RESUMO
Pure and Fe-doped TiO2 nanoparticles were synthesized by the sol-gel method. The samples were characterized by X-ray diffraction, Raman spectroscopy, BET, UV-vis diffuse reflectance spectroscopy, and scanning electron microscopy. The results show a dependence between the crystallite size and the amount of dopant, which decreases from 13.02 to 12.81 nm. The same behavior was observed in the optical properties, where the band gap decreased from 3.2 to 2.86 eV. The arsenic (V) adsorption was tested in aqueous solution containing 5 mg/L of arsenic and 0.5 g/L of adsorbent at pH 7 and in dark conditions. The results indicate that the TiO2-B sample shows a higher arsenic removal, reaching 88% arsenic removal from the water at pH 7. Thus, it is also shown that the best performance occurs at pH 5, where it reaches an arsenic removal of 94%. Ion competition studies show that arsenic removal capacity is slightly affected by chloride, carbonate, nitrate, and sulfate ions. According to the results, the synthesized samples are a promising material for treating arsenic-contaminated water.
RESUMO
Multi-walled carbon nanotubes (MWCNTs) are an alternative for storage with low cost, eco-friendly, and good performance for both process adsorption and desorption. Herein, a purification procedure of MWCNTs was successfully described and studied by using XRD, TEM, Raman spectroscopy and by means of N2 adsorption-desorption isotherms using the BET method. The H2 storage properties at room temperature of the purified carbon nanotubes exposed to gas under pressures between 0.39 and 13.33 kPa was investigated by using the quartz crystal microbalance technique. It was found that the H2 adsorption capacity is strongly dependent on the morphological and structural characteristics of the carbon nanotubes and their specific surface area. The best sample with specific surface area of 729.4 ± 3 m2 g-1 shows a maximum adsorption capacity of 3.46 wt% at 12.79 kPa of H2 exposure pressure. The adsorption kinetics (t95%) from the different purified MWCNTs was also investigated as a function of the H2 exposure pressure as well as the performance of these MWCNTs on the reversibility of the H2 loading/unloading process when underwent to successive cycles of gas exposure.
RESUMO
Arsenic (As) contamination of water is a serious problem in developing countries. In water streams, arsenic can be as As(V) and As(III), the latter being the most toxic species. In this work, an innovative adsorbent based on CaTiO3 nanoparticles (CTO) was prepared by the sol-gel technique for the removal of As(III) from aqueous solution. X-ray diffraction of the CTO nanoparticles powders confirmed the CTO phase. Transmission electron microscopy observations indicated an average particle size of 27 nm, while energy dispersive X-ray spectroscopy analysis showed the presence of Ca, Ti, and O in the expected stoichiometric amounts. The surface specific area measured by Brunauer, Emmett, and Teller (BET) isotherm was 43.9 m2/g, whereas the isoelectric point determined by Zeta Potential measurements was at pH 3.5. Batch adsorption experiments were used to study the effect of pH on the equilibrium adsorption of As(III), using an arsenite solution with 15 mg/L as initial concentration. The highest removal was achieved at pH 3, reaching an efficiency of up to 73%, determined by X-ray fluorescence from the residual As(III) in the solution. Time dependent adsorption experiments at different pHs exhibited a pseudo-second order kinetics with an equilibrium adsorption capacity of 11.12 mg/g at pH 3. Moreover, CTO nanoparticles were regenerated and evaluated for four cycles, decreasing their arsenic removal efficiency by 10% without affecting their chemical structure. X-ray photoelectron spectroscopy analysis of the CTO surface after removal experiments, showed that arsenic was present as As(III) and partially oxidized to As(V).