Characterization and Performance Analysis of Hydrolyzed versus Non-Hydrolyzed Poly(NVF-co-HEA) Hydrogels for Cosmetic Applications.

This study explores the synthesis and modification of poly(N-vinylformamide-co-N-hydroxyethyl acrylamide) (poly(NVF-co-HEA)) hydrogels for cosmetic applications. Poly(NVF-co-HEA) hydrogels were produced followed by an acid hydrolysis reaction to produce poly(NVF-co-VAm-co-HEA) hydrogels, introducing poly(vinyl amine) (PVAm) into the structure. This modification considerably alters the hydrogels' properties, yielding materials with over 96% water content, predominantly in the form of non-freezing or free water, which is beneficial in the uptake and release of hydrophilic species. The primary amine groups from inclusion of VAm also improved the mechanical properties, as evidenced by an 8-fold increase in Young's modulus. The hydrogels also possessed pH-responsive behavior, which was particularly noticeable under acidic and basic conditions, where a large decrease in water content was observed (40% to 75% reduction). Characterizing the hydrogels' release capabilities involved using organic dyes of different functional groups and sizes to examine the pH impact on release. The results indicated that hydrolyzed hydrogels interacted more effectively with charged species, highlighting their suitability for pH-responsive delivery. The release of cosmetic active ingredients was also demonstrated through the controlled release of Liquid Azelaic™, specifically potassium azeloyl diglycinate (PAD). Our findings reveal that the hydrolyzed hydrogels exhibit superior burst release, especially under alkaline conditions, suggesting their suitability for cosmetic applications where controlled, pH-responsive delivery of active ingredients is desired. Overall, this investigation highlights the potential of hydrolyzed poly(NVF-co-HEA) hydrogels in cosmetic applications. Their ability to combine high water content with mechanical integrity, along with their pH-responsive release ability, allows for use in cosmetic formulations.

Hydroquinine Enhances the Efficacy of Contact Lens Solutions for Inhibiting Pseudomonas aeruginosa Adhesion and Biofilm Formation.

P. aeruginosa is one of the most common bacteria causing contact lens-related microbial keratitis (CLMK). Previous studies report that disinfecting solutions were ineffective in preventing biofilm formation. Solutions containing novel natural agents may be an excellent alternative for reducing the risk of CLMK. Here, we investigate the disinfecting properties of hydroquinine in combination with multipurpose solutions (MPSs) to prevent P. aeruginosa adhesion and biofilm formation. We examined the antibacterial, anti-adhesion, and anti-biofilm properties of hydroquinine-formulated MPSs compared to MPSs alone. Using RT-qPCR, hydroquinine directly affected the expression levels of adhesion-related genes, namely, cgrC, cheY, cheZ, fimU, and pilV, resulting in reduced adhesion and anti-biofilm formation. Using ISO 14729 stand-alone testing, hydroquinine met the criteria (>99.9% killing at disinfection time) against both P. aeruginosa reference and clinical strains. Using the crystal violet retention assay and FE-SEM, MPSs combined with hydroquinine were effective in inhibiting P. aeruginosa adhesion and destroying preexisting biofilms. This report is the first to highlight the potential utility of hydroquinine-containing formulations as a disinfecting solution for contact lenses, specifically for inhibiting adhesion and destroying biofilm. These findings may aid in the development of novel disinfectants aimed at combating P. aeruginosa, thereby potentially reducing the incidence of CLMK.

In Vitro Wound Healing Potential of a Fibroin Film Incorporating a Cannabidiol/2-Hydroxypropyl-ß-cyclodextrin Complex.

