Evaluation of Starch-Garlic Husk Polymeric Composites through Mechanical, Thermal, and Thermo-Mechanical Tests.

The present work evaluates the influence of different properties of composite materials from natural sources. Films were prepared using the evaporative casting technique from corn starch reinforced with a waste material such as garlic husk (GH), using glycerin as a plasticizer. The results of the syntheses carried out demonstrated the synergy between these materials. In the morphological analysis, the compatibility and adequate dispersion of the reinforcer in the matrix were confirmed. Using Fourier transform infrared spectroscopy (FTIR), the interaction and formation of bonds between the matrix and the reinforcer were confirmed by the presence of some signals such as S-S and C-S. Similarly, thermogravimetric analysis (TGA) revealed that even at low concentrations, GH can slightly increase the decomposition temperature. Finally, from the results of dynamic mechanical analysis (DMA), it was possible to identify that the storage modulus increases significantly, up to 115%, compared to pure starch, especially at low concentrations of the reinforcer.

Evaluation of Thermal Properties of Composites Prepared from Pistachio Shell Particles Treated Chemically and Polypropylene.

The purpose of the present work was to prepare polypropylene (PP) matrix composited filled with chemically treated pistachio shell particles (PTx), and evaluate their effect on the composites' thermal properties. PP-PTx composites were formulated in different PTx content (from 2 to 10 phr) in a mixing chamber, using the melt-mixing process. The PTx were chemically treated using a NaOH solution and infrared spectroscopy (FTIR). According to thermogravimetric analysis (TGA), the treatment of pistachio shell particles resulted in the remotion of lignin and hemicellulose. The thermal stability was evaluated by means of TGA, where the presence of PTx in composites showed a positive effect compared with PP pristine. Thermal properties such as crystallization temperature (Tc), crystallization enthalpy (∆Hc), melting temperature (Tm) and crystallinity were determinate by means differential scanning calorimetry (DSC); these results suggest that the PTx had a nucleation effect on the PP matrix, increasing their crystallinity. Dynamic mechanical analysis (DMA) showed that stiffness of the composites increase compared with that PP pristine, as well as the storage modulus, and the best results were found at a PTx concentration of 4 phr. At higher concentrations, the positive effect decreased; however, they were better than the reference PP.