Influence of Service Conditions and Mix Design on the Physical-Mechanical Properties of Roller-Compacted Concrete for Pavement.

This research focuses on the behavior of roller-compacted concrete (RCC) used in pavements, which are prone to deterioration affecting their performance. These deteriorations result from various causes, including traffic load, errors during construction, mix design, and ambient conditions. Among these, ambient conditions could lead to a marked variable impact on material behavior and durability depending on the conditions associated with each region. Accordingly, this study aims to deepen the understanding of the effect, which a broader range of ambient conditions and different mix designs have on the physical and mechanical properties of RCC. Measurements such as the amount of water vapor per kilogram of air were used to apply the findings comprehensively. The RCC analysis encompassed experimentation with different compositions, altering the cement water ratio amount, and adding a superplasticizer. The impact of curing on the materials was evaluated before subjecting them to various humidity and temperature conditions. Laboratory tests were conducted to measure performance, including moisture, shrinkage, compressive strength, and the progression of flexural fracture resistance over curing periods of up to 90 days. The results revealed a logarithmic correlation between shrinkage and ambient humidity, which is the most determining factor in performance. Mix optimization through increased cement and reduced water enhanced the tensile strength of the material. Furthermore, the curing process was confirmed to increase resistance to shrinkage, especially in the long term, establishing it as a crucial element for the structural stability of RCC, which is relatively insensitive to variations in ambient conditions.

Prediction of the Physical-Mechanical Properties of Roller-Compacted Concrete Pavements under Different Service and Mix Conditions Based on Cement and Water Content.

Roller-compacted concrete (RCC) for pavements has experienced problems with its physical-mechanical performance over extended periods due to ambient and in situ curing conditions. Accordingly, this study aimed to present multiple regression equations for calculating the physical-mechanical properties of RCC for pavements under different service and mix conditions. For this purpose, the research included two cement and two water contents, one reduced with admixture, and four combinations of temperature and relative humidity. For model calibration and definition of the equations, cubic and beam samples were fabricated to carry out physical-mechanical tests, such as moisture content, shrinkage, and modulus of rupture. Laboratory-obtained data were studied with the Response Surface Methodology (RSM) to determine the best regression equations. The main findings determined that the behavior of a mixture of RCC at a prolonged ambient exposure time is possible because the surface models and the RSM were consistent with the different service and mix conditions. The models showed an accuracy of 98.99% in detecting shrinkage changes from 12 to 16% cement with 5.65% water in dry to wet ambient conditions. Similarly, moisture content and modulus of rupture had a 98.27 to 98.88% fit. Finally, the drying shrinkage, with mixes of 12% cement and water content variations with water-reducing admixture and superplasticizer effects, had an adjustment of 94.87%.

The Use of Deconstructed Tires as Elastic Elements in Railway Tracks.

Elastic elements such as rail pads, under sleeper pads and under ballast mats are railway components that allow for a reduction in track deterioration and vibrations. And they are furthermore commonly used to obtain an optimal vertical stiffness of the infrastructure. However, the use of elastomeric materials can increase construction costs and the consumption of raw materials. Thus, the utilization of used tire layers offers an alternative to reuse an abundant waste reducing the cost of elastic elements. In addition, an innovator technique allows deconstructing tire layers without grinding up the material, reducing production costs at the same time that tire properties are remained. This research is focused on the study of the viability of developing elastic components from used tire layers by evaluating the influence of thickness, the resistance capacity of the elements and their behavior in a ballast box. Results indicate the ability of tire pads to manufacture elastic elements (rail pads, under sleeper pads and under ballast mats) to be used in railway tracks.