This study aimed to develop a film dressing prepared by incorporating a complex of cannabidiol and 2-hydroxypropyl-ß-cyclodextrin (CBD/HP-ß-CD) into a fibroin-based film and to investigate its wound healing capabilities. The fibroin from silkworm cocoons exhibited a total protein content of 96.34 ± 0.14% w/w and a molecular weight range of 25 to 245 kDa. Fourier-transform infrared spectroscopy (FTIR) revealed the presence of characteristic amide peaks (I, II, and III) in the isolated fibroin. The CBD/HP-ß-CD complex, prepared with a molar ratio of 1:2 (CBD to HP-ß-CD), had 81.5 ± 1.2% w/w CBD content, as determined by high-performance liquid chromatography (HPLC). X-ray diffraction (XRD) and FTIR analyses demonstrated successful encapsulation of CBD's hydrophobic aromatic rings by HP-ß-CD. Blending the fibroin solution with the CBD/HP-ß-CD complex produced a transparent, slightly yellowish film. Mechanical testing revealed a tensile strength of 48.67 ± 2.57 MPa and a % elongation at a break of 1.71 ± 0.21%. XRD and FTIR analyses showed distinctive crystalline and chemical structures of the film. In subsequent in vitro experiments with normal human dermal fibroblasts, the film demonstrated potential for wound healing. An increase in cell division (G2/M phase) was observed compared to the fibroin film without the CBD/HP-ß-CD complex. Additionally, fibroblasts treated with the film exhibited enhanced cell migration in a scratch assay and increased expression of vascular endothelial growth factor protein compared to the control group. Overall, these findings underscore the film's potential for enhancing wound healing outcomes.

Porous Poly(2-hydroxyethyl methacrylate) Hydrogel Scaffolds for Tissue Engineering: Influence of Crosslinking Systems and Silk Sericin Concentration on Scaffold Properties.

Tailored porous structures of poly(2-hydroxyethyl methacrylate) (PHEMA) and silk sericin (SS) were used to create porous hydrogel scaffolds using two distinct crosslinking systems. These structures were designed to closely mimic the porous nature of the native extracellular matrix. Conventional free radical polymerization of 2-hydroxyethyl methacrylate (HEMA) was performed in the presence of different concentrations of SS (1.25, 2.50, 5.00% w/v) with two crosslinking systems. A chemical crosslinking system with N'N-methylene bisacrylamide (MBAAm) and a physical crosslinking system with dimethylurea (DMU) were used: C-PHEMA/SS (crosslinked using MBAAm) and C-PHEMA/pC-SS (crosslinked using MBAAm and DMU). The focus of this study was on investigating the impact of these crosslinking methods on various properties of the scaffolds, including pore size, pore characteristics, polymerization time, morphology, molecular interaction, in vitro degradation, thermal properties, and in vitro cytotoxicity. The various crosslinked networks were found to appreciably influence the properties of the scaffolds, especially the pore sizes, in which smaller sizes and higher numbers of pores with high regularity were seen in C-PHEMA/1.25 pC-SS (17 ± 2 µm) than in C-PHEMA/1.25 SS (34 ± 3 µm). Semi-interpenetrating networks were created by crosslinking PHEMA-MBAAm-PHEMA while incorporating free protein molecules of SS within the networks. The additional crosslinking step involving DMU occurred through hydrogen bonding of the -C=O and -N-H groups with the SS, resulting in the simultaneous incorporation of DMU and SS within the PHEMA networks. As a consequence of this process, the scaffold C-PHEMA/pC-SS exhibited smaller pore sizes compared to scaffolds without DMU crosslinking. Moreover, the incorporation of higher loadings of SS led to even smaller pore sizes. Additionally, the gelation time of C-PHEMA/pC-SS was delayed due to the presence of DMU in the crosslinking system. Both porous hydrogel scaffolds, C-PHEMA/pC-SS and PHEMA, were found to be non-cytotoxic to the normal human skin dermal fibroblast cell line (NHDF cells). This promising result indicates that these hydrogel scaffolds have potential for use in tissue engineering applications.

Exploring the Potential of Roselle Calyx and Sappan Heartwood Extracts as Natural Colorants in Poly(butylene Succinate) for Biodegradable Packaging Films.

