RESUMO
In this study, we combine in situ fast differential scanning calorimetry (FDSC) with synchrotron X-ray measurements to study simultaneously the structure and thermophysical properties of materials. Using the example of the organic compound BCH-52, we show that the X-ray beam can heat the sample and induce a shift of the heat-flow signal. The aim of this paper is to investigate the influence of radiation on sample behavior. The calorimetric data is used to quantify the absorbed beam energy and, together with the diffraction data, reveal an irreversible damage of the sample. The results are especially important for materials with high absorption coefficients and for high-energy X-ray and electron beams. Our findings illustrate that FDSC combined with X-ray diffraction is a suitable characterization method when beam damage must be minimized.
RESUMO
Ni-free Ti-based bulk metallic glasses (BMGs) are exciting materials for biomedical applications because of their outstanding biocompatibility and advantageous mechanical properties. The glassy nature of BMGs allows them to be shaped and patterned via thermoplastic forming (TPF). This work demonstrates the versatility of the TPF technique to create micro- and nano-patterns and hierarchical structures on Ti40Zr10Cu34Pd14Sn2 BMG. Particularly, a hierarchical structure fabricated by a two-step TPF process integrates 400 nm hexagonal close-packed protrusions on 2.5 µm square protuberances while preserving the advantageous mechanical properties from the as-cast material state. The correlations between thermal history, structure, and mechanical properties are explored. Regarding biocompatibility, Ti40Zr10Cu34Pd14Sn2 BMGs with four surface topographies (flat, micro-patterned, nano-patterned, and hierarchical-structured surfaces) are investigated using Saos-2 cell lines. Alamar Blue assay and live/dead analysis show that all tested surfaces have good cell proliferation and viability. Patterned surfaces are observed to promote the formation of longer filopodia on the edge of the cytoskeleton, leading to star-shaped and dendritic cell morphologies compared with the flat surface. In addition to potential implant applications, TPF-patterned Ti-BMGs enable a high level of order and design flexibility on the surface topography, expanding the available toolbox for studying cell behavior on rigid and ordered surfaces.
RESUMO
The effects of severe plastic deformation (SPD) by means of high-pressure torsion (HPT) on the structural properties of the two iron-based metallic glasses Fe73.9Cu1Nb3Si15.5B6.6 and Fe81.2Co4Si0.5B9.5P4Cu0.8 have been investigated and compared. While for Fe73.9Cu1Nb3Si15.5B6.6, HPT processing allows us to extend the known consolidation and deformation ranges, HPT processing of Fe81.2Co4Si0.5B9.5P4Cu0.8 for the first time ever achieves consolidation and deformation with a minimum number of cracks. Using numerous analyses such as X-ray diffraction, dynamic mechanical analyses, and differential scanning calorimetry, as well as optical and transmission electron microscopy, clearly reveals that Fe81.2Co4Si0.5B9.5P4Cu0.8 exhibits HPT-induced crystallization phenomena, while Fe73.9Cu1Nb3Si15.5B6.6 does not crystallize even at the highest HPT-deformation degrees applied. The reasons for these findings are discussed in terms of differences in the deformation energies expended, and the number and composition of the individual crystalline phases formed. The results appear promising for obtaining improved magnetic properties of glassy alloys without additional thermal treatment.
RESUMO
This paper envisions Ti40Zr10Cu36Pd14 bulk metallic glass as an oral implant material and evaluates its antibacterial performance in the inhabitation of oral biofilm formation in comparison with the gold standard Ti-6Al-4V implant material. Metallic glasses are superior in terms of biocorrosion and have a reduced stress shielding effect compared with their crystalline counterparts. Dynamic mechanical and thermal expansion analyses on Ti40Zr10Cu36Pd14 show that these materials can be thermomechanically shaped into implants. Static water contact angle measurement on samples' surface shows an increased surface wettability on the Ti-6Al-4V surface after 48 âh incubation in the water while the contact angle remains constant for Ti40Zr10Cu36Pd14. Further, high-resolution transmission and scanning transmission electron microscopy analysis have revealed that Ti40Zr10Cu36Pd14 interior is fully amorphous, while a 15 ânm surface oxide is formed on its surface and assigned as copper oxide. Unlike titanium oxide formed on Ti-6Al-4V, copper oxide is hydrophobic, and its formation reduces surface wettability. Further surface analysis by X-ray photoelectron spectroscopy confirmed the presence of copper oxide on the surface. Metallic glasses cytocompatibility was first demonstrated towards human gingival fibroblasts, and then the antibacterial properties were verified towards the oral pathogen Aggregatibacter actinomycetemcomitans responsible for oral biofilm formation. After 24 âh of direct infection, metallic glasses reported a >70% reduction of bacteria viability and the number of viable colonies was reduced by â¼8 times, as shown by the colony-forming unit count. Field emission scanning electron microscopy and fluorescent images confirmed the lower surface colonization of metallic glasses in comparison with controls. Finally, oral biofilm obtained from healthy volunteers was cultivated onto specimens' surface, and proteomics was applied to study the surface property impact on species composition within the oral plaque.
