Characterization and In Vitro Behavior of PEO Coated Mg Modified with Antibacterial Ag(I) and Cu(II) Complexes.

The use of Mg-based biomaterials with a number of their advantageous properties are overshadowed by uncontrollable metal corrosion. Moreover, the use of implants goes alongside with the threat of pathogens-associated complications. In this study, PEO coated Mg biomaterial loaded with antibacterial Ag(I) and Cu(II) complexes is produced and tested to meet both appropriate protective characteristics as well as sufficient level of antibacterial activity. To achieve a suitable level of anticorrosion protection phosphate and fluoride-phosphate electrolytes are used in the PEO process. Investigation of the surface thickness and morphology done by means of cross-section analysis and scanning electron microscopy (SEM), as well as electrochemical impedance spectroscopy (EIS) assay show precedence of the fluoride containing PEO coating and make it the material of choice for further modification with Ag(I) and Cu(II) complexes. The presence of the complexes on the PEO surface is confirmed by energy dispersive X-ray spectroscopy (EDX). X-ray photoelectron spectroscopy (XPS), transmission electron microscopy (TEM) and glow discharge optical emission spectroscopy (GDOES) are used to estimate the complexes' chemical state and depth of penetration in the coating surface. Based on the results of antibacterial assay, the modified coatings are found to be active against both Gram-positive and Gram-negative bacteria.

Compromising Between Phase Stability and Electrical Performance: SrVO3 -SrTiO3 Solid Solutions as Solid Oxide Fuel Cell Anode Components.

The applicability of perovskite-type SrVO3-δ in high-temperature electrochemical energy conversion technology is hampered by the limited stability domain of the perovskite phase. The aim of the present work was to find a compromise between the phase stability and electrical performance by designing solid solutions in the SrVO3 -SrTiO3 system. Increasing titanium content in SrV1-y Tiy O3-δ (y=0-0.9) perovskites is demonstrated to result in a gradual shift of the upper-p(O2 ) phase stability boundary toward oxidizing conditions: from ≈10-15  bar at 900 °C for undoped SrVO3-δ to ≈10-11 -10-5  bar for y=0.3-0.5. Although the improvement in the phase stability is accompanied by a decrease in electrical conductivity, the conductivities of SrV0.7 Ti0.3 O3-δ and SrV0.5 Ti0.5 O3-δ at 900 °C remain as high as 80 and 20 S cm-1 , respectively, and is essentially independent of p(O2 ) within the phase-stability domain. Combined XRD, thermogravimetric analysis, and electrical studies revealed very sluggish kinetics of oxidation of SrV0.5 Ti0.5 O3-δ ceramics under inert gas conditions and a nearly reversible behavior after exposure to an inert atmosphere at elevated temperatures. Substitution by titanium in the SrV1-y Tiy O3-δ system results also in a decrease of oxygen deficiency in perovskite lattice and a favorable suppression of thermochemical expansion. Variations of oxygen nonstoichiometry and electrical properties in the SrV1-y Tiy O3-δ series are discussed in combination with the simulated defect chemistry of solid solutions.

The Influence of PSA Pre-Anodization of AA2024 on PEO Coating Formation: Composition, Microstructure, Corrosion, and Wear Behaviors.

In the frame of the current work, it was shown that plasma electrolytic oxidation (PEO) treatment can be applied on top of phosphoric sulfuric acid (PSA) anodized aluminum alloy AA2024. Being hard and well-adherent to the substrate, PEO layers improve both corrosion and wear resistance of the material. To facilitate PEO formation and achieve a dense layer, the systematic analysis of PEO layer formation on the preliminary PSA anodized layer was performed in this work. The microstructure, morphology, and composition of formed PEO coatings were investigated using scanning electron microscopy (SEM), x-ray diffraction (XRD), and glow-discharge optical emission spectroscopy (GDOES). It was shown that under constant current treatment conditions, the PSA layer survived under the applied voltage of 350 V, whilst 400 V was an intermediate stage; and under 450 V, the PSA layer was fully converted after 5 min of the treatment. The comparison test with PEO formation on the bare material was performed. It was confirmed that during the "sparking" mode (400 V) of PEO formation, the PEO coatings, formed on PSA treated AA2024, were more wear resistant than the same PEO coatings on bare AA2024.

Gold nanorods induce early embryonic developmental delay and lethality in zebrafish (Danio rerio).

Due to their unique electronic and optical features, gold nanoparticles (AuNP) have received a great deal of attention for application in different fields such as catalysis, electronics, and biomedicine. The large-volume manufacturing predicted for future decades and the inevitable release of these substances into the environment necessitated an assessment of potential adverse human and ecological risks due to exposure to AuNP. Accordingly, this study aimed to examine the acute and developmental toxicity attributed to a commercial suspension of Au nanorods stabilized with cetyltrimethylammonium bromide (CTAB-AuNR) using early embryonic stages of zebrafish (Danio rerio), a well-established model in ecotoxicology. Zebrafish embryos were exposed to CTAB-AuNR (0-150 µg/L) to determine for developmental assessment until 96 hr post fertilization (hpf) and lethality. Uptake of CTAB-AuNR by embryos and nanoparticles potential to induce DNA damage was also measured at 48 and 96 hpf. Analysis of the concentration-response curves with cumulative mortality at 96 hpf revealed a median lethal concentration (LC50,96h) of 110.2 µg/L. At sublethal concentrations, CTAB-AuNR suspensions were found to produce developmental abnormalities such as tail deformities, pericardial edema, decreased body length, and delayed eye, head, and tail elongation development. Further, less than 1% of the initial concentration of CTAB-AuNR present in the exposure media was internalized by zebrafish embryos prior to (48 hpf) and after hatching (96 hpf). In addition, no marked DNA damage was detected in embryos after exposure to CTAB-AuNR. Overall, CTAB-AuNR suspensions produced lethal and sublethal effects on zebrafish embryos with possible repercussions in fitness of adult stages. However, these results foresee a low risk for fish since the observed effects occurred at concentrations above the levels expected to find in the aquatic environment.

Photocatalytic Deposition of Hydroxyapatite onto a Titanium Dioxide Nanotubular Layer with Fine Tuning of Layer Nanoarchitecture.

A new effective method of photocatalytic deposition of hydroxyapatite (HA) onto semiconductor substrates is proposed. A highly ordered nanotubular TiO2 (TNT) layer formed on titanium via its anodization is chosen as the photoactive substrate. The method is based on photodecomposition of the phosphate anion precursor, triethylphosphate (TEP), on the semiconductor surface with the following reaction of formed phosphate anions with calcium cations presented in the solution. HA can be deposited only on irradiated areas, providing the possibility of photoresist-free HA patterning. It is shown that HA deposition can be controlled via pH, light intensity, and duration of the process. Energy-dispersive X-ray spectroscopy profile analysis and glow discharge optical emission spectroscopy of HA-modified TNT prove that HA deposits over the entire TNT depth. High biocompatibility of the surfaces is proven by protein adsorption and pre-osteoblast cell growth.