Evaluation of the antibacterial effect of titanium dioxide nanoparticles combined with acrylic laminates for functional orthodontic appliances: a randomized controlled clinical trial.

BACKGROUND: The objective of this study was to evaluate the antibacterial effect of titanium dioxide nanoparticles incorporated into the acrylic baseplates of the maxillary part of twin block appliances in orthodontic patients during the treatment period. MATERIALS AND METHODS: Twenty-six patients were selected randomly and divided into two groups(n = 13). Test group patients used orthodontic functional appliances containing 1% titanium dioxide nanoparticles in acrylic baseplates. Control group patients used orthodontic functional appliances without titanium dioxide nanoparticles in acrylic baseplates. Swap samples were taken from the palatal gingiva facing the fitting surface of the acrylic component of the maxillary part of a twin block appliance for each patient at five-time intervals (baseline sample, after one, two, four, and six months) and then cultured in blood agar plates to calculate bacterial colony count. The Mann‒Whitney U test and the Friedman test were used to compare data. Bonferroni correction (p value ≤ 0.05) was applied to detect significant differences. THE RESULTS: showed a decrease in the bacterial colony count in the test group compared to the control group. Pairwise comparisons revealed a statistically significant difference in samples after four- and six-month groups (p values = 0.002 and 0.011, respectively) vs. the one-month test group. A higher statistically significant difference was observed in the six-month group (p-value = 0.037) vs. the baseline group in the control group. CONCLUSION: The addition of 1% titanium dioxide nanoparticles to acrylic baseplates of orthodontic functional appliances significantly reduced the bacterial colony count under the base plate after at least four months of application.

Can antioxidant treatment replace delay in bracket bonding? An in vitro study.

BACKGROUND: Deterioration in shear bond strength has been reported after immediate bracket bonding following hydrogen peroxide bleaching. This study compared the effectiveness of three antioxidant agents, namely, alpha-tocopherol, green tea extract, and sodium ascorbate, in reversing the bleaching effect and as possible alternatives to delayed bonding. METHODS: A total of 105 extracted human premolars were arbitrarily assigned to 7 groups (n = 15 each), including group 1 as the unbleached control group and six experimental groups, which were bleached with 40% hydrogen peroxide in three sessions of 15 min each. In experimental group 2, bonding was performed immediately after bleaching, whereas in groups 3 and 4, bonding was delayed for 1 and 2 weeks, respectively; meanwhile, the specimens were immersed in artificial saliva at 37 °C. Groups 5, 6, and 7 were treated immediately after bleaching with 10% of alpha-tocopherol, green tea extract, and sodium ascorbate solutions, respectively, for 15 min. Specimens were processed using 500 thermal cycles between 5 and 55 °C, with a dwell time of 30 s after 24 h of bracket bonding, and then tested for shear bond strength. The adhesive remnant index was examined to evaluate fracture mode. One-way analysis of variance, Kruskal-Wallis H, and post hoc Tukey's honestly significant difference tests were used to compare the data. Significant results were subjected to pairwise comparisons with Bonferroni's correction-adjusted of p values ≤ 0.050. RESULTS: Shear bond strength was significantly lower (p < 0.001) in the immediate bonding and 1-week delay groups than in the control group. However, no significant difference was detected among the 2-week delay, antioxidant-treated, and control groups (p > 0.05). CONCLUSIONS: Application of 10% alpha-tocopherol, green tea extract, or sodium ascorbate for 15 min could restore shear bond strength after 40% hydrogen peroxide bleaching as an alternative to delay in bracket bonding.