Zirconia enriched dental adhesive: a solution for OCT contrast enhancement. Demonstrative study by synchrotron radiation microtomography.

OBJECTIVE: The major aim of this study was to prove the capability of the optical coherence tomography (OCT) method in visualizing the integrity of the adhesive fillings and of the interfaces between the adhesive, tooth structures and composite resin. As zirconium dioxide was added to the composition of the adhesive layer in order to strengthen the backscattered light in the OCT investigation, for a better visualization of the interfaces, the determination of a proper zirconia concentration was another aim of our study. METHOD: Several class II cavities were prepared in human premolars and were filled with dental adhesive containing different zirconia concentrations and light-curing composite resin. Both OCT and synchrotron radiation microtomography (micro-CT) were used to analyse the morphology of the tooth-adhesive-composite interfaces and to investigate the adhesive layer. RESULTS: The pore distribution, both at the interfaces level and in the resin, and the analysis of the adhesive layer integrity were obtained. A good agreement between OCT and micro-CT analyses was observed in terms of detecting discontinuities in the adhesive layer. Furthermore, micro-CT showed that zirconia percentages in the adhesive higher than 20 vol.% lead to conglomerates formation, which can negatively influence mechanical properties. Meanwhile, OCT confirmed a factor of 3 for the contrast enhancement when 20% of zirconia was included in the adhesive composition. SIGNIFICANCE: The present study proved the capability of the OCT method in visualizing the morphology and integrity of zirconia doped tooth adhesive fillings, to be used for a further in vivo tool development.

Cervical microleakage in Class II cavities restored with the Sonicsys approx system.

OBJECTIVE: To investigate the cervical microleakage in Class II cavities restored with Sonicsys approx ceramic inserts and four resin-based materials. METHOD AND MATERIALS: Forty noncarious and crack-free mandibular third molars were used. These teeth were randomly assigned to four groups each containing 10 teeth. No control group was created. On each tooth, one mesial boxlike cavity was prepared using the active head Sonicsys approx no. 3. The cervical margin of each cavity was in enamel about 1 mm coronal to the cementoenamel junction. According to manufacturer's instructions, the prepared cavities were restored using a Sonicsys approx ceramic inserts no.3 and four resin-based materials as follows: group 1, Tetric Flow; group 2, Admira Flow; group 3, Nexus 2; group 4, X-Flow. After finishing and polishing, all specimens were stored in distilled water for 7 days at 37 degrees C, thermocycled 1,000 cycles between 5 degrees and 55 degrees C, and stored for 24 hours in basic fuchsine 2%. All specimens were then embedded in clear acrylic resin and sectioned along a mesial-distal plane through the middle of the cervical margin. The cervical areas of the resulting sections were examined using an optical microscope to assess the dye penetration. The registered scores were analyzed using Kruskal-Wallis and Mann-Whitney U tests. RESULTS: Microleakage was detected in each experimental group. Kruskal-Wallis test revealed statistically significant differences among groups (P = .009, alpha = .01). The Mann-Whitney U test showed significant differences between Admira Flow group and Tetric Flow (P = .011, alpha = .05), Nexus 2 (P = .001, alpha = .01), and X-Flow (P = .004, alpha = .01), respectively. CONCLUSION: Within the limitations of this study, the extent of microleakage in the cervical area (enamel) of Class II cavities restored with Sonicsys approx ceramic inserts depends on the material used for luting. The highest leakage occurred when Admira flow was used.