Cartilage-inspired surface textures for improved tribological performance of orthopedic implants.

Joint replacements have become one of the most common orthopedic procedures due to the significant demands of retaining functional mobility. While these procedures are of great value to patients, there are some limitations. Durability is the most important limitation associated with joint replacement that needs to be addressed due to the increasing number of younger patients. Titanium is a commonly used implant material which has high biocompatibility, high strength-to-density ratio, and high corrosion resistance. However, current titanium implants have poor wear resistance which shortens their lifespan. In this study, microscale dimples with four different dimple shapes (circular, triangular, square, and star) of similar sizes to the pores found in natural articular cartilage were fabricated on titanium disks to improve implant lubrication and reduce wear. Biotribology tests were performed on dimpled and non-dimpled titanium disks in a condition similar to that inside of a patient's body. It was shown that dimpling the titanium disks optimized the lubricant film formation and decreased the wear rate significantly while also reducing the coefficient of friction (COF). The star-shaped dimples had the lowest COF and almost no detectable wear after 8 h of testing. To investigate whether dimpling increased bacterial colonization due to increased surface area, and to determine whether any increase could be limited by coating with antibacterial materials, bacterial colonization with Staphylococcus aureus was tested with non-dimpled and star-shaped dimpled titanium disks with and without coating with polydopamine (PDA), silver (Ag) nanoparticles (NPs), and PDA + Ag NPs. It was found that dimpling did not increase bacterial colonization, and that coating with PDA, Ag NPs, or PDA + Ag NPs did not decrease bacterial colonization. Nevertheless, we conclude that star-shaped dimpled titanium surfaces have potential utility as more durable orthopedic implants.

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens.

This study presents a methodology for the rapid fabrication and micro-tensile testing of additively manufactured (AM) 17-4PH stainless steels by combining photolithography, wet-etching, focused ion beam (FIB) milling, and modified nanoindentation. Detailed procedures for proper sample surface preparation, photo-resist placement, etchant preparation, and FIB sequencing are described herein to allow for high throughput (rapid) specimen fabrication from bulk AM 17-4PH stainless steel volumes. Additionally, procedures for the nano-indenter tip modification to allow tensile testing are presented and a representative micro specimen is fabricated and tested to failure in tension. Tensile-grip-to-specimen alignment and sample engagement were the main challenges of the micro-tensile testing; however, by reducing the indenter tip dimensions, alignment and engagement between the tensile grip and specimen were improved. Results from the representative micro-scale in situ SEM tensile test indicate a single slip plane specimen fracture (typical of a ductile single crystal failure), differing from macro-scale AM 17-4PH post-yield tensile behavior.