Bonding effectiveness of self-etch adhesives to dentin after 24 h water storage.

PURPOSE: This study evaluated the immediate bonding effectiveness of five self-etch adhesive systems bonded to dentin. MATERIALS AND METHODS: The microtensile bond strength of five self-etch adhesives systems, including one two-step and four one-step self-etch adhesives to dentin, was measured. Human third molars had their superficial dentin surface exposed, after which a standardized smear layer was produced using a medium-grit diamond bur. The selected adhesives were applied according to their respective manufacturer's instructions for µTBS measurement after storage in water at 37°C for 24 h. RESULTS: The µTBS varied from 11.1 to 44.3 MPa; the highest bond strength was obtained with the two-step self-etch adhesive Clearfil SE Bond and the lowest with the one-step self-etch adhesive Adper Prompt L-Pop. Pretesting failures mainly occurring during sectioning with the slow-speed diamond saw were observed only with the one-step self-etch adhesive Adper Prompt L-Pop (4 out of 18). CONCLUSIONS: When bonded to dentin, the self-etch adhesives with simplified application procedures (one-step self-etch adhesives) still underperform as compared to the two-step self-etch adhesive Clearfil SE Bond.

Root canal shaping by single-file systems and rotary instruments: a laboratory study.

INTRODUCTION: The aim of this study was to compare the shaping ability of two single-file systems and conventional rotary instruments in severely curved root canals of extracted human molars. METHODS AND MATERIALS: Mesiobuccal canals of 120 mandibular molars with angles of curvature ranging between 25(°) and 35(°) and radii of curvature from 5 to 9 mm, were divided into three groups (n=40). In each group the canals were instrumented with either WaveOne (W), Reciproc (R) or ProTaper (P). The time required for canal shaping and the frequency of broken instruments were recorded. The standardized pre and post-instrumentation radiographs were taken to determine changes in working length (WL) and straightening of canal curvature. The presence of blockage or perforation was also evaluated. Data were analyzed using the one-way analysis of variance (ANOVA) and post-hoc Tukey's test. The level of significance was set at 0.05. RESULTS: Both single-instrument systems reduced the canal preparation time by approximately 50% (P<0.05). No incidence of broken instruments from single-file systems was reported; however, two F2 instruments in the P group were broken (P<0.05). Reduction in WL and straightening of canal curvature was observed in all three systems with the highest scores belonging to P system (P<0.05). No case of blockage or perforation was found during shaping in any group. CONCLUSION: Single-file systems shaped curved canals with substantial saving in time and a significant decrease in incidence of instrument separation, change in WL, and straightening of canal curvature.

One-year clinical evaluation of the bonding effectiveness of a one-step, self-etch adhesive in noncarious cervical lesion therapy.

This study evaluated the one-year clinical performance of a one-step, self-etch adhesive (Optibond All-in-One, Kerr, CA, USA) combined with a composite (Herculite XRV Ultra, Kerr Hawe, CA, USA) to restore NCCLs with or without prior acid etching. Restorations performed by the same practitioner were evaluated at baseline and after 3, 6, and 12 months using modified USPHS criteria. At 6 months, the recall rate was 100%. The retention rate was 84.2% for restorations with prior acid etching, but statistically significant differences were observed between baseline and 6 months. Without acid etching, the retention rate was 77%, and no statistically significant difference was noted between 3 and 6 months. Marginal integrity (93.7% with and 87.7% without acid etching) and discoloration (95.3% with and 92.9% without acid etching) were scored as Alpha or Bravo, with better results after acid etching. After one year, the recall rate was 58.06%. Loss of pulp vitality, postoperative sensitivity, or secondary caries were not observed. After one year retention rate was of 90.6% and 76.9% with and without acid conditioning. Optibond All-in-One performs at a satisfactory clinical performance level for restoration of NCCLs after 12 months especially after acid etching.

Microtensile bond strength and interfacial characterization of 11 contemporary adhesives bonded to bur-cut dentin.

