RESUMO
Assessment of the antimicrobial, micro tensile bond strength (µTBS), and degree of conversion (DC) of fifth-generation adhesive modified using photoactivated 0.5% rose bengal (RB) and photoactivated RB-doped titanium dioxide nanoparticles (TiO2NPs) in different concentrations (2% and 5%) as compared with the unmodified adhesive bonded to the carious affected dentin (CAD). Forty mandibular molars with caries progression up to the middle third of the dentin, as per the International Caries Detection and Assessment System (ICDAS) score of 4 and 5 were included. Specimens were divided into four groups based on etch and rinse adhesive (ERA) modification group 1: unmodified ERA, group 2: photoactivated 0.5% RB photosensitizer (PS) modified ERA, group 3: photoactivated RB-doped 2 wt% TiO2NPs adhesive, group 4: photoactivated RB-doped 5 wt% TiO2NPs adhesive. Followed by adhesive and composite restoration on the CAD surface. All the specimens were thermocycled and an assessment of µTBS and failure pattern analysis was performed. The antibacterial potency of RB and RB-doped TiO2NPs (2% and 5%) followed by their activation using visible light against Streptococcus mutans (S.mutans) were tested. The survival rate of S.mutans was assessed using the Kruskal-Wallis test. The analysis of µTBS involved the use of ANOVA, followed by a post-hoc Tukey honestly significant difference (HSD) multiple comparisons test. Group 1 (Unmodified ERA) (0.52 ± 0.31 CFU/mL) treated samples unveiled the highest means of bacterial survival and lowest µTBS (11.32 ± 0.63 MPa). Nevertheless, group 4: photoactivated RB-doped 5 wt% TiO2NPs adhesive displayed the lowest outcomes of S.mutans survival (0.11 ± 0.02 CFU/mL) and highest bond strength (18.76 ± 1.45 MPa). The photoactivated RB-doped 2 wt% TiO2NPs in adhesive demonstrated promising enhancements in both µTBS and antibacterial efficacy against S.mutans. However, it is noteworthy that this modification led to a decrease in the DC of the adhesive. RESEARCH HIGHLIGHTS: Unmodified ERA-treated samples unveiled the highest bacterial survival and the lowest µTBS. Photoactivated RB-doped 5 wt% TiO2NPs adhesive displayed the lowest S.mutans survival rate and highest bond strength. DC decreased with an increase in concentration of TiO2.
RESUMO
AIM: To investigate the effect of different cavity disinfectants, Phycocyanin (PC), Ocimum Sanctum (OS), and Ti Sapphire Laser, on the bond integrity and microleakage of resin restorations. MATERIAL AND METHOD: 60 human mandibular molars were extracted and prepared based on ICDAS scores of 4 and 5. To obtain the CAD surface, a visual examination was supported by tactile sensation and a dye for caries detection. Samples were randomly allocated into 4 groups based on cavity disinfectants applied (n = 15). Group 1: Specimens disinfected with CHX, Group 2: Specimens disinfected with Ti sapphire laser, Group 3: Specimens disinfected with Phycocyanin activated by Photodynamic therapy, and Group 4: Specimens disinfected with OS. Following the disinfection of the CAD surfaces, composite bulk-fill restorative material was bonded to each specimen and all samples were subjected to thermocycling. Ten samples from each group underwent SBS testing performed on a universal testing machine. Five samples were subjected to a microleakage analysis. RESULT: The maximum microleakage scores were displayed by Group 3: PC (0.521 nm) treated specimens. Whereas, and minimum microleakage was exhibited by Group 4: OS (0.471 nm). Group 4: OS (23.06±0.21 MPa) treated group displayed the maximum bond scores of resin adhesive to the CAD surface. However, Group 3: PC (21.67±0.24 MPa) treated specimens exhibited the lowest bond scores. Failure mode analysis revealed that among all the investigated groups the predominant type of failure was cohesive failure i.e., Group 1 (80%), Group 2 (80%), Group 3 (70%), and Group 4 (90%). CONCLUSION: Ocimum Sanctum, Phycocyanin activated by Photodynamic therapy, and Ti-sapphire laser for disinfection of caries-affected dentin have shown promise in terms of improved bond strength and reduced microleakage.