Abrasion Wear Resistance of Precipitation-Hardened Al-Zn-Mg Alloy.

The heat treatment of aluminum alloys is very important in industries where low weight in combination with high wear resistance, good strength, and hardness are important. However, depending on their chemical composition, aluminum alloys are subjected to different mechanical and thermal treatments to achieve the most favorable properties. In this study, an Al-Zn-Mg alloy was heat-treated including solution annealing at 490 °C for 1 h with subsequent artificial aging at 130, 160, and 190 °C for 1, 5, and 9 h. The hardness (HV1) and abrasive wear resistance with three different abrasive grain sizes were measured for all samples. The highest hardness was measured for the samples artificially aged at 130 °C/5 h, 227 HV1, while the lowest hardness was measured for the samples aged at 190 °C/9 h. The highest and the lowest wear resistance was also observed for the same state, i.e., artificially aged at 130 °C/5 h and 190 °C/9 h, respectively. The critical abrasive grain size was detected for some samples, where a decrease in wear rate was observed with an increase in the abrasive grain size from the medium value to the largest. The Response Surface Methodology (RSM) was applied to demonstrate the influence of the input parameters on the material wear rate.

The Effect of Foaming Agents on the Thermal Behavior of Aluminum Precursors.

Various foaming agents can be used to achieve foaming of the precursors obtained by using the powder metallurgy method. However, the thermal behavior of pure aluminum precursors with different foaming agents has been studied very little in recent times. For the production of aluminum foams with closed cells, 1 wt.% of calcium carbonate (CaCO3), titanium hydride (TiH2), heat-treated TiH2 and zirconium hydride (ZrH2) were used. The foaming capability of the compacted precursors was investigated at temperatures 700, 720 and 750 °C. CaCO3 and TiH2 showed the best foamability at all considered temperatures, while ZrH2 achieved relatively good foaming only at the highest temperature, 750 °C. Due to their low onset temperature of the decomposition compared to the melting point of the unalloyed aluminum, in hydride-based foaming agents the drainage occurred at the bottom part of the foam samples. Among the investigated foaming agents, precursors with heat-treated TiH2 had the worst foaming properties, while CaCO3 showed the best foamability without the occurrence of drainage.