RESUMO
PURPOSE: To determine the number of torque/reverse torque cycles attachment screws can withstand before fracture, and to record the magnitude of reverse torque values for each of the 10 cycles of screw tightening and loosening. MATERIALS AND METHODS: The testing assemblies consisted of 30 temporary cylinder/multiunit abutment/internal connection implants (10 each from Dentsply Sirona Astra, Biohorizons, and Zimmer Biomet Dental). The assemblies were inserted into resin blocks, and temporary cylinders were connected to the multiunit abutments with new attachment screws and torqued to the recommended preload (15 Ncm Dentsply Sirona Astra; 15 Ncm Biohorizons; 10 Ncm Zimmer Biomet Dental) using a digital torque gauge instrument (Model 3, MARK-10 Corporation, New York, USA) at room temperature without lubrication. After 24 h, the attachment screws were reverse torqued with the same instrument and the values were recorded. The torque/reverse torque cycles were repeated every 24 h for 10 days. Data were analyzed using mixed model analysis. A second test included torquing the used screws (30) until fracture or stripping occurred. The reverse torque values were recorded and compared with new screws that were torqued until fracture or stripping. A sample of used and new attachment screws from each assembly were viewed under both laser microscope (LEXT OLS4000, 3D Measuring Laser Microscope, Olympus) and scanning electron microscope (JEOL-JSM6510, Tokyo, Japan). Data were analyzed using t-test. RESULTS: Following 10 cycles of torquing and reverse torquing, the reverse torque values measured on day 10 were lesser compared with the reverse torque value measured on day 1 for 29/30 attachment screws (96.6%). According to the t-test used for the second test, the p-values among all three groups were ≥0.9 which were not statistically significant. CONCLUSION: The results of this study indicated that after 10 cycles of torquing and reverse torquing attachment screws, the reverse torque values decreased. There were no statistical differences between the magnitude of torque necessary to fracture new and used attachment screws.
RESUMO
PURPOSE: Many elastomeric impressions sent to commercial laboratory dental technicians may include marginal defects. To fabricate accurate restorations, digital technology may be used to merge digital files of defective impressions into a single standard tessellation language (STL) file free of errors. This would save clinicians and patients time and may improve clinical care. The purpose of this study was to compare the accuracy of digital master casts reconstructed from merged STL files of defective impressions with the file of the original defect-free preparations. MATERIAL AND METHODS: Ivorine teeth on a dentoform were prepared to receive a posterior fixed dental prosthesis (FDP) with complete coverage preparations. An impression was made in a stock tray using polyvinyl siloxane (PVS) impression material and an extraoral scanner (E3, 3Shape, Denmark) was used to digitize the impression; this was the reference cast. Wax was used to create defects on the buccal and lingual margins of the preparations. Fifteen PVS impressions were made of the FDP preparations with defects in the mesial and distal margins; another set of 15 PVS impressions was made of FDP preparations with defects in the buccal and palatal margins for a total of 30 impressions. All impressions were digitized using the same extraoral scanner (E3, 3Shape, Denmark). Corresponding STL files were paired and merged, and a master cast was created by eliminating the defects using the scanned data. This master cast was compared to the reference cast using reverse engineering software (Geomagic, Morrisville, NC, USA). The results were expressed as average errors and standard deviations in the master casts relative to the reference cast. To account for the presence of positive and negative values in the data set, in terms of errors, the root mean square (RMS) value was calculated for each sample. RESULTS: The mean average error in the sample was -0.4 µm. The average upper limit of 95% confidence interval was +36.5 µm, while the average lower limit of 95% confidence interval was -37.3 µm. The mean RMS of the errors found was 18.9 µm. CONCLUSIONS: The results of this study indicated that merging digitized definitive impressions to correct marginal defects resulted in master casts with a high level of accuracy relative to the reference cast.
