A novel porcine dentin-derived bone graft material provides effective site stability for implant placement after tooth extraction: a randomized controlled clinical trial.

OBJECTIVES: Assessment of the clinical performance of a porcine dentin-derived particulate bone graft material for bone regeneration after tooth extraction with implant placement at 4 months, in comparison to a commercially available porcine bone-derived graft. MATERIAL AND METHODS: This study was a randomized, parallel-group, semi-double-blinded clinical trial evaluating the clinical safety, tolerability, and performance of Ivory Dentin Graft™ in comparison with a commercial bone-derived material in alveolar ridge preservation following tooth extraction (registered at ClinicalTrials.gov, May 12th, 2017, Identifier NCT03150472). Extraction sites were grafted with test or comparator material and a titanium implant placed at 4 months after taking a graft site biopsy. Primary endpoints were the extent of new bone growth and bone-graft integration at 4 months. RESULTS: The dentin graft material had statistically significantly more new bone formation (60.75% vs 42.81%, p = 0.0084, N = 20 vs 16), better bone-graft integration scores (good integration in 85% vs 40%, p = 0.0066), and higher mean radiodensity of the bone (981.5HU vs 727.7HU, p = 0.0011) at the graft site compared to the bone-derived material. The mean implant insertion torque force was similar for the dentin and bone materials (34.75 Ncm vs 34.06 Ncm). Titanium implant placement was successful in 95% of patients with the dentin graft material compared to 81.25% for the bone graft. Both materials had similar clinical safety and tolerability as determined by adverse events and local site reactions. Physician-assessed ease of grafting and ease of implant placement on a 10-point scale showed no statistical differences (8.78 vs 8.27, p = 0.2355; 8.05 vs 8.75, p = 0.1118, respectively). CONCLUSIONS: A porcine dentin-derived bone graft material has clinical safety, tolerability, and performance for implant placement at 4 months after tooth extraction at least as good as a commercial bone-derived material. CLINICAL RELEVANCE: The availability of porcine dentin-derived bone graft material allows wider use of dentin-derived material which has so far only been available in the form of autologous dentin from the patient's own teeth.

Dentin Particulate for Bone Regeneration: An In Vitro Study.

The aim of this in vitro study was to investigate the commitment and behavior of dental pulp stem cells (DPSCs) seeded onto two different grafting materials, human dentin particulate (DP) and deproteinized bovine bone matrix (BG), with those cultured in the absence of supplements. Gene expression analyses along with epigenetic and morphological tests were carried out to examine odontogenic and osteogenic differentiation and cell proliferation. Compressive testing of the grafting materials seeded with DPSCs was performed as well. DPSC differentiation into odontoblast-like cells was identified from the upregulation of odontogenic markers (DSPP and MSX) and osteogenic markers (RUNX2, alkaline phosphatase, osteonectin, osteocalcin, collagen type I, bmp2, smad5/8). Epigenetic tests confirmed the presence of miRNAs involved in odontogenic or osteogenic commitment of DPSCs cultured for up to 21 days on DP. Compressive strength values obtained from extracellular matrix (ECM) synthesized by DPSCs showed a trend of being higher when seeded onto DP than onto BG. High expression of VEGF factor, which is related to angiogenesis, and of dentin sialoprotein was observed only in the presence of DP. Morphological analyses confirmed the typical phenotype of adult odontoblasts. In conclusion, the odontogenic and osteogenic commitment of DPSCs and their respective functions can be achieved on DP, which enables exceptional dentin and bone regeneration.

A new procedure for processing extracted teeth for immediate grafting in post-extraction sockets. An experimental study in American Fox Hound dogs.

OBJECTIVES: To investigate freshly extracted dental particulate used to graft post-extraction sockets in dogs, comparing new bone formation at experimental and control sites. MATERIALS AND METHODS: Bilateral premolars P2, P3, P4 and first mandibular molars were extracted atraumatically from six American Fox Hound dogs. The teeth were ground immediately using a 'Smart Dentin Grinder'. The dentin particulate was sieved to ensure a grain size of 300-1200µm and immersed in an alcohol cleanser to dissolve organic debris and bacteria, followed by washing in sterile saline buffer solution. The animals were divided into two groups randomly: group 'A' (control) samples were left to heal without any extraction socket grafting procedure; group 'B' (experimental) sockets were filled with the autogenous dentin particulate graft. The rate of tissue healing and the quantity of bone formation were evaluated using histological and histomorphometric analyses at 60 and 90 days post-grafting. The type of bone generated was categorized as woven (immature bone) or lamellar bone (mature bone). RESULTS: Substantially more bone formation was found in Group B (experimental) than Group A (control) at 60 and 90 days (p<0.05). Less immature bone was identified in the dentin grafted group (25.7%) than the control group (55.9%) [corrected]. Similar differences were also observed at 90 days post grafting. CONCLUSION: Autogenous dentin particulate grafted immediately after extractions may be considered a useful biomaterial for socket preservation, protecting both buccal and lingual plates, generating large amounts of new woven bone formation after 60 days, and small amounts of lamellar bone after 90 days healing.