The compression behavior of zircon-type samarium orthovanadate, SmVO4, has been investigated using synchrotron-based powder x-ray diffraction and ab initio calculations of up to 21 GPa. The results indicate the instability of ambient zircon phase at around 6 GPa, which transforms to a high-density scheelite-type phase. The high-pressure phase remains stable up to 21 GPa, the highest pressure reached in the present investigations. On pressure release, the scheelite phase is recovered. The crystal structure of the high-pressure phase and the equations of state for the zircon- and scheelite-type phases have been determined. Various compressibilities, such as the bulk, axial and bond compressibilities, estimated from the experimental data are found to be in good agreement with the results obtained from theoretical calculations. The calculated elastic constants show that the zircon structure becomes mechanically unstable beyond the transition pressure. Overall there is good agreement between the experimental and theoretical findings.
RESUMO
The compression process in the α-phase of europium trimolybdate was revised employing several experimental techniques. X-ray diffraction (using synchrotron and laboratory radiation sources), Raman scattering and photoluminescence experiments were performed up to a maximum pressure of 21 GPa. In addition, the crystal structure and Raman mode frequencies have been studied by means of first-principles density functional based methods. Results suggest that the compression process of α-Eu2(MoO4)3 can be described by three stages. Below 8 GPa, the α-phase suffers an isotropic contraction of the crystal structure. Between 8 and 12 GPa, the compound undergoes an anisotropic compression due to distortion and rotation of the MoO4 tetrahedra. At pressures above 12 GPa, the amorphization process starts without any previous occurrence of a crystalline-crystalline phase transition in the whole range of pressure. This behavior clearly differs from the process of compression and amorphization in trimolybdates with [Formula: see text]-phase and tritungstates with α-phase.