RESUMO
PURPOSE: The purpose of this in vitro study was to analyze the shear bond strength of composite resin to a commercially available high-performance polymer material for fixed, screw-retained full arch restorations. MATERIAL AND METHODS: A total of 135 computer-aided design and computer-aided manufacturing, high-performance polymer (HPP) blocks were cut and obtained from discs (Trilor 95, Harvest Dental, Brea, CA). The samples were 10 mm × 10 mm × 10 mm. The specimen surfaces were grouped as untreated (Group A), 50 µm Al2O3 (Group B), 110 µm Al2O3 (Group C), Rocatec (3 M, St. Paul, MN) activated with silica-modified alumina oxide treatment (Group D); and trimmed coarsely with a carbide bur (Group E). Group A samples were used as controls. After surface treatments, the specimens were gently cleansed with oil-free steam and alcohol wipes. Surface conditioning was performed on all physically treated samples. The manufacturer's recommendations were followed for bonding composite resin to the samples with light-cured Visio.link (Bredent, Chesterfield, UK). Cylinders were veneered with composite resins (diameter 5 mm, height 4 mm) and polymerized on the specimen surfaces through plastic tubes. Twenty-seven specimens were used for each testing group and aging tests were performed. The experimental samples were thermocycled. Shear bond strength and scanning electron microscopic tests were performed. Means and standard deviations were calculated. Statistical analysis was performed with post-hoc Tukey tests. RESULTS: Statistical analysis revealed that there was a significant difference between the groups (p<0.001). The highest shear bond strengths were achieved for the specimens bonded with Visio.link without physical surface treatments (270.47 MPa). The lowest bond strengths were found for specimen surfaces abraded with 110 µm Al2O3 (117.03 Mpa) CONCLUSIONS: The results of this laboratory study indicated that the specimens used with Visio.link as provided by the manufacturer had the highest shear bond strengths between the composite resin and high-performance polymer test specimens. Modifications of the high-performance polymer surfaces with carbide burs did not change bonding strengths with the composite materials.
RESUMO
STATEMENT OF PROBLEM: The Kois Dento-Facial Analyzer (KDFA) is used by clinicians to mount maxillary casts and to evaluate and treat patients. Limited information is available for understanding whether the KDFA should be considered as an alternative to an arbitrary facebow. PURPOSE: The purpose of this clinical study was to evaluate and compare maxillary casts mounted by using the KDFA with casts mounted by using the Panadent Pana-Mount Facebow (PMF) and a kinematic axis (KA) facebow. MATERIAL AND METHODS: Fifteen participants were enrolled in the study. Three maxillary impressions were made of each study participant. One cast from each study participant was mounted on an articulator by means of the KDFA, PMF, and KA. A standardized photograph of each mounting was made, and the condylar center-incisor distance and the occlusal and incisal plane angles were measured. A randomized complete block design analysis of variance (RCBD) (α=.05) and post hoc tests (Tukey-Kramer HSD) were used to evaluate the occlusal and incisal plane angles and the condylar center-incisor distance. RESULTS: Compared with the occlusal plane angle (OPA), the KDFA mounted the maxillary cast at an angle that was statistically lower than those of PMF and KA (P<.001). The KDFA and the PMF condylar center-incisor distances were both significantly greater than that of KA (P=.01). No differences were found between the incisal plane angle (IPA) on maxillary casts mounted with the KDFA, KA, or PMF (P=.16). CONCLUSIONS: The KDFA and PMF mounted the maxillary casts in a position that was farther from the axis when compared with the KA mounted casts. The KDFA resulted in a lower articulator OPA compared with both PMF and KA. No difference was found between the IPAs of the KDFA, PMF, and KA.
