined vulcanization systems was lower than that for vulcanizates cured with the peroxide or sulfur system. Good correlation between the cross-link density as well as the structure of the formed cross-links and physical-mechanical characteristics of the cured materials was established. Both filled and unfilled vulcanizates cured with combined vulcanization systems exhibited a higher tensile strength and elongation at break when compared to their equivalents vulcanized in the presence of the peroxide or sulfur curing system. It can be stated that by proper combination of vulcanization systems, it is possible to modify the tensile behavior of vulcanizates in a targeted manner. On the other side, dynamical-mechanical properties were found not be significantly influenced by the curing system composition.
RESUMO
Calcium lignosulfonate in the amount 30 phr was incorporated into rubber compounds based on pure NBR and an NBR carbon black batch, in which the content of carbon black was 25 phr. Glycerine, as a cheap and environmentally friendly plasticizer, was applied into both types of rubber formulations in a concentration scale ranging from 5 to 20 phr. For the cross-linking of rubber compounds, a sulfur-based curing system was used. The work was aimed at the investigation of glycerine content on the curing process and rheological properties of rubber compounds, cross-link density, morphology and physical-mechanical properties of vulcanizates. The results show that glycerine influences the shapes of curing isotherms and results in a significant decrease between the maximum and minimum torque. This points to the strong plasticizing effect of glycerine on rubber compounds, which was also confirmed from rheological measurements. The application of glycerine resulted in better homogeneity of the rubber compounds and in the better dispersion and distribution of lignosulfonate within the rubber matrix, which was subsequently reflected in the significant improvement of tensile characteristics of vulcanizates. A higher cross-link density as well as better physical-mechanical properties were exhibited by the vulcanizates based on the carbon black batch due to the presence of a reinforcing filler.
RESUMO
Ethylene-propylene-diene monomer (EPDM)-based composites including four different types of graphene nanoplatelets (GnPs) were prepared to evaluate the size effects of GnPs in terms of both specific surface area and lateral size on the morphological, mechanical, and viscoelastic properties, swelling ratio, crosslink density, and oxygen permeability. EPDM-based hybrid composites with GnPs and carbon black (CB) fillers were prepared, with the concentrations of 20 and 50 phr of CB and GnPs up to 7 phr. All samples were prepared using the melt mixing method, followed by compression molding. The specific surface area of GnPs is a more important key factor for mechanical and viscoelastic properties than its lateral size. The presence of GnPs leads to a decrease in the swelling ratio and oxygen permeability of the matrix while an increase in the crosslinking density. For a given specific surface area of GnPs (170 m2/g) and the same thickness (5 nm), the optimum lateral size for mechanical properties, swelling ratio, and crosslinking density is about 30 µm. There is a distinct synergic effect on the mentioned properties when hybrid fillers are used. For hybrid composites, the optimum total and each filler concentration are found to be important for achieving the best performance in terms of mechanical properties, swelling ratio, and crosslink density.
RESUMO
A procedure is described of grafting the acrylic acid onto an oxygen/ozone-activated metallocene poly(ethylene-co-propylene). Consequently, the grafted copolymer is applied as a component in a metallocene polyolefin-based hot-melt adhesive composition with increased adhesion. The surface properties and adhesion strength of the prepared hot-melt adhesive (HMA) were determined and used to account for the effect of grafting. The application of grafted polyolefin as one of the components of the HMA mixture provides significant increase in adhesive strength, and it also results in increased compatibility and negligible effects on the technological parameters of the final composition. The obtained results may have significant impact for the practical application of prepared HMA for book bonding.