OBJECTIVES: This study evaluated mechanically and ultra-morphologically 11 different adhesive systems bonded to dentin. METHODS: The microtensile bond strength (microTBS) of 11 contemporary adhesives, including two three-step etch&rinse, three two-step etch&rinse, two two-step self-etch and four one-step self-etch adhesives to dentin, were measured. The resultant interfacial ultra-structure at dentin was characterized by transmission electron microscopy (TEM). Human third molars had their superficial dentin surface exposed, after which a standardized smear layer was produced using a medium-grit diamond bur. The selected adhesives were applied according to their respective manufacturer's instructions for microTBS measurement after storage in water at 37 degrees C for 24 hours or for TEM interfacial characterization. RESULTS: The microTBS varied from 11.1 to 63.6 MPa; the highest bond strengths were obtained with the three-step etch&rinse adhesives and the lowest with one-step self-etch adhesives. TEM evaluation showed very different interaction patterns, especially for the self-etch adhesives. "Mild" self-etch adhesives demineralized the dentin surface sufficiently to provide micro-mechanical retention, while preserving hydroxyapatite within the hybrid layer to enable additional chemical interaction. CONCLUSIONS: When bonded to dentin, the adhesives with simplified application procedures (in particular, one-step self-etch adhesives) still underperform as compared to conventional three-step adhesives. "Mild" two-step self-etch adhesives that provide additional chemical bonding appear to most optimally combine bonding effectiveness with a simplified application protocol.

Immediate bonding effectiveness of contemporary composite cements to dentin.

The objective of this study was to compare the one-week bonding effectiveness of nine contemporary composite cements used to lute ceramic to dentin and to determine an appropriate processing method for pretesting failures. The microtensile bond strengths (µTBS) of different luting agents including five self-adhesive cements (Unicem, 3 M ESPE; Maxcem, Kerr; Monocem, Shofu; G-Cem, GC; and Multilink Sprint, Ivoclar-Vivadent), two self-etch cements (Panavia F2.0 and Clearfil Esthetic Cement, Kuraray), and two etch-and-rinse cements (Calibra, Dentsply, and Variolink II, Ivoclar-Vivadent) were measured using a standardized protocol. As control, a two-step self-etch adhesive combined with a restorative composite (Clearfil SE+Clearfil APX, Kuraray) were included as luting material. Depending on the processing of the pretesting failures, two groups of cements could be distinguished: (1) those with low bond strength and many pretesting failures and (2) those with relatively high bond strength and few pretesting failures. Nevertheless, the control luting procedure involving a self-etch adhesive combined with a restorative composite presented with a significantly higher µTBS. The µTBS was clearly product-dependent rather than being dependent on the actual adhesive approach. Fracture analysis indicated that failure usually occurred at the dentin-cement interface especially for the cements with low bond strength and many pretesting failures. Depending on the cement system, an adequate immediate ceramic-to-dentin bond strength can be obtained, even with self-adhesive cements that do not use a separate dental adhesive. Yet, the self-etch adhesive Clearfil SE combined with the restorative composite revealed a superior bonding performance and should therefore be preferred in clinical situations where the restoration transmits light sufficiently.

Noncarious cervical lesions among a non-toothbrushing population with Hansen's disease (leprosy): initial findings.

OBJECTIVE: The purpose of this preliminary investigation was to examine the presence of noncarious cervical lesions (NCCLs) among a convenience sample of non-toothbrushing subjects with Hansen's disease (leprosy). METHOD AND MATERIALS: A cross-sectional sample of 102 non-toothbrushing subjects (20 to 77 years of age) was examined. The clinical parameter of interest for this study was the presence or absence of NCCLs and their probable etiology as it relates to the subjects' diet, occlusion, and use of medication. Subjects were examined clinically and interviewed according to study protocol. RESULTS: NCCLs were found in 48 subjects (47% of the studied sample). Widespread consumption of acidic foods and beverages acting as corrodents, signs of parafunction, and use of medication that causes xerostomia were also noted. Thus, all may be contributing factors in the etiology of NCCLs in this population. CONCLUSION: This preliminary report suggests that toothbrush/dentifrice abrasion was not a factor in the etiology of NCCLs in the population studied. The authors intend to expand their study among these non-toothbrushing