Assuntos
Articuladores Dentários , Maxila , Humanos , Fenômenos Biomecânicos , Oclusão Dentária , Registro da Relação Maxilomandibular/métodosRESUMO
STATEMENT OF PROBLEM: More translucent dental zirconias have been developed by incorporating the cubic phase and reducing the tetragonal phase content that undergoes transformation toughening, leading to reduced mechanical properties. Whether the clinically relevant mechanical property of the edge chipping toughness of the material is also reduced is unclear. PURPOSE: The purpose of this in vitro study was to evaluate the edge chipping toughness and translucency of translucent zirconia, 3mol% yttria-stabilized tetragonal zirconia polycrystal (3Y-TZP), and lithium disilicate. MATERIAL AND METHODS: Two translucent zirconia products, Katana and Lava Esthetic; one 3Y-TZP, Lava Plus; and one lithium disilicate, IPS e.max Press were prepared and tested for phase composition via X-ray diffraction (XRD) (n=3), translucency via a spectrophotometer (n=20), and edge chipping via a universal testing machine with a custom-machined specimen holder and diamond indenter (n=20). The 3Y-TZP and lithium disilicate served as the optimal control materials for edge chipping and translucency, respectively. Translucency was compared with 1-way ANOVA and edge toughness with ANCOVA (α=.05). RESULTS: The XRD showed the 3Y-TZP to be almost completely tetragonal phase compared with the 2 translucent zirconia products that were predominantly cubic. Katana UTML and IPS e.max Press had a statistically similar (P>.05) translucency that was significantly (P<.05) greater than that of Lava Esthetic and Lava Plus. The edge toughness of Katana UTML was 304 N/mm, IPS e.max Press was 354 N/mm, Lava Esthetic was 394 N/mm, and Lava Plus was 717 N/mm, with significance rankings of Katana UTMAssuntos
Materiais Dentários
, Estética Dentária
, Cerâmica/química
, Materiais Dentários/química
, Teste de Materiais
, Propriedades de Superfície
, Zircônio/química
RESUMO
STATEMENT OF PROBLEM: Soft-tissue attachment to different surfaces may play a pivotal role in the long-term success of dental implants. However, studies on the issue, especially on newer materials, are sparse. PURPOSE: The purpose of this in vitro study was to evaluate the viability and adhesion of human gingival fibroblasts (HGFs) on different implant abutment materials with specific surface modifications. MATERIAL AND METHODS: One hundred and fifty specimens in 6 experimental groups were evaluated: smooth-machined titanium alloy (Ti), laser-modified titanium (TiL), smooth-machined polyetheretherketone (PEEK) (P), laser-modified PEEK (PL), plasma-treated PEEK (PP), laser- and plasma-treated PEEK (PLP). Machined Ti was considered as the control group. Surface roughness (Sa), water contact angle (WCA), and X-ray photoelectron spectroscopy (XPS) were measured. HGF attachment and proliferation were observed at 1, 3, and 7 days after cell seeding. Comparison of the means among the groups was performed with 1-way analysis of variance (ANOVA) with post hoc comparison using the Tukey test (α=.05). RESULTS: Sa values of the laser modified groups were significantly higher than those of the nonmodified (smooth-machined) groups (P<.001). WCAs were significantly different among PEEK groups, and plasma-sprayed groups had the lowest WCAs. XPS analysis of both Ti and PEEK groups showed laser treatment did not have any significant effect on the surface composition of the PEEK as the same bonds with similar ratio/fraction were detected in the spectrum of the modified specimens. Scanning electron microscopy (SEM) revealed more functionally oriented HGF cells on the laser-grooved surfaces. On the first, third, and seventh day of proliferation, the titanium groups showed no significant differences (P>.05). On the first and third days of proliferation, the plasma sprayed groups (PP, PLP) showed significantly greater proliferation than all experimental groups (P<.001). On the seventh day of proliferation, statistically significant differences were observed between all PEEK groups and between all PEEK groups and the Ti group (P<.001), with the exception of the PL and P groups and the PLP and Ti groups (P>.05). CONCLUSIONS: Laser-modified titanium and PEEK surfaces led to guided gingival fibroblast attachment. Plasma treatment of PEEK surfaces increased the wettability of this polymer and improved proliferation of HGF.