RESUMO
Polyetheretherketone (PEEK) is a high-performance semi-crystalline thermoplastic polymer with outstanding mechanical properties, high thermal stability, resistance to most common solvents, and good biocompatibility. A high temperature thermally induced phase separation technique was used to produce PEEK foams with controlled foam density from PEEK in 4-phenylphenol (4PPH) solutions. Physical and mechanical properties, foam and bulk density, surface area, and pore morphology of foamed PEEK were characterized and the role of PEEK concentration and cooling rate was investigated. Porous PEEK with densities ranging from 110 to 360 kg/m3 with elastic moduli and crush strength ranging from 13 to 125 MPa and 0.8 to 7 MPa, respectively, was produced.
RESUMO
The atomistic mechanisms occurring during the processes of aging and rejuvenation in glassy materials involve very small structural rearrangements that are extremely difficult to capture experimentally. Here we use in-situ X-ray diffraction to investigate the structural rearrangements during annealing from 77 K up to the crystallization temperature in Cu44Zr44Al8Hf2Co2 bulk metallic glass rejuvenated by high pressure torsion performed at cryogenic temperatures and at room temperature. Using a measure of the configurational entropy calculated from the X-ray pair correlation function, the structural footprint of the deformation-induced rejuvenation in bulk metallic glass is revealed. With synchrotron radiation, temperature and time resolutions comparable to calorimetric experiments are possible. This opens hitherto unavailable experimental possibilities allowing to unambiguously correlate changes in atomic configuration and structure to calorimetrically observed signals and can attribute those to changes of the dynamic and vibrational relaxations (α-, ß- and γ-transition) in glassy materials. The results suggest that the structural footprint of the ß-transition is related to entropic relaxation with characteristics of a first-order transition. Dynamic mechanical analysis data shows that in the range of the ß-transition, non-reversible structural rearrangements are preferentially activated. The low-temperature γ-transition is mostly triggering reversible deformations and shows a change of slope in the entropic footprint suggesting second-order characteristics.
RESUMO
The structure of matter at the nanoscale, in particular that of amorphous metallic alloys, is of vital importance for functionalization. With the availability of synchrotron radiation, it is now possible to visualize the internal features of metallic samples without physically destroying them. Methods based on computed tomography have recently been employed to explore the local features. Tomographic reconstruction, while it is relatively uncomplicated for crystalline materials, may generate undesired artifacts when applied to featureless amorphous or nanostructured metallic alloys. In this study we show that X-ray diffraction computed nanotomography can provide accurate details of the internal structure of a metallic glass. We demonstrate the power of the method by applying it to a hierarchically phase-separated amorphous sample with a small volume fraction of crystalline inclusions, focusing the X-ray beam to 500 nm and ensuring a sub-micrometer 2D resolution via the number of scans.
RESUMO
Flash Joule-heating was applied to the Cu47.5Zr47.5Al5 metallic glass for designing fully crystalline metastable nanocomposites consisting of the metastable B2 CuZr and low-temperature equilibrium Cu10Zr7 phases. The onset of crystallization was in situ controlled by monitoring resistivity changes in the samples. The effect of heating rate and annealing time on the volume fraction of the crystalline phases and mechanical properties of the nanocomposites was studied in detail. Particularly, an increase of the heating rate and a decrease of the annealing time lead to a lower number of equilibrium Cu10Zr7 precipitates and an increase of tensile ductility. Tailoring of these non-equilibrium microstructures and mechanical properties may not be possible unless one starts with a fully glassy material that opens new perspectives for designing metastable nanomaterials with unique physical properties.
RESUMO
The aim of this study is to investigate the effects of cryogenic and room temperature pre-deformation on subsequent artificial ageing of Al-Mg-Si alloys. Naturally aged and pre-aged samples were strained to 5%, 10% and 20% at RT (25 °C) and under liquid nitrogen, and artificially aged at 185 °C. Pre-deformation generally increases ageing kinetics for both the naturally aged and pre-aged alloys, which increase in proportion to the degree of pre-deformation, and which are slightly more pronounced for the cryogenic condition. The peak strength is constant, except for when a low degree of pre-deformation is used, in which case it is slightly reduced. Cryogenically deformed samples show an increased strength and hardness, compared to samples pre-deformed at RT, when subjected to an equal magnitude of strain. This difference is reduced during artificial ageing. Synchrotron measurements reveal that this behaviour can be linked to the greater dislocation density, which is not completely recovered even after prolonged ageing at 185 °C.
RESUMO
We directly determine the thermodynamic fragility index of two metallic glasses (Mg65Cu25Gd10 and Au49Cu26.9Si16.3Ag5.5Pd2.3) from fictive temperature shifts induced by a variation of the quenching rate using fast differential scanning calorimetry (FDSC). Recent chip calorimeters are able to achieve the cooling rates necessary to perform such an evaluation. For the Mg65Cu25Gd10 and Au49Cu26.9Si16.3Ag5.5Pd2.3 metallic glasses studied, we find very good agreement of the kinetic fragility index with literature data obtained by conventional calorimetry and rheology. The thermodynamic fragility indices are m=25.5 ± 1.5 for Mg65Cu25Gd10 and m=50.3 ± 2.3 for Au49Cu26.9Si16.3Ag5.5Pd2.3, respectively. The FDSC method discussed here allows for fast and reliable determination of the kinetic fragility of metallic glasses, and is thus competitive with high-frequency methods.