The study is devoted to X-ray fluorescence spectroscopy (XRF) features of micro- and nanosized powder mixtures of copper and nickel. XRF is a high accuracy method that allows for both qualitative and quantitative analysis. However, the XRF measurement error due to the size of the studied particles is not usually taken into account, which limits the use of the method in some cases, such as analysis of Ni-Cu mixtures and coatings. In this paper, a method for obtaining copper and nickel nanoparticles was investigated, and the XRF of powder compositions was considered in detail. The initial micro- and nanoparticles of copper and nickel were studied in detail using SEM, TEM, XRD, and EDX. Based on experimental data, calibration curves for copper-nickel powder compositions of various sizes were developed. According to the results, it was experimentally established that the calibration curves constructed for nanoscale and microscale powders differ significantly. The presented approach can be expanded for other metals and particle sizes.
RESUMO
In this study, the mechanism of nickel nanoparticle formation from its hydroxide was analyzed. Metallic nickel nanoparticles were obtained through the hydroxide's reduction under hydrogen. Nickel hydroxides were produced from nickel (II) nitrate hexahydrate and NaOH by deposition under various initial conditions. The influence of washing treatment on the dispersion of obtained nickel powders was studied. The washing procedure of precipitates was carried out by centrifugation, ultrasonic treatment, and decantation. X-ray diffractometry, transmission electron microscopy, low-temperature nitrogen adsorption, infrared spectroscopy, Raman spectroscopy, and X-ray photoelectron spectroscopy methods were used for nanoparticle characterization. Based on the resulting data, a model of the Ni(OH)2 aggregate structure after deposition was proposed. The number of nickel hydroxide particles required to form one nickel nanoparticle was estimated, and a model of its formation was proposed.