Assuntos
Implantes Dentários , Titânio , Benzofenonas , Adesão Celular , Fibroblastos , Humanos , Cetonas , Microscopia Eletrônica de Varredura , Polietilenoglicóis , Polímeros , Propriedades de Superfície , ZircônioRESUMO
STATEMENT OF PROBLEM: Selective laser melting (SLM) technology has been introduced for printing metal dental restorations from Co-Cr base alloys or Au-Pt high noble alloys. However, information regarding the fit of restorations fabricated by using this technique is limited. PURPOSE: The purpose of this in vitro study was to determine the effect of 3 different finish line designs on the marginal and internal gaps of metal copings made from a base (Co-Cr), high noble (Au-Pd-Ag), and noble alloy (Co-Pd) by using the SLM technology. MATERIAL AND METHODS: Three Ivorine right maxillary central incisors were prepared with a chamfer, deep chamfer, or shoulder finish line. The preparations were scanned by using a TRIOS scanner, and a total of 90 dies were printed using DPR 10 Resin (30×3 finish line designs). Ten SLM copings were fabricated for each margin design and metal alloy combination for a total of 90 copings (10×3 finish line designs×3 alloys). Copings were cemented onto dies using an autopolymerizing composite-resin luting material. All coping-die assemblies were sectioned buccolingually by using a low-speed diamond saw, and images were obtained by using an inverted bright field metallurgical microscope at ×100 magnification. Marginal and internal gaps were measured at 5 locations: buccal margin, midfacial, incisal, midlingual, and lingual margin. After gap measurements, representative specimens were embedded in autopolymerizing resin and prepared for metallographic examination. A 2-way multivariate analysis of variance (MANOVA) was conducted to determine the overall significance, followed by ANOVA for each dependent variable (α=.05). RESULTS: The results indicated that alloy type and finish line had a significant influence on marginal gap of copings (P<.001). Relative to the internal gap, alloy type had a significant effect (P<.001), but the type of finish line had no statistically significant influence (P=.337). No statistically significant interactions occurred. Base alloys were printed with almost no observable porosity, whereas noble and high noble alloys exhibited hot tears and porosity. CONCLUSIONS: Thefinish line type did not influence the internal gap between copings and dies, whereas the alloy type influenced the marginal gap between copings and dies. SLM-fabricated Co-Cr copings on teeth prepared with a deep chamfer finish line demonstrated the lowest marginal gap.
Assuntos
Coroas , Adaptação Marginal Dentária , Adaptação Psicológica , Planejamento de Prótese Dentária , Impressão TridimensionalRESUMO
STATEMENT OF PROBLEM: Zirconia and lithium disilicate have been commonly used as materials for tooth-supported complete-coverage restorations. Adhesive and conventional cements have been suggested for cementation of these restorations. However, evidence on the effect of cement type on the clinical outcomes of teeth restored with zirconia or lithium disilicate restorations is unclear. PURPOSE: The purpose of this systematic review was to evaluate the clinical outcomes of teeth restored with zirconia or lithium disilicate restorations when adhesive or conventional cements are used. MATERIAL AND METHODS: This systematic review adopted the Preferred Reporting Items for Systematic Reviews and Meta-Analyses (PRISMA) statement and was registered at the international prospective register of systematic reviews (PROSPERO) (CRD42018096493). An electronic search was performed in 2 databases (MEDLINE-PubMed and Cochrane Central), and a manual search, from January 2008 through January 2018. The primary clinical question was framed according to the Problem/Patient/Population, Intervention/Indicator, Comparison, Outcome (PICO) approach. The following question was the primary clinical question: "For patients requiring a single tooth-supported complete-coverage ceramic restoration, does adhesive cementation, as compared with conventional cementation, improve the clinical performance and limit the complications of this restoration?" The search included articles published in peer-reviewed journals in English and was limited to randomized clinical trials and prospective and retrospective clinical studies. RESULTS: Seventeen clinical studies met the eligibility criteria and were included for qualitative analysis. Included studies had 1280 participants who received 2436 zirconia and lithium disilicate crowns. The survival rates for adhesively cemented zirconia crowns ranged from 83.3% to 100%, whereas those reported for conventionally cemented zirconia crowns ranged from 82.0% to 100%. Survival rates for adhesively cemented lithium disilicate crowns ranged from 83.5% to 100%, whereas the survival rate reported for conventionally cemented lithium disilicate crowns was 98.5%. Commonly reported clinical complications included fracture of the veneering ceramic, crown fracture, and loss of crown retention. The mean follow-up time ranged from 25.5 months to 121.2 months. The studies that were assessed for risk of bias showed poor quality of evidence. CONCLUSIONS: Based on the available evidence and within the limitations of this systematic review, zirconia and lithium disilicate tooth-supported crowns exhibited comparable survival rates and complication patterns after adhesive or conventional cementation.