Recently, there has been a growing concern among consumers regarding the safety of packaging products, particularly due to the presence of potentially harmful substances like synthetic pigments and inorganic dyes. These substances, which are often used to attract consumer attention, can migrate and contaminate products over extended shelf storage periods. To address this issue, the focus of this research was the development of a biodegradable packaging film using poly(butylene succinate) (PBS) incorporated with natural colorants extracted from roselle (RS) and sappan heartwood (SP). RS and SP serve as non-toxic and alternative pigments when compared to synthetic colorants. The biodegradable packaging films were prepared using blown film extrusion, encompassing different weight percentages of RS and SP (0.1%, 0.2%, and 0.3%). The films exhibited distinct colors, with RS films appearing pink to purple and SP films exhibiting an orange hue. The water vapor transmission rate slightly decreased with an increasing content of RS and SP extracts, indicating improved barrier properties. Additionally, the films showed reduced light transmittance, as evidenced by the UV-Vis light barrier results. The degree of crystallinity in the films was enhanced, as confirmed by X-ray diffraction and differential scanning calorimetry techniques. Regarding mechanical properties, the PBS/RS and PBS/SP films exhibited slight increases in tensile strength and elongation compared to neat PBS films. Moreover, the blended films demonstrated higher stability after undergoing an aging test, further highlighting their potential for use in biodegradable packaging applications. The key advantages of these films lie in their non-toxicity, biodegradability, and overall environmental friendliness.

Hydroquinine Inhibits the Growth of Multidrug-Resistant Pseudomonas aeruginosa via the Suppression of the Arginine Deiminase Pathway Genes.

Hydroquinine has antimicrobial potential with demonstrated activity against several bacteria, including multidrug-resistant (MDR) P. aeruginosa reference strains. Despite this, there is limited evidence confirming the antibacterial activity of hydroquinine against clinical isolates and the underlying mechanism of action. Here, we aimed to investigate the antibacterial effect of hydroquinine in clinical P. aeruginosa strains using phenotypic antimicrobial susceptibility testing and synergistic testing. In addition, we examined the potential inhibitory mechanisms against MDR P. aeruginosa isolates using informatic-driven molecular docking analysis in combination with RT-qPCR. We uncovered that hydroquinine inhibits and kills clinical P. aeruginosa at 2.50 mg/mL (MIC) and 5.00 mg/mL (MBC), respectively. Hydroquinine also showed partial synergistic effects with ceftazidime against clinical MDR P. aeruginosa strains. Using SwissDock, we identified potential interactions between arginine deiminase (ADI)-pathway-related proteins and hydroquinine. Furthermore, using RT-qPCR, we found that hydroquinine directly affects the mRNA expression of arc operon. We demonstrated that the ADI-related genes, including the arginine/ornithine antiporter (arcD) and the three enzymes (arginine deiminase (arcA), ornithine transcarbamylase (arcB), and carbamate kinase (arcC)), were significantly downregulated at a half MIC of hydroquinine. This study is the first report that the ADI-related proteins are potential molecular targets for the inhibitory effect of hydroquinine against clinically isolated MDR P. aeruginosa strains.

Enhanced mechanical properties and biocompatibility of bacterial cellulose composite films with inclusion of 2D MoS2 and helical carbon nanotubes for use as antimicrobial drug carriers.

Bacterial cellulose (BC) is a biomaterial being investigated for a range of applications. Herein, BC films derived from nata de coco pieces are reinforced by two-dimensional molybdenum disulfide (MoS2) and helical carbon nanotubes (HCNTs) to enhance their tensile mechanical properties, and the biocompatibility of the BC composite films is demonstrated. A simple preparation is presented using a kitchen blender to disperse and blend the BC fibers and additives in a common fabrication medium, followed by vacuum filtration. The mechanical properties of the BC/MoS2/HCNTs composite films are enhanced due to the synergistic effect of MoS2 and HCNTs embedded in the BC films. The MoS2/HCNTs binary additive (1 phr) is capable of increasing the strength and Young's modulus by 148 % and 333 %, respectively, relative to the BC films. The cell cytotoxicity of the BC/MoS2/HCNTs films was assessed using an MTT assay. The composite films are biocompatible with a cell viability of L929 fibroblast cells >70 %, coupled with observations of direct cell attachment on the films. The composite films also exhibited good performance in absorbing and releasing gentamicin antibiotics to inhibit the growth of Escherichia coli and Staphylococcus aureus. The BC/MoS2/HCNTs films are thus potential BC-based candidates as biocompatible robust antibiotic carriers.

