Synthesis of Silver, Gold, and Platinum Doped Zinc Oxide Nanoparticles by Pulsed Laser Ablation in Water.

In this paper, we propose a simple two-step method for the synthesis of Ag, Au, and Pt-doped ZnO nanoparticles. The method is based on the fabrication of targets using the pulsed laser deposition (PLD) technique where thin layers of metals (Ag, Pt, Au) have been deposited on a metal-oxide bulk substrate (ZnO). Such formed structures were used as a target for the production of doped nanoparticles (ZnO: Ag, ZnO: Au, and ZnO: Pt) by laser ablation in water. The influence of Ag, Au, and Pt doping on the optical properties, structure and composition, sizing, and morphology was studied using UV-Visible (UV-Vis) and photoluminescence (PL) spectroscopies, X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), scanning electron microscopy (SEM), and transmission electron microscopy (TEM), respectively. The band-gap energy decreased to 3.06, 3.08, and 3.15 for silver, gold, and platinum-doped ZnO compared to the pure ZnO (3.2 eV). PL spectra showed a decrease in the recombination rate of the electrons and holes in the case of doped ZnO. SEM, TEM, and AFM images showed spherical-shaped nanoparticles with a relatively smooth surface. The XRD patterns confirm that Ag, Au, and Pt were well incorporated inside the ZnO lattice and maintained a hexagonal wurtzite structure. This work could provide a new way for synthesizing various doped materials.

Enhancement of Methylene Blue Photodegradation Rate Using Laser Synthesized Ag-Doped ZnO Nanoparticles.

In this work, Ag-doped ZnO nanoparticles are obtained via pulsed laser ablation of the Ag-coated ZnO target in water. The ratio of Ag dopant in ZnO nanoparticles strongly depends on the thickness of the Ag layer at the ZnO target. Synthesized nanoparticles were characterized by XRD, XPS, SEM, EDS, ICP-OES, and UV-VIS spectrophotometry to obtain their crystal structure, elemental composition, morphology and size distribution, mass concentration, and optical properties, respectively. The photocatalytic studies showed photodegradation of methylene blue (MB) under UV irradiation. Different ratios of Ag dopant in ZnO nanoparticles influence the photodegradation rate. The ZnO nanoparticles doped with 0.32% silver show the most efficient photodegradation rate, with the chemical reaction constant of 0.0233 min-1. It exhibits an almost twice as large photodegradation rate compared to pure ZnO nanoparticles, showing the doping effect on the photocatalytic activity.

'Sandwich'-like hybrid ZnO thin films produced by a combination of atomic layer deposition and wet-chemistry using a mercapto silane as single organic precursor.

This study describes a straightforward preparation of hybrid organic-inorganic thin films containing a stable 'sandwich'-like structure of two atomic layer deposited (ALD) ZnO layers separated by a thin organosilane phase, which is built from a single organic component (3-mercaptopropyl)trimethoxysilane (MPTMS). Grafting of MPTMS on the first ALD ZnO layer was performed in solution and driven by the strong affinity of the terminal thiol functionality (-SH) towards ZnO. We demonstrate that under different reaction conditions, either MPTMS monolayers are prepared or a 5 nm thick cross-linked polymeric network is formed due to the self-condensation of silane, which covers the ALD ZnO surface. This film served as a soft template for the nucleation of an ALD ZnO top layer by creation of S-Zn and Si-O-Zn bonds at the upper interface, as confirmed by XPS measurements. An increase in surface roughness, as compared to the initial ZnO film, is observed after removal of the organic layer from the hybrid structure by calcination, which is accompanied by an improvement in UVA photocatalytic activity towards the degradation of methyl orange dye. Thus, MPTMS can be used as a sacrificial agent in combination with low temperature ALD processes for building rougher and photocatalytically efficient ZnO coatings.