Surface-functionalized and surface-functionalizable poly(vinylidene fluoride) graft copolymer membranes via click chemistry and atom transfer radical polymerization.

Poly(vinylidene fluoride) (PVDF) with azide-functionalized poly(glycidyl methacrylate) (PGMA) side chains (PVDF-g-P[GMA-(N3)(OH)]) were synthesized via free radical-initiated graft copolymerization of glycidyl methacrylate (GMA) from ozone-pretreated PVDF backbone (PVDF-g-PGMA), followed by reaction of the oxirane rings in the GMA side chains with sodium azide. Alkyne-functionalized poly(N-isopropylacrylamide) (alkynyl-PNIPAM), prepared a priori by atom transfer radical polymerization (ATRP), was used for the click reaction with the azido-containing PGMA side chains of the PVDF-g-P[GMA-(N3)(OH)] copolymer to give rise to the thermoresponsive PVDF-g-P[GMA-click-PNIPAM] copolymer. Both the PVDF-g-P[GMA-(N3)(OH)] and PVDF-g-P[GMA-click-PNIPAM] copolymers can be readily cast into microporous membranes by phase inversion in an aqueous medium. The PVDF-g-P[GMA-(N3)(OH)] microporous membranes with azido-containing surfaces could be further functionalized via surface click reaction with alkyne-terminated PNIPAM of controlled chain lengths to obtain the PVDF-g-P[GMA-click-PNIPAM]surface microporous membranes. The surface composition and morphology of the PVDF-g-P[GMA-click-PNIPAM] membranes can be adjusted by the temperature of casting medium, while the flux through both types of membranes exhibits thermoresponsive behavior.

Influence of fouling on the efficiency of sacrificial anodes in providing cathodic protection in Southeast Asian tropical seawater.

Aluminum and zinc based sacrificial anodes are routinely used to provide corrosion protection to metals (typically steel) exposed to seawater, for example in steel pipelines and storage tanks. However, the high fouling rates experienced in South East Asia means that both the anodes and the metals to be protected rapidly become coated with macrofoulers, which could potentially prevent the anodes from being effective. The present study, involving exposure tests of up to 18 months, indicates that both aluminum and zinc sacrificial anodes remain effective even after being completely coated with biofouling. Furthermore, it was easier to remove the biofouling on the cathodically protected samples than on their unprotected counterparts, possibly due to the higher local pH produced by cathodic protection at the metal and seawater interface.