Reactive Blending of Modified Thermoplastic Starch Chlorhexidine Gluconate and Poly(butylene succinate) Blending with Epoxy Compatibilizer.

Biodegradable starch-based polymers were developed by melt-blending modified thermoplastic starch (MTPS) with poly(butylene succinate) (PBS) blended with epoxy resin (Er). A modified thermoplastic starch blend with chlorhexidine gluconate (MTPSCh) was prepared by melt-blending cassava starch with glycerol and chlorhexidine gluconate (CHG) 1.0% wt. The Er was melt-blended with PBS (PBSE) at concentrations of 0.50%, 1.0%, 2.5%, and 5.0% (wt%/wt%). The mechanical properties, water resistance, and morphology of the MTPSCh/PBSE blends were investigated. The MTPSCh/PBSE2.5% blend showed an improvement in tensile strength (8.1 MPa) and elongation at break (86%) compared to the TPSCh/PBS blend (2.6 MPa and 53%, respectively). In addition, water contact angle measurements indicated an increase in the hydrophobicity of the MTPSCh/PBSE blends. Thermogravimetric analysis showed an improvement in thermal stability when PBS was added to the MTPSCh blends. Fourier transform infrared spectroscopy data confirmed a new reaction between the amino groups of CHG in MTPSCh and the epoxy groups of Er in PBSE, which improved the interfacial adhesion of the MTPSCh/PBSE blends. This reaction improved the mechanical properties, water resistance, morphology, and thermal stability of the TPSCh/PBSE blends.

Development of Natural Active Agent-Containing Porous Hydrogel Sheets with High Water Content for Wound Dressings.

This work was concerned with the fabrication of a porous hydrogel system suitable for medium to heavy-exudating wounds where traditional hydrogels cannot be used. The hydrogels were based on 2-acrylamido-2-methyl-1-propane sulfonic acid (AMPs). In order to produce the porous structure, additional components were added (acid, blowing agent, foam stabilizer). Manuka honey (MH) was also incorporated at concentrations of 1 and 10% w/w. The hydrogel samples were characterized for morphology via scanning electron microscopy, mechanical rheology, swelling using a gravimetric method, surface absorption, and cell cytotoxicity. The results confirmed the formation of porous hydrogels (PH) with pore sizes ranging from ~50-110 µm. The swelling performance showed that the non-porous hydrogel (NPH) swelled to ~2000%, while PH weight increased ~5000%. Additionally, the use of a surface absorption technique showed that the PH absorbed 10 µL in <3000 ms, and NPH absorbed <1 µL over the same time. Incorporating MH the enhanced gel appearance and mechanical properties, including smaller pores and linear swelling. In summary, the PH produced in this study had excellent swelling performance with rapid absorption of surface liquid. Therefore, these materials have the potential to expand the applicability of hydrogels to a range of wound types, as they can both donate and absorb fluid.

Carboxymethyl cellulose/poly(vinyl alcohol) blended films reinforced by buckypapers of carbon nanotubes and 2D material (MoS2): Enhancing mechanical strength, toughness, and barrier properties.

Plastic waste is one cause of climate change. To solve this problem, packaging films are increasingly produced from biodegradable polymers. Eco-friendly carboxymethyl cellulose and its blends have been developed for such a solution. Herein, a unique strategy is demonstrated to improve the mechanical and barrier properties of carboxymethyl cellulose/poly(vinyl alcohol) (CMC/PVA) blended films for the packaging of nonfood dried products. The blended films were impregnated with buckypapers containing different combinations of multiwalled carbon nanotubes, two-dimensional molybdenum disulfide (2D MoS2) nanoplatelets, and helical carbon nanotubes (HCNTs). Compared to the blend, the polymer composite films exhibit significant increases in tensile strength (~105 %, from 25.53 to 52.41 MPa), Young's modulus (~297 %, from 155.48 to 617.48 MPa), and toughness (~46 %, from 6.69 to 9.75 MJ m-3). Polymer composite films containing HCNTs in buckypapers offer the highest toughness. For barrier properties, the polymer composite films are opaque. The water vapor transmission rate of the blended films decreases (~52 %, from 13.09 to 6.25 g h-1 m-2). Moreover, the maximum thermal-degradation temperature of the blend rises from 296 to 301 °C, especially for the polymer composite films with buckypapers containing MoS2 nanosheets that contribute to the barrier effect for both water vapor and thermal-decomposition gas molecules.

