Polyethylene pipes exposed to chlorine dioxide in drinking water supply system: A critical review of degradation mechanisms and accelerated aging methods.

Polyethylene (PE) pipes have been widely used in drinking water distribution systems across the world. In many cases, chlorine dioxide (ClO2) is used to maintain a residual disinfectant concentration in potable water. Practical experiences have shown that the lifetime of PE pipes is significantly reduced due to exposure to drinking water with ClO2. Recently, many companies have proposed new PE pipes with a modified formulation, which are more resistant to chlorine dioxide. However, a standardized test method for evaluating the long-term performances of PE pipes is still missing. This literature review was performed to provide a description of chlorine dioxide uses and degradation mechanisms of polyethylene pipes in real water distribution systems. Current accelerated aging methods to evaluate long-term performances of PE pipes exposed to ClO2 are described and discussed along with the common technics used to characterize the specimens. Accelerate aging methods can be distinguished in immersion aging tests and pressurized pipe loop tests. Wide ranges of operational conditions (chlorine dioxide concentration, water pressure, water temperature, etc.) are applied, resulting in a great variety of results. It was concluded that pressurized looping tests applying semi-realistic operational conditions could better replicate the aging mechanisms occurring in service. Despite this, the acceleration and the evaluation of the long-term performance are still difficult to determine precisely. Further experimentation is needed to correlate chemical-mechanical characterization parameters of PE pipes with their lifetime in service.

Monitoring for Coastal Resilience: Preliminary Data from Five Italian Sandy Beaches.

Video-monitoring can be exploited as a valuable tool to acquire continuous, high-quality information on the evolution of beach morphology at a low cost and, on such basis, perform beach resilience analyses. This manuscript presents preliminary results of an ongoing, long-term monitoring programme of five sandy Italian beaches along the Adriatic and Tyrrhenian sea. The project aims at analyzing nearshore morphologic variabilities on a time period of several years, to link them to resilience indicators. The observations indicate that most of the beach width variations can be linked to discrete variations of sandbar systems, and most of all to an offshore migration and decay of the outermost bars. Further, the largest net shoreline displacements across the observation period are experienced by beaches with a clear NOM (Net Offshore Migration)-type evolution of the seabed.

Summertime conditions of a muddy estuarine environment: the EsCoSed project contribution.

As part of the Estuarine Cohesive Sediments (EsCoSed) project, a field experiment was performed in a highly engineered environment, acting as a natural laboratory, to study the physico-chemical properties of estuarine sediments and the associated hydro-morphodynamics during different seasons. The present contribution focuses on the results obtained from the summertime monitoring of the most downstream part of the Misa River (Senigallia, Italy). The measured hydrodynamics suggested a strong interaction between river current, wave forcing and tidal motion; flow velocities, affected by wind waves traveling upstream, changed significantly along the water column in both direction and magnitude. Surficial salinities in the estuary were low in the upper reaches of the estuary and exceeded 10 psu before the river mouth. Montmorillonite dominated the clay mineral assemblage, suggesting that large, low density flocs with high settling velocities (>1 mm s(-1)) may dominate the suspended aggregate materials.