A novel organo-zeolite adduct for environmental applications: sorption of phenol.

A novel organo-zeolite adduct has been synthesized by sorbing humic acids (HA) onto zeolitic tuff and then heating the resulting complex at 330°C for 1.5h. Desorption tests showed that this procedure effectively immobilized HA on the tuff. The crystal structure of the zeolitic tuff and the chemical structure of HA were not altered during the preparation. Phenol sorption analysis demonstrated that the HA-zeolite adduct had good sorbing properties; moreover, the sorbed amount markedly decreased with increased ionic strength. These results point to prospective application of the HA-zeolite adduct as a low-cost and environmentally friendly sorbent for water purification from phenol and possibly other neutral organic pollutants.

Removal of humic substances from water by means of calcium-ion-enriched natural zeolites.

The ability of the natural zeolited Neapolitan Yellow Tuff (NYT) enriched with calcium ions to remove humic acids from water was evaluated by batch adsorption equilibrium tests and dynamic experiments carried out by percolating humic acid solutions through a small NYT column (breakthrough curves). Under the experimental condition explored, the sorption capacity increases with the ionic strength and has the highest value at pH 7.4. The partition coefficient for a low concentration of humic acid ([humic acid] --> 0), at pH 7.4 in 0.01 M sodium chloride, was approximately 1000 L/kg, versus the value of approximately 100 L/kg in the absence of the alkaline metal salt. Therefore, after humic acids have been adsorbed in a column filled with the calcium-ion-enriched tuff, a reduction of the salt concentration in the ongoing solution enhances the release of the adsorbed material. These findings show that NYT can be used for the removal of humic acids from water.