Assuntos
Porcelana Dentária , Falha de Restauração Dentária , Coroas , Planejamento de Prótese Dentária , Humanos , Estudos Retrospectivos , Estados Unidos , ZircônioRESUMO
STATEMENT OF PROBLEM: Debonding is the most common complication of fiber-reinforced posts (FRPs). Airborne-particle abrasion (APA) has been suggested to increase resin cement adhesion to the surface of FRPs. However, which abrasion protocol is the most favorable is unclear. PURPOSE: The purpose of this in vitro study was to compare the surface roughness and characteristic failure load of three FRP systems following different APA protocols. MATERIAL AND METHODS: A total of 150 posts from 3 manufacturers (glass FRP, quartz FRP, and zirconia-enriched glass FRP) were randomly assigned to different surface treatments (NT: no treatment-control; E0: cleaned with 96% ethanol solution; E2: APA for 2 seconds/mm2-ethanol cleaned, E5: APA for 5 seconds/mm2-ethanol cleaned; and E10: APA for 10 seconds/mm2-ethanol cleaned) forming 15 groups in total. APA was performed with 50-µm aluminum oxide. Each post was observed under a 3-dimensional (3D) laser microscope, and average 3D surface roughness (Sa) was measured. Failure was induced with a universal testing machine. Two specimens per group were evaluated under the same microscope to evaluate failure patterns. Surface roughness data were analyzed with the Welch ANOVA (α=.05), followed by the post hoc Games-Howell test. Failure load differences were determined by 2-parameter Weibull statistics and likelihood ratio contour plots (95% confidence bounds). RESULTS: Statistically significant differences were found in the mean surface roughness among the groups (Welch ANOVA, P<.001). APA resulted in a significant surface roughness increase in all tested post systems. No surface roughness difference was found between surface treatments E2, E5, and E10 in any tested post systems. Weibull statistics and likelihood contour plots revealed a significant decrease in the characteristic failure load for glass FRP after surface treatment E2 (88.7 N) compared with the control (95.3 N). Quartz FRP showed a significant decrease in the characteristic failure load after surface treatment E5 (103.6 N) compared with the control (108.9 N). Zirconia-enriched glass FRP showed no significant decrease in the characteristic failure load after any of the tested surface treatments. Qualitative morphological changes and failure pattern differences were observed among the tested post systems after the different surface treatments. CONCLUSIONS: APA significantly increased surface roughness in all post systems. APA effects on characteristic failure load were dependent on the material used.
Assuntos
Colagem Dentária , Técnica para Retentor Intrarradicular , Resinas Compostas , Análise do Estresse Dentário , Teste de Materiais , Cimentos de Resina , Propriedades de Superfície , ZircônioRESUMO
STATEMENT OF PROBLEM: Research evaluating load-to-failure of pressed lithium disilicate glass-ceramic (LDGC) with a clinically validated test after adjustment and repair procedures is scarce. PURPOSE: The purpose of this in vitro study was to investigate the effect of the simulated chairside adjustment of the intaglio surface of monolithic pressed LDGC and procedures intended to repair damage. MATERIAL AND METHODS: A total of 423 IPS e.max Press (Ivoclar Vivadent AG) disks (15 mm diameter, 1 mm height) were used in the study. The material was tested by using an equibiaxial loading arrangement (n≥30/group) and a contact pressure test (n≥20/group). Specimens were assigned to 1 of 14 groups. One-half was assigned to the equibiaxial load test and the other half underwent contact pressure testing. Testing was performed in 2 parts, before glazing and after glazing. Before-glazing specimens were devested and entered in the test protocol, while after-glazing specimens were devested and glazed before entering the test protocol. Equibiaxial flexure test specimens were placed on a ring-on-ring apparatus and loaded until failure. Contact pressure specimens were cemented to epoxy resin blocks with a resin cement and loaded with a 50-mm diameter hemisphere until failure. Tests were performed on a universal testing machine with a crosshead speed of 0.5 mm/min. Weibull statistics and likelihood ratio contour plots determined intergroup differences (95% confidence bounds). RESULTS: Before glazing, the equibiaxial flexural strength test and the Weibull and likelihood ratio contour plots demonstrated a significantly higher failure strength for 1EC (188 MPa) than that of the damaged and/or repaired groups. Glazing following diamond-adjustment (1EGG) was the most beneficial post-damage procedure (176 MPa). Regarding the contact pressure test, the Weibull and likelihood ratio contour plots revealed no significant difference between the 1PC (98 MPa) and 1PGG (98 MPa) groups. Diamond-adjustment, without glazing (1EG and 1PG), resulted in the next-to-lowest equibiaxial flexure strength and the lowest contact pressure. After glazing, the strength of all the groups, when subjected to glazing following devesting, increased in comparison with corresponding groups in the before-glazing part of the study. CONCLUSIONS: A glazing treatment improved the mechanical properties of diamond-adjusted IPS e.max Press disks when evaluated by equibiaxial flexure and contact pressure tests.