Development of Biocellulose Sheet Incorporating Aloe vera Gel Extract for Diabetic Wound Healing.

In this study, a biocellulose (BC) sheet containing Aloe vera gel extract (AE) was developed for application in healing chronic wounds, such as diabetic wounds. The BC sheet was produced by Acetobacter xylinum and then lyophilized to obtain dried sheets. A. vera gel was extracted by precipitation in 35% ammonium sulfate, lyophilized, dried, and incorporated into the BC sheet. The protein content of the AE was 12.32 ± 3.4% w/w, with a molecular weight of ∼20 kDa. The release of TNF-α from lipopolysaccharide-induced RAW264.7 cells was reduced by treatment with AE in a dose-dependent manner. The physicochemical and biological properties of the developed sheet were investigated. Morphological examination of the BC/AE sheet using scanning electron microscopy revealed the 3D construction of nanofibrils, which showed high porosity. The BC/AE sheet exhibited water absorption at 74%, and the release of proteins in the AE reached 97.23% at 4 h. The BC sheet incorporated with proteins in the AE at 283.78 ± 7.7 µg/cm2 can promote the wound healing in streptozotocin-induced diabetic rats. The recovering skin in diabetic wounds treated with the BC/AE sheet exhibited a normal cell arrangement without fibrosis, as revealed by histological staining. The research findings indicate that the BC/AE sheet has potential for applications in wound dressings.

Homo- and Copolymer Hydrogels Based on N-Vinylformamide: An Investigation of the Impact of Water Structure on Controlled Release.

This study investigated the performance of novel hydrogels based on poly (N-vinylformamide) (PNVF), copolymers of NVF with N-hydroxyethyl acrylamide (HEA) (P(NVF-co-HEA)), and 2-carboxyethyl acrylate (CEA) (P(NVF-co-CEA)), which were synthesized by photopolymerization using a UVLED light source. The hydrogels were analyzed for important properties such as equilibrium water content (%EWC), contact angle, freezing and non-freezing water, and diffusion-based in vitro release. The results showed that PNVF had an extremely high %EWC of 94.57%, while a decreasing NVF content in the copolymer hydrogels led to a decrease in water content with a linear relationship with HEA or CEA content. Water structuring in the hydrogels showed appreciably more variance, with ratios of free to bound water differing from 16.7:1 (NVF) to 1.3:1 (CEA), corresponding to PNVF having ~67 water molecules per repeat unit. The release studies of different dye molecules followed Higuchi's model, with the amount of dye released from the hydrogels depending on the amount of free water and the structural interactions between the polymer and the molecule being released. The results suggest that PNVF copolymer hydrogels have potential for controlled drug delivery by altering the polymer composition to govern the amount and ratio of free to bound water contained in the hydrogels.

In Situ Compatibilized Blends of PLA/PCL/CAB Melt-Blown Films with High Elongation: Investigation of Miscibility, Morphology, Crystallinity and Modelling.

