Towards high-quality nitrogen-doped diamond single crystals for X-ray optics.

In this manuscript, characterization of single-crystalline (111) plates prepared from type-Ib diamonds with a nitrogen content of 100-150 ppm by means of high-resolution rocking-curve imaging (RCI) is reported. Contrary to common opinion regarding the intrinsically poor diffraction quality of type-I diamonds, RCI showed the presence of nearly defect-free areas of several millimetres squared in the central part of the diamond plates. The observed broadening of the rocking curves is a result of the cutting and polishing processes, causing strains around the edges of the plates and rare defects. An improvement of the preparation technique will thus allow single-crystalline diamond plates to be made for Laue and Bragg monochromators and beam splitters from type-Ib material with areas large enough to be used as optical elements at fourth-generation synchrotron facilities.

Diamond refractive micro-lenses for full-field X-ray imaging and microscopy produced with ion beam lithography.

We demonstrate that ion-beam lithography can be applied to the fabrication of rotationally parabolic refractive diamond X-ray micro-lenses that are of interest to the field of high-resolution X-ray focusing and microscopy. Three single half-lenses with curvature radii of 4.8 µm were produced and stacked to form a compound refractive lens, which provided diffraction-limited focusing of X-ray radiation at the P14 beamline of PETRA-III (DESY). As shown with SEM, the lenses are free of expressed low- and high-frequency shape modulations with a figure error of < 200 nm and surface roughness of 30 nm. Precise micro-manipulation and stacking of individual lenses are demonstrated, which opens up new opportunities for compact X-ray microscopy with nanometer resolution.