RESUMO
Nanosized maghemite (below 10 nm average diameter), surface-functionalized with meso-2,3-dimercaptosuccinic acid (DMSA), was investigated with respect to the content of DMSA molecules attached onto its surface and the onset of S-S bridges due to oxidation of neighboring S-H groups. To support our investigation, we introduced the use of photoacoustic spectroscopy to monitor thiol groups (S-H) conjugated with Raman spectroscopy to monitor the disulfide bridges (S-S). The normalized intensity (N(R)) of the Raman feature peaking at 500 cm(-1) was used to probe the S-S bridge whereas the normalized intensity (N(P)) of the photoacoustic band-S (0.42-0.65 µm) was used to probe the S-H moiety. The perfect linearity observed in the N(R) versus (1 - N(P)) plot strongly supports the oxidation process involving neighboring S-H groups as the DMSA surface grafting coefficient increases whereas the approach used in this report allows the evaluation of the [S-H]/[S-S] ratio. The observation of the reduction of the hydrodynamic diameter as the nominal DMSA-grafting increases supports the proposed model picture, in which the intraparticle (interparticle) S-S bridging takes place at higher (lower) DMSA-grafting values.