Ternary-blended, melt-blown films of polylactide (PLA), polycaprolactone (PCL) and cellulose acetate butyrate (CAB) were prepared from preliminary miscibility data using a rapid screening method and optical ternary phase diagram (presented as clear, translucent, and opaque regions) as a guide for the composition selection. The compositions that provided optically clear regions were selected for melt blending. The ternary (PLA/PCL/CAB) blends were first melt-extruded and then melt-blown to form films and characterized for their tensile properties, tensile fractured-surface morphology, miscibility, crystallinity, molecular weight and chemical structure. The results showed that the tensile elongation at the break (%elongation) of the ternary-blended, melt-blown films (85/5/10, 75/10/15, 60/15/25 of PLA/PCL/CAB) was substantially higher (>350%) than pure PLA (ca. 20%). The range of compositions in which a significant increase in %elongation was observed at 55−85% w/w PLA, 5−20% w/w PCL and 10−25% w/w CAB. Films with high %elongation all showed good interfacial interactions between the dispersed phase (PCL and CAB) and matrix (PLA) in FE-SEM and showed improvements in miscibility (higher intermolecular interaction and mixing) and a decrease in the glass transition temperature, when compared to the low %elongation films. The decrease in Mw and Mn and the formation of the new NMR peaks (1H NMR at 3.68−3.73 ppm and 13C NMR at 58.54 ppm) were observed in only the high %elongation films. These are expected to be in situ compatibilizers that are generated during the melt processing, mostly by chain scission. In addition, mathematical modelling was used to study the optimal ratio and cost-effectiveness of blends with optimised mechanical properties. These ternary-blended, melt-blown films have the potential for use in both packaging and medical devices with excellent mechanical performance as well as inherent economic and environmental capabilities.

Antimicrobial thermoplastic starch reactive blend with chlorhexidine gluconate and epoxy resin.

An antimicrobial thermoplastic starch (TPS) was developed by melt-mixing TPS with chlorhexidine gluconate (CHG) and epoxy resin (Er). The tensile strength and hardness of the TPSCh blend increased with the addition of Er (TPSCh/Er), especially at 5 wt% Er (TPSCh/Er5) (19.5 MPa and 95 %, respectively). The water contact angle of TPSCh/Er was higher than those of TPS and TPSCh because of the improved interfacial tension. Fourier transform infrared and nuclear magnetic resonance analyses confirmed the reaction between the epoxy groups of Er, hydroxyl groups of starch, and amino groups of CHG. TPSCh/Er5 exhibited a significantly lower CHG release than TPSCh owing to the rearrangement of TPSCh chains via Er crosslinking. TPSCh/Er0.5 and TPSCh/Er1 showed inhibition zones against both tested bacteria (Staphylococcus aureus and Bacillus cereus), whereas TPSCh/Er2.5, TPSCh/Er5, and TPSCh/Er10 showed inhibition zones only against S. aureus. Moreover, TPSCh and TPSCh/Er0.5-2.5 exhibited inhibition zones with Saccharomyces cerevisiae.

High-Throughput Transcriptomic Profiling Reveals the Inhibitory Effect of Hydroquinine on Virulence Factors in Pseudomonas aeruginosa.

Hydroquinine is an organic alkaloid compound that exhibits antimicrobial activity against several bacterial strains including strains of both drug-sensitive and multidrug-resistant P. aeruginosa. Despite this, the effects of hydroquinine on virulence factors in P. aeruginosa have not yet been characterized. We therefore aimed to uncover the mechanism of P. aeruginosa hydroquinine-sensitivity using high-throughput transcriptomic analysis. We further confirmed whether hydroquinine inhibits specific virulence factors using RT-qPCR and phenotypic analysis. At half the minimum inhibitory concentration (MIC) of hydroquinine (1.250 mg/mL), 254 genes were differentially expressed (97 downregulated and 157 upregulated). We found that flagellar-related genes were downregulated by between −2.93 and −2.18 Log2-fold change. These genes were consistent with the analysis of gene ontology and KEGG pathway. Further validation by RT-qPCR showed that hydroquinine significantly suppressed expression of the flagellar-related genes. By analyzing cellular phenotypes, P. aeruginosa treated with ½MIC of hydroquinine exhibited inhibition of motility (30−54% reduction) and pyocyanin production (~25−27% reduction) and impaired biofilm formation (~57−87% reduction). These findings suggest that hydroquinine possesses anti-virulence factors, through diminishing flagellar, pyocyanin and biofilm formation.

Surface-Modified Polypyrrole-Coated PLCL and PLGA Nerve Guide Conduits Fabricated by 3D Printing and Electrospinning.

