Quantitative Strain and Topography Mapping of 2D Materials Using Nanobeam Electron Diffraction.

It is known that 2D materials can exhibit a nonflat topography, which gives rise to an inherent strain. Since local curvature and strain influence mechanical, optical, and electrical properties, but are often difficult to distinguish from each other, a robust measurement technique is needed. In this study, a novel method is introduced, which is capable of obtaining quantitative strain and topography information of 2D materials with nanometer resolution. Relying on scanning nanobeam electron diffraction (NBED), it is possible to disentangle strain from the local sample slope. Using the positions of the diffraction spots of a specimen at two different tilts to reconstruct the locations and orientations of the reciprocal lattice rods, the local strain and slope can be simultaneously retrieved. We demonstrate the differences to strain measurements from a single NBED map in theory, simulation, and experiment. MoS2 monolayers with different shapes are used as simulation test structures. The slope and height information are recovered, as well as tensile and angular strain which have an absolute difference of less than 0.2% and 0.2° from the theoretical values. An experimental proof of concept using a freely suspended WSe2 monolayer together with a discussion of the accuracy of the method is provided.

Magnetic and Optical Properties of Gold-Coated Iron Oxide Nanoparticles.

In this work, magnetic and optical properties of magnetic nanoparticles were investigated, where the particles of iron oxide were prepared with a co-precipitation route and the component of gold was built up by reduction of AuCl4- on the surface of iron oxide to assemble nanocomposite structures in the form of an electrostatic stabilized suspension. The size of the particles obtained with TEM increased from of 8.9 ± 2.7 to 16 ± 6 nm after the procedure of hybridisation. In order to distinguish the impact of the gold on the optical properties, UV-Vis and Raman spectroscopy techniques were used. Magnetic properties were studied in the temperature range of 5-300 K and the superparamagnetic state of MNPs at room temperature was confirmed for both systems.