Assuntos
Cerâmica/uso terapêutico , Porcelana Dentária/uso terapêutico , Prótese Dentária , Restauração Dentária Permanente/métodos , Força Compressiva , Adaptação Marginal Dentária , Reparação de Restauração Dentária/métodos , Resistência à Flexão , Humanos , Técnicas In VitroRESUMO
STATEMENT OF PROBLEM: Currently, dental articulators can recreate mandibular movements and occlusal contacts. However, whether virtual articulators can also provide information about occluding dental surfaces, functional movements, and the mandibular condyles is unclear. PURPOSE: The purpose of this in vitro study was to evaluate the occluding surfaces on dental casts obtained from a patient and approximate them to a hemispherical contact model. Both models were tested by digitizing the Dentatus ARL dental articulator. MATERIAL AND METHODS: A combination of photogrammetry and structure from motion methods were used to scan a Dentatus ARL articulator and representative dental casts. Using computer-aided engineering and finite element analysis, contact points and action vectors to the forces on occluding surfaces and condyles were obtained for cast and hemispherical models. This experiment was performed using centric occlusion and 3 different condylar inclinations. The Kruskal-Wallis 1-way analysis of variance on ranks test was used to allow all pairwise comparisons between condylar inclination and mechanical action vector values in each location (α=.05). RESULTS: Action vectors from the cast model and each location of the hemispherical model were calculated to show the mechanical consequences and the similarity among models. Overall, no significant differences were observed for action vectors (A20 versus A40 versus A60) at each location (dental cast/hemisphere, right condylar, and left condylar) in the analysis of dental casts and the hemisphere model (.382≤P≤.999). CONCLUSIONS: This study provided graphical information that may assist the dental professional in determining which occlusal contacts should be modified to attain condylar and balanced centric occlusion.
Assuntos
Articuladores Dentários , Oclusão Dentária Central , Registro da Relação Maxilomandibular/instrumentação , Modelos Dentários , Desenho de Equipamento , Análise de Elementos Finitos , Humanos , Processamento de Imagem Assistida por Computador , Técnicas In Vitro , Fotogrametria , Propriedades de SuperfícieRESUMO
In managing loose abutment screws, locating precisely the position of the screw access channel is difficult. This technique describes the use of cone-beam computed tomography (CBCT) and surgical guide planning software to locate the screw access channel with the intention of retrieving a loosened cement-retained implant-supported prosthesis. The method minimizes damage to the abutment crown assembly.
Assuntos
Tomografia Computadorizada de Feixe Cônico , Dente Suporte , Prótese Dentária Fixada por Implante/efeitos adversos , Falha de Restauração Dentária , Impressão Tridimensional , Tomografia Computadorizada de Feixe Cônico/métodos , Dente Suporte/efeitos adversos , Projeto do Implante Dentário-Pivô/efeitos adversos , HumanosRESUMO
This report describes a method for fabricating access openings for implant-supported complete fixed dental prostheses (ICFP) by using a dental milling machine and silicone putty matrix. The method can help clinicians achieve the accurate and precise fabrication of access openings for ICFPs without excessive grinding.