The efficiency of nerve guide conduits (NGCs) in repairing peripheral nerve injury is not high enough yet to be a substitute for autografts and is still insufficient for clinical use. To improve this efficiency, 3D electrospun scaffolds (3D/E) of poly(l-lactide-co-ε-caprolactone) (PLCL) and poly(l-lactide-co-glycolide) (PLGA) were designed and fabricated by the combination of 3D printing and electrospinning techniques, resulting in an ideal porous architecture for NGCs. Polypyrrole (PPy) was deposited on PLCL and PLGA scaffolds to enhance biocompatibility for nerve recovery. The designed pore architecture of these "PLCL-3D/E" and "PLGA-3D/E" scaffolds exhibited a combination of nano- and microscale structures. The mean pore size of PLCL-3D/E and PLGA-3D/E scaffolds were 289 ± 79 and 287 ± 95 nm, respectively, which meets the required pore size for NGCs. Furthermore, the addition of PPy on the surfaces of both PLCL-3D/E (PLCL-3D/E/PPy) and PLGA-3D/E (PLGA-3D/E/PPy) led to an increase in their hydrophilicity, conductivity, and noncytotoxicity compared to noncoated PPy scaffolds. Both PLCL-3D/E/PPy and PLGA-3D/E/PPy showed conductivity maintained at 12.40 ± 0.12 and 10.50 ± 0.08 Scm-1 for up to 15 and 9 weeks, respectively, which are adequate for the electroconduction of neuron cells. Notably, the PLGA-3D/E/PPy scaffold showed superior cytocompatibility when compared with PLCL-3D/E/PPy, as evident via the viability assay, proliferation, and attachment of L929 and SC cells. Furthermore, analysis of cell health through membrane leakage and apoptotic indices showed that the 3D/E/PPy scaffolds displayed significant decreases in membrane leakage and reductions in necrotic tissue. Our finding suggests that these 3D/E/PPy scaffolds have a favorable design architecture and biocompatibility with potential for use in peripheral nerve regeneration applications.

The analytical and biomedical applications of carbon dots and their future theranostic potential: A review.

In recent years, carbon dots (C-dots) have gained appreciable interest owing to their unique optical properties, including tunable fluorescence, stability against photobleaching and photoblinking, and strong fluorescence. Simple and low-cost hydrothermal and electrochemical approaches have been widely used in the preparation of biocompatible and high-quality C-dots. Various C-dots have been used for the quantitation of small analytes, mostly based on analyte induced fluorescence quenching. Depending on the nature of precursors, synthetic conditions (such as reaction temperature and time), and surface conjugation, multi-function C-dots can be prepared and used in diagnostics and therapeutics. Their strong fluorescence and photostability, enables use in cell imaging. Their biological activity from the surface residues and capability of generating reactive oxygen species, have allowed many C-dots to become candidates as antibacterial and anticancer reagents. After suitable conjugation, biocompatible and fluorescent C-dots can be used for diagnostics and therapeutics, thus, showing their great potential in the area of theranostics.

Bioactive Nanocomposites for Tissue Repair and Regeneration: A Review.

This review presents scientific findings concerning the use of bioactive nanocomposites in the field of tissue repair and regeneration. Bioactivity is the ability of a material to incite a specific biological reaction, usually at the boundary of the material. Nanocomposites have been shown to be ideal bioactive materials due the many biological interfaces and structures operating at the nanoscale. This has resulted in many researchers investigating nanocomposites for use in bioapplications. Nanocomposites encompass a number of different structures, incorporating organic-inorganic, inorganic-inorganic and bioinorganic nanomaterials and based upon ceramic, metallic or polymeric materials. This enables a wide range of properties to be incorporated into nanocomposite materials, such as magnetic properties, MR imaging contrast or drug delivery, and even a combination of these properties. Much of the classical research was focused on bone regeneration, however, recent advances have enabled further use in soft tissue body sites too. Despite recent technological advances, more research is needed to further understand the long-term biocompatibility impact of the use of nanoparticles within the human body.