Influence of the Type of Soft Segment on the Selected Properties of Polyurethane Materials for Biomedical Applications.

This work presents the synthesis and characterization of new TPUs obtained by melt polyaddition using 1,1'-methanediylbis(4-isocyanatocyclohexane) (HMDI, Desmodur W®), a new unconventional chain extender, i.e., (methanediyldibenze-ne-4,1-diyl)dimethanediol, and five types of soft segments differing in structure and molar masses. The structure of the obtained polymers was determined (by using the Fourier transform infrared spectroscopy and X-ray diffraction methods), and the physicochemical (reduced viscosity, density), optical (UV-VIS), processing (MFR) and thermal (DSC and TGA-FTIR) as well as surface, antibacterial and cytotoxic properties were determined. Based on the results obtained, it can be stated that the type of soft segment used significantly affects the properties of the obtained polymers. The most favorable properties for use in medicine were demonstrated by materials based on a polycarbonate soft segment.

Synthesis and Characterization of New Polycarbonate-Based Poly(thiourethane-urethane)s.

The new segmented poly(thiourethane-urethane)s (PTURs) based on 1,1'-methanediylbis(4-isocyanatocyclohexane) (HMDI, Desmodur W®), polycarbonate diol (PCD, Desmophen C2200) and (methanediyldibenzene-4,1-diyl)dimethanethiol were synthesized by one-step melt polyaddition method. The obtained PTURs, with a content of 30-60 wt% of the hard segments (HS), were tested in which the influence of changes in the HS content on their properties was determined. The polymers were characterized by Fourier transform infrared spectroscopy (FTIR), gel permeation chromatography (GPC), thermal analysis (DSC, TGA) and thermomechanical analysis (DMTA). Additionally, tensile strength, optical (refractive index, UV-VIS and color) and surface properties of the obtained polymers (contact angle and surface free energy) and adhesion to copper were examined. FTIR analysis verified the supposed structure of the polymers obtained and showed a complete conversion of the isocyanate groups. TGA analysis confirmed the relatively good thermal stability of the polymers. On the other hand, after performing the DSC analysis, it was possible to state that the obtained materials were partially or completely amorphous, and the microphase separation decreased with increasing HS content in the polymer. Similar observations were made from the DMTA data. In addition, the hardness, tensile strength, modulus of elasticity, storage modulus, adhesion to copper, refractive index and total free surface energy increased with increasing HS content in the polymer.

New Segmented Poly(Thiourethane-Urethane)s Based on Poly(ε-Caprolactone)Diol Soft Segment: Synthesis and Characterization.

New segmented poly(thiourethane-urethane)s (SPTURs) were synthesized by the reaction of 1,1'-methanediylbis (4-isocyanatocyclohexane) (Desmodur W®, HMDI) and poly(ε-caprolactone)diol (PCL) and (methanediyldibenzene-4,1-diyl)dimethanethiol as nonconventional polymer chain extender. FTIR spectroscopy was used for the structural analysis of obtained polymers. The molecular weight distribution was examined by GPC chromatography. Based on the measured contact angles, free surface energy parameters were calculated. Thermal properties of polymers were examined by DSC and TGA, while viscoelastic properties were measured by DMTA. The tensile, adhesive and optical properties were also investigated for the obtained polymers. It was shown that SPTURs were transparent or partially transparent solids with high molar masses up to 84,300 Da. These polymers showed a good resistance to hydrolysis during incubation in Optylite® physiological saline over 8 weeks. Obtained polymers possessed a tensile strength of up to 43.26 MPa, hardness of up to 96.25/59.00 Sh A/D and adhesion to copper of 14.66 MPa. The surface properties of the obtained polymers show that all obtained SPTURs were hydrophilic (CAs for water between 64.07° and 73.12°) with calculated SFE up to 46.69 mN/m.

Special Issue: Processing, Structure, Dynamics and Mechanical Properties of Polymeric Materials.

The current Special Issue entitled "Processing, structure, dynamics and mechanical properties of polymeric materials" brings together scientists working at universities, research institutes, laboratories and various industries to discuss cutting-edge research on processing new polymeric materials using standard and innovative machines and to understand the structure and properties of these materials [...].

Modern Biodegradable Plastics-Processing and Properties Part II.

Four different plastics were tested: potato starch based plastic (TPS-P)-BIOPLAST GF 106/02; corn starch based plastic (TPS-C)-BioComp BF 01HP; polylactic acid (polylactide) plastic (PLA)-BioComp BF 7210 and low density polyethylene, trade name Malen E FABS 23-D022; as a petrochemical reference sample. Using the blown film extrusion method and various screw rotational speeds, films were obtained and tested, as a result of which the following were determined: breaking stress, strain at break, static and dynamic friction coefficient of film in longitudinal and transverse direction, puncture resistance and strain at break, color, brightness and gloss of film, surface roughness, barrier properties and microstructure. The biodegradable plastics tested are characterized by comparable or even better mechanical strength than petrochemical polyethylene for the range of film blowing processing parameters used here. The effect of the screw rotational speed on the mechanical characteristics of the films obtained was also demonstrated. With the increase in the screw rotational speed, the decrease of barrier properties was also observed. No correlation between roughness and permeability of gases and water vapor was shown. It was indicated that biodegradable plastics might be competitive for conventional petrochemical materials used in film blowing niche applications where cost, recyclability, optical and water vapor barrier properties are not critical.

Polyethylene-Matrix Composites with Halloysite Nanotubes with Enhanced Physical/Thermal Properties.

The aim of the present work is to investigate the effect of halloysite nanotubes (HNT) on the mechanical properties of low-density polyethylene composites modified by maleic anhydride-grafted PE (PE-graft-MA). Polyethylene nanocomposites were prepared using an injection molding machine, Arburg Allrounder 320 C 500-170; the HNT content was varied at 0 wt %, 2 wt %, 4 wt % and 6 wt %, and the PE-graft-MA content was varied at 5 wt %. The composites were examined for their ultimate tensile stress, strain at ultimate stress, hardness, impact strength, melt flow rate, heat deflection temperature, Vicat softening temperature, crystallinity degree and phase transition temperature. It was found that the addition of halloysite nanotubes to low-density polyethylene (LDPE) led to an increased heat deflection temperature (HDT, up to 47 °C) and ultimate tensile strength (up to 16.00 MPa) while the Vicat softening temperature, strain at ultimate stress, impact strength and hardness of examined specimens slightly decreased. Processing properties of the materials specified by the melt flow rate (MFR) deteriorated almost twice. The results have demonstrated that the nanoparticles can reinforce enhance LDPE at low filler content without any considerable loss of its ductility, but only when halloysite nanotubes are superbly distributed in the polyethylene matrix.