Preparation of wavy three-dimensional graphene-like biochar and its adsorption mechanism of embedded separation for dimethoate.

In this study, graphene-like biochar (IZBC) was prepared by pyrolysis of wheat straw in the presence of catalyst and activator. The formation of graphene in IZBC could be divided into three stages: shell core generation, carburization, and carbon precipitation. When the pyrolysis temperatures were in the ranges of 500-600 â„ƒ, 600-700 â„ƒ, 700-800 â„ƒ and 800-900 â„ƒ, 17%, 32%, 13% and 38% of graphene were produced, respectively. The contribution ratios of graphene by FeCl3, ZnCl2 and HCl were 64%, 23% and 13%, respectively. Moreover, IZBC was filled with porous wavy three-dimensional graphene nanosheets that enabled self-aggregation to be effectively prevented, which was superior to the striped two-dimensional structure. The adsorption of IZBC for dimethoate was a spontaneous exothermic reaction with the adsorption capacity of 980 µmol/g, which was consistent with the pseudo-second-order and intraparticle diffusion models. The adsorption was inhibited by coexisting cations, anions, and humic acid in water. Dimethoate was adsorbed on graphene through embedded separation, with pore filling, cation-π and electrostatic attraction as the key driving forces. In addition, the adsorbed saturated IZBC could be effectively regenerated for many times by 2 mol/L HCl solution.