Assuntos
Prótese Dentária Fixada por Implante/microbiologia , Planejamento de Dentadura/métodos , Prótese Total , Humanos , Modelos DentáriosRESUMO
This article has been withdrawn at the request of the author(s) and/or editor. The Publisher apologizes for any inconvenience this may cause. The full Elsevier Policy on Article Withdrawal can be found at http://www.elsevier.com/locate/withdrawalpolicy.
RESUMO
BACKGROUND: To adequately perform rehabilitation of edentulous patients by a complete removable dental prosthesis (CRDP) is from basic interest to dentists to understand the morphologic changes caused by re-establishment of a physiologic jaw relationship. Anthropometric analyses of standardized frontal view and profile photographs may help elucidate such changes. MATERIAL AND METHODS: Photographs of 31 edentulous patients were compared in relaxed lip closure and after insertion of a CRDP in stable occlusion. 2232 anthropometric distances were raised. Eighteen anthropometric indices reflecting the perioral morphology and its integration in the vertical facial harmony were investigated. RESULTS: The intercanthal - mouth width index (p < 001), medial - lateral cutaneous upper lip height index (p = .007), lower vermilion contour index (p = .022), vermilion - total upper lip height index (p = .018), cutaneous - total upper lip height index (p=.023), upper lip - nose height index (p = .001), nose - upper face height index (p = .002), chin - mandible height index (p = .013), upper lip - mandible height index (p = .045), nose - lower face height index (p = .018), and nose - face height index (p = .029) showed significant pre- to post-treatment changes. CONCLUSIONS: The investigated anthropometric indices presented reproducible results related to an increase in occlusal vertical dimension. Their application may be helpful in assessment, planning, and explanation of morphologic effects of CRDPs on the perioral and overall facial morphology, which may helps to improve the aesthetic outcome
Assuntos
Humanos , Prótese Total , Boca Edêntula , Oclusão Dentária , Estética Dentária , Boca/anatomia & histologia , Antropometria , Registro da Relação Maxilomandibular/métodosRESUMO
STATEMENT OF PROBLEM: Two novel restorative materials, a polymer infiltrated ceramic network (PICN) and a resin nanoceramic (RNC), for computer-assisted design and computer-assisted manufacturing (CAD-CAM) applications have recently become commercially available. Little independent evidence regarding their mechanical properties exists to facilitate material selection. PURPOSE: The purpose of this in vitro study was to measure the edge chipping resistance and flexural strength of the PICN and RNC materials and compare them with 2 commonly used feldspathic ceramic (FC) and leucite reinforced glass-ceramic (LRGC) CAD-CAM materials that share the same clinical indications. MATERIAL AND METHODS: PICN, RNC, FC, and LRGC material specimens were obtained by sectioning commercially available CAD-CAM blocks. Edge chipping test specimens (n=20/material) were adhesively attached to a resin substrate before testing. Edge chips were produced using a 120-degree, sharp, conical diamond indenter mounted on a universal testing machine and positioned 0.1 to 0.7 mm horizontally from the specimen's edge. The chipping force was plotted against distance to the edge, and the data were fitted to linear and quadratic equations. One-way ANOVA determined intergroup differences (α=.05) in edge chipping toughness. Beam specimens (n=22/material) were tested for determining flexural strength using a 3-point bend test. Weibull statistics determined intergroup differences (α=.05). Flexural modulus and work of fracture were also calculated, and 1-way ANOVA determined intergroup differences (α=.05) RESULTS: Significant (P<.05) differences were found among the 4 CAD-CAM materials for the 4 mechanical properties. Specifically, the material rankings were edge chipping toughness: RNC>LRGC=FC>PICN; flexural strength: RNC=LRGC>PICN>FC; flexural modulus: RNC
Assuntos
Cerâmica/uso terapêutico , Materiais Dentários/uso terapêutico , Restauração Dentária Permanente/métodos , Nanoestruturas/uso terapêutico , Desenho Assistido por Computador , Planejamento de Prótese Dentária , Análise do Estresse Dentário , Humanos , Polímeros/uso terapêutico , Resistência à TraçãoRESUMO
