RESUMO
The proper treatment of lollingite is of great significance due to its rapid oxidation leading to release of arsenic into the environment. Herein, a green multi-solid waste geopolymer, consisting of red mud, metakaolin, blast furnace slag, and flue gas desulfurization gypsum, was developed. The obtained red mud-metakaolin-based (RMM) geopolymer demonstrated good arsenic retention capability. The results showed that the replacement of SO42- in ettringite with AsO42- via ion exchange, formation of Ca-As and Fe-As precipitates, and physical encapsulation with aluminosilicate gel were the main mechanisms that prevented the release of arsenic. Further dissolution of ettringite in RMM was alleviated by adding a suitable amount of Ca(OH)2 and controlling the pH of the leachate. TCLP results verified that RMM materials possessed an outstanding ability to stabilize arsenic, with a leaching rate below the permitted value of 5 mg/L for safe disposal. The low leachability of the RMM geopolymers (<0.50 mg/L) is potentially related to the pH buffering capacity of the hydration products at a pH range of 2-5. RMM geopolymers showed a high compressive strength (>15 MPa) and low arsenic leaching concentration (<2.66 mg/L) after 28 days of curing. These results demonstrate the potential of RMM geopolymers to be utilized as an environmentally friendly backfilling cementitious material for sustainable remediation of arsenic pollution.