Residual thermal stress simulation in three-dimensional molar crown systems: a finite element analysis.

PURPOSE: To simulate coefficient of thermal expansion (CTE)-generated stress fields in monolithic metal and ceramic crowns, and CTE mismatch stresses between metal, alumina, or zirconia cores and veneer layered crowns when cooled from high temperature processing. MATERIALS AND METHODS: A 3D computer-aided design model of a mandibular first molar crown was generated. Tooth preparation comprised reduction of proximal walls by 1.5 mm and of occlusal surfaces by 2.0 mm. Crown systems were monolithic (all-porcelain, alumina, metal, or zirconia) or subdivided into a core (metallic, zirconia, or alumina) and a porcelain veneer layer. The model was thermally loaded from 900°C to 25°C. A finite element mesh of three nodes per edge and a first/last node interval ratio of 1 was used, resulting in approximately 60,000 elements for both solids. Regions and values of maximum principal stress at the core and veneer layers were determined through 3D graphs and software output. RESULTS: The metal-porcelain and zirconia-porcelain systems showed compressive fields within the veneer cusp bulk, whereas alumina-porcelain presented tensile fields. At the core/veneer interface, compressive fields were observed for the metal-porcelain system, slightly tensile for the zirconia-porcelain, and higher tensile stress magnitudes for the alumina-porcelain. Increasingly compressive stresses were observed for the metal, alumina, zirconia, and all-porcelain monolithic systems. CONCLUSIONS: Variations in residual thermal stress levels were observed between bilayered and single-material systems due to the interaction between crown configuration and material properties.

Thermal/mechanical simulation and laboratory fatigue testing of an alternative yttria tetragonal zirconia polycrystal core-veneer all-ceramic layered crown design.

This study evaluated the stress levels at the core layer and the veneer layer of zirconia crowns (comprising an alternative core design vs. a standard core design) under mechanical/thermal simulation, and subjected simulated models to laboratory mouth-motion fatigue. The dimensions of a mandibular first molar were imported into computer-aided design (CAD) software and a tooth preparation was modeled. A crown was designed using the space between the original tooth and the prepared tooth. The alternative core presented an additional lingual shoulder that lowered the veneer bulk of the cusps. Finite element analyses evaluated the residual maximum principal stresses fields at the core and veneer of both designs under loading and when cooled from 900 degrees C to 25 degrees C. Crowns were fabricated and mouth-motion fatigued, generating master Weibull curves and reliability data. Thermal modeling showed low residual stress fields throughout the bulk of the cusps for both groups. Mechanical simulation depicted a shift in stress levels to the core of the alternative design compared with the standard design. Significantly higher reliability was found for the alternative core. Regardless of the alternative configuration, thermal and mechanical computer simulations showed stress in the alternative core design comparable and higher to that of the standard configuration, respectively. Such a mechanical scenario probably led to the higher reliability of the alternative design under fatigue.