STATEMENT OF PROBLEM: The Kois Dento-Facial Analyzer System (KDFA) is used by clinicians to mount maxillary casts and evaluate and treat patients. Limited information is available for understanding whether the KDFA should be considered as an alternative to an earbow. PURPOSE: The purpose of this study was to evaluate maxillary casts mounted using the KDFA with casts mounted using Panadent's Pana-Mount Facebow (PMF). Both articulation methods were compared against a lateral cephalometric radiograph. MATERIAL AND METHODS: Fifteen dried human skulls were used. Lateral cephalometric radiographs and 2 maxillary impressions were made of each skull. One cast from each skull was mounted on an articulator by means of the KDFA and the other by using the PMF. A standardized photograph of each articulation was made, and the distance from the articular center to the incisal edge position and the occlusal plane angle were measured. The distance from condylar center to the incisal edge and the occlusal plane angle were measured from cephalometric radiographs. Finally, the 3-dimensional position of each articulation was determined with a Panadent CPI-III. A randomized complete block design analysis of variance (RCBD) and post hoc tests (Tukey-Kramer HSD) (α=.05) were used to evaluate the occlusal plane angle and axis-central incisor distance. A paired 2-sample t test for means (α=.05) was used to compare the X, Y, and Z distance at the right and left condyle. RESULTS: The KDFA and PMF mounted the maxillary cast in a position that was not statistically different from the skull when comparing the occlusal plane angle (P=.165). Both the KDFA and the PMF located the maxillary central incisor edge position in a significantly different position compared with the skull (P=.001) but were not significantly different from each other. The 3-dimensional location of the maxillary casts varied at the condyles by approximately 9 to 10.3 mm. CONCLUSION: The KDFA mounted the maxillary cast in a position that was not statistically different from the PMF when comparing the incisal edge position and the occlusal plane angle. Both the KDFA and the PMF located the maxillary incisal edge position in a significantly different position compared with the anatomic position on dried human skulls.
Assuntos
Articuladores Dentários , Registro da Relação Maxilomandibular , Maxila/anatomia & histologia , Modelos Dentários , Cefalometria , Oclusão Dentária , Face/anatomia & histologia , Feminino , Humanos , Incisivo/anatomia & histologia , Masculino , Crânio/anatomia & histologiaRESUMO
STATEMENT OF PROBLEM: The inability to control die spacer thickness has been reported. However, little information is available on the congruency between the computer-aided design parameters for die spacer thickness and the actual printout. PURPOSE: The purpose of this study was to evaluate the accuracy and precision of the die spacer thickness achieved by combining computer-aided design and 3-dimensional printing technology. MATERIAL AND METHODS: An ivorine maxillary central incisor was prepared for a ceramic crown. The prepared tooth was duplicated by using polyvinyl siloxane duplicating silicone, and 80 die-stone models were produced from Type IV dental stone. The dies were randomly divided into 5 groups with assigned die spacer thicknesses of 25 µm, 45 µm, 65 µm, 85 µm, and 105 µm (n=16). The printed resin copings, obtained from a printer (ProJet DP 3000; 3D Systems), were cemented onto their respective die-stone models with self-adhesive resin cement and stored at room temperature until sectioning into halves in a buccolingual direction. The internal gap was measured at 5 defined locations per side of the sectioned die. Images of the printed resin coping/die-stone model internal gap dimensions were obtained with an inverted bright field metallurgical microscope at ×100 magnification. The acquired digital image was calibrated, and measurements were made using image analysis software. Mixed models (α=.05) were used to evaluate accuracy. A false discovery rate at 5% was used to adjust for multiple testing. Coefficient of variation was used to determine the precision for each group and was evaluated statistically with the Wald test (α=.05). RESULTS: The accuracy, expressed in terms of the mean differences between the prescribed die spacer thickness and the measured internal gap (standard deviation), was 50 µm (11) for the 25 µm group simulated die spacer thickness, 30 µm (10) for the 45 µm group, 15 µm (14) for the 65 µm group, 3 µm (23) for the 85 µm group, and -10 µm (32) for the 105 µm group. The precision mean of the measurements, expressed as a coefficient of variation, ranged between 14% and 33% for the 5 groups. CONCLUSIONS: For the accuracy evaluation, statistically significant differences were found for all the groups, except the group of 85 µm