Mechanical Properties Optimization of Hybrid Aramid and Jute Fabrics-Reinforced Graphene Nanoplatelets in Functionalized HDPE Matrix Nanocomposites.

Natural lignocellulosic fibers (NLFs) have been used as a reinforcement for polymer matrix composites in the past couple of decades. Their biodegradability, renewability, and abundance make them appealing for sustainable materials. However, synthetic fibers surpass NLFs in mechanical and thermal properties. Combining these fibers as a hybrid reinforcement in polymeric materials shows promise for multifunctional materials and structures. Functionalizing these composites with graphene-based materials could lead to superior properties. This research optimized the tensile and impact resistance of a jute/aramid/HDPE hybrid nanocomposite by the addition of graphene nanoplatelets (GNP). The hybrid structure with 10 jute/10 aramid layers and 0.10 wt.% GNP exhibited a 2433% increase in mechanical toughness, a 591% increase in tensile strength, and a 462% reduction in ductility compared to neat jute/HDPE composites. A SEM analysis revealed the influence of GNP nano-functionalization on the failure mechanisms of these hybrid nanocomposites.

Evaluation of Hot Pressing Processing by Physical Properties of Ecofriendly Composites Reinforced by Eucalyptus Sawdust and Chamotte Residues.

The particleboard industry consumes large amounts of raw material, and this type of product consumption has been increasing over the last few years. The research for alternative raw materials becomes interesting, since most of the resources come from planted forests. In addition, the investigation of new raw materials must take into account environmentally correct solutions, such as the use of alternative natural fibers, use of agro-industrial residues, and resins of vegetable origin. The objective of this study was to evaluate the physical properties of panels manufactured by hot pressing using eucalyptus sawdust, chamotte, and polyurethane resin based on castor oil as raw materials. Eight formulations were designed with variations of 0, 5, 10, and 15% of chamotte, and two variations of resin with 10% and 15% of volumetric fraction. Tests of gravimetric density, X-ray densitometry, moisture content, water absorption, thickness swelling, and scanning electron microscopy were carried out. Through the results it can be noticed that the incorporation of chamotte in the manufacture of the panels increased the water absorption and the swelling in thickness, around 100% and the use of 15% of resin decreased, more than 50%, the values of these properties. X-ray densitometry analyzes showed that the addition of chamotte alters the density profile of the panel. In addition, the panels manufactured with 15% resin were classified as P7, the most demanding type on EN 312:2010 standard.

Properties of Luffa Cylindrica Mats Reinforced Castor Oil-Based Polyurethane Composite as an Alternative for Oriented Strand Board.

The main objective of this work was to produce and characterize a novel ecofriendly castor oil-based polyurethane (COPU) matrix composite reinforced by Luffa cylindrica mats, luffa for short, to be used as panels, as an alternative to oriented strand board (OSB). To do so, the mechanical behavior was evaluated by tree point flexural, perpendicular o surface tensile, screw pullout, and impact tests that were carried on the novel composite along with the neat matrix. Furthermore, the physical characteristics, the thermomechanical behavior, and the functional groups of the materials were observed by water absorption and thickness swelling tests along with dilatometry and Fourier transform infrared spectroscopy (FTIR). A comparison with commercialized OSB was also performed for control. The luffa/COPU composite was prepared by hand lay-up with 48 vol% of luffa mats incorporated as the maximum allowed by the mold under the available resources for manufacturing. The luffa fibers acted as a good reinforcement for the COPU matrix, where the flexural strength and modulus of elasticity were increased by more than 23 and 10 times, respectively, and the other mechanical properties more than doubled for the composites compared to the neat COPU resin. In general, the composite presented a lower performance compared to the commercial OSB, with the impact results being the exception. The water absorption and thickness swallowing results showed an already-expected behavior for the studied materials, where the better performance was found for the hydrophobic neat resin. The FTIR revealed that there was little interaction between luffa and COPU resin, which can be translated to a weak interface between these materials. However, the mechanical behavior, together with the other results presented by the luffa/COPU composite, confirm it is more than enough to be used as civil construction panels such as OSB.

Dynamic Mechanical Analysis and Ballistic Performance of Kenaf Fiber-Reinforced Epoxy Composites.

Several industry sectors have sought to develop materials that combine lightness, strength and cost-effectiveness. Natural lignocellulosic natural fibers have demonstrated to be efficient in replacing synthetic fibers, owing to several advantages such as costs 50% lower than that of synthetic fibers and promising mechanical specific properties. Polymeric matrix composites that use kenaf fibers as reinforcement have shown strength increases of over 600%. This work aims to evaluate the performance of epoxy matrix composites reinforced with kenaf fibers, by means of dynamic-mechanical analysis (DMA) and ballistic test. Through DMA, it was possible to obtain the curves of storage modulus (E'), loss modulus (E″) and damping factor, Tan δ, of the composites. The variation of E' displayed an increase from 1540 MPa for the plain epoxy to 6550 MPa for the 30 vol.% kenaf fiber composites, which evidences the increase in viscoelastic stiffness of the composite. The increase in kenaf fiber content induced greater internal friction, resulting in superior E″. The Tan δ was considerably reduced with increasing reinforcement fraction, indicating better interfacial adhesion between the fiber and the matrix. Ballistic tests against 0.22 caliber ammunition revealed similar performance in terms of both residual and limit velocities for plain epoxy and 30 vol.% kenaf fiber composites. These results confirm the use of kenaf fiber as a promising reinforcement of polymer composites for automotive parts and encourage its possible application as a ballistic armor component.

Physical and Mechanical Characterization of Titica Vine (Heteropsis flexuosa) Incorporated Epoxy Matrix Composites.

Titica vine (Heteropsis flexuosa) is a typical plant of the Amazon region commonly used for making baskets, bags, brooms and furniture, owing to its stiff fibers. In spite of its interesting properties, there is so far no reported information regarding the use of titica vine fibers (TVFs) in engineering composite materials. In this work, the TVF and its epoxy composites were for the first time physically, thermally and mechanically characterized. Additionally, the effect of two kinds of chemical treatments, one with sodium carbonate and one with calcium lignosulfonate, as well as different volume fractions, 10, 20, 30 and 40 vol%, of TVF-reinforced composites were assessed for corresponding basic properties. The thermogravimetric results of the composites reveal enhanced thermal stability for higher TVF content. In addition, the composite incorporated with 40 vol% of TVFs treated with sodium carbonate absorbed 19% more water than the composites with untreated fibers. By contrast, the calcium lignosulfonate treatment decreased water absorption by 8%. The Charpy and Izod impact tests showed that the composites, incorporated with the highest investigated volume fraction (40 vol%) of TVF, significantly increased the absorbed energy by 18% and 28%, respectively, compared to neat epoxy. ANOVA and Tukey statistical analyses displayed no direct influence of the chemical treatments on the energy absorption of the composites for either impact tests. SEM images revealed the main fracture mechanisms responsible for the performance of TVF composites.