Synthesis and Sensing Response of Magnesium Antimoniate Oxide (MgSb2O6) in the Presence of Propane Atmospheres at Different Operating Voltages.

Nanoparticles of MgSb2O6 were synthesized using a microwave-assisted wet chemistry method, followed by calcination at 700 °C. Their ability to detect different concentrations of propane gas (C3H8) at various operating voltages was evaluated. The material's crystalline phase was identified using X-ray powder diffraction (XRD). The morphology was analyzed by scanning electron microscopy (SEM), finding bar- and polyhedron-type geometries. Through transmission electron microscopy (TEM), we found particle sizes of 8.87-99.85 nm with an average of ~27.63 nm. Employing ultraviolet-visible (UV-Vis) spectroscopy, we found a band gap value of ~3.86 eV. Thick films made with MgSb2O6 powders were exposed to atmospheres containing 150, 300, 400, and 600 ppm of propane gas for dynamic testing. The time-dependent sensitivities were ~61.09, ~88.80, ~97.65, and ~112.81%. In addition, tests were carried out at different operating voltages (5-50 V), finding very short response and recovery times (~57.25 and ~18.45 s, respectively) at 50 V. The excellent dynamic response of the MgSb2O6 is attributed mainly to the synthesis method because it was possible to obtain nanometric-sized particles. Our results show that the trirutile-type oxide MgSb2O6 possesses the ability, efficiency, and thermal stability to be applied as a gas sensor for propane.

Photocatalytic Evaluation and Application as a Sensor for the Toxic Atmospheres (Propane and Carbon Monoxide) of Nickel Antimonate (NiSb2O6) Powders.

Nickel antimonate (NiSb2O6) powders were synthesized using a wet chemistry process assisted by microwave radiation and calcination from 600 to 700 °C to evaluate their photocatalytic and gas-sensing properties. The crystalline phase obtained at 800 °C of trirutile-type nickel antimonate was confirmed with powder X-ray diffraction. The morphology and size of the nanostructures were analyzed employing electron microscopy (SEM and TEM), identifying irregular particles and microrods (~277 nm, made up of polyhedral shapes of size ~65 nm), nanorods with an average length of ~77 nm, and nanostructures of polyhedral type of different sizes. UV-vis analysis determined that the bandgap of the powders obtained at 800 °C was ~3.2 eV. The gas sensing tests obtained a maximum response of ~5 for CO (300 ppm) at 300 °C and ~10 for C3H8 (500 ppm) at 300 °C. According to these results, we consider that NiSb2O6 can be applied as a gas sensor. On the other hand, the photocatalytic properties of the antimonate were examined by monitoring the discoloration of malachite green (MG) at five ppm. MG concentration monitoring was carried out using UV-visible spectroscopy, and 85% discoloration was achieved after 200 min of photocatalytic reaction.