Surface-Anchored Acetylcholine Regulates Band-Edge States and Suppresses Ion Migration in a 21%-Efficient Quadruple-Cation Perovskite Solar Cell.

Although incorporating multiple halogen (bromine) anions and alkali (rubidium) cations can improve the open-circuit voltage (Voc ) of perovskite solar cells (PSCs), severe voltage loss and poor stability have remained pivotal limitations to their further commercialization. In this study, acetylcholine (ACh+ ) is anchored to the surface of a quadruple-cation perovskite to provide additional electron states near the valence band maximum of the perovskite surface, thereby enhancing the band alignment and minimizing the Voc loss significantly. Moreover, the quaternary ammonium and carbonyl units of ACh+ passivate the antisite and vacancy defects of the organic/inorganic hybrid perovskite. Because of strong interactions between ACh+ and the perovskite, the formation of lead clusters and the migration of halogen anions in the perovskite film are suppressed. As a result, the device prepared with ACh+ post-treatment delivers a power conversion efficiency (PCE) (21.56%) and a value of Voc (1.21 V) that are much higher than those of the pristine device, along with a twofold decrease in the hysteresis index. After storage for 720 h in humid air, the device subjected to ACh+ treatment maintained 70% of its initial PCE. Thus, post-treatment with ACh+ appears to be a useful strategy for preparing efficient and stable PSCs.

Lead-free bright blue light-emitting cesium halide nanocrystals by zinc doping.

Cesium lead halide perovskite nanocrystals (NCs) have attracted extensive attention for photoelectric device application due to their excellent optoelectronic properties. However, the toxicity of lead has hindered their commercialization. Consequently, lead free cesium metal halide NCs have been developed, but these materials suffer from low photoluminescence quantum yield (PLQY) and poor stability. Here, a new class of lead-free non-perovskite blue-emitting cesium bromine (CsBr) and cesium iodine (CsI) halide NCs are realized by zinc doping. High PLQYs of 79.05% and 78.95% are achieved by CsBr:Zn and CsI:Zn NCs, respectively, attributed to the improved local structural order and reduced strain between the lattices of the NCs after storing under ambient conditions for 20 to 30 days. Moreover, zinc doped cesium halide NCs show excellent air stability for at least 50 days. Our results for zinc doped cesium halide NCs have shown a new avenue to fabricate lead-free halide NCs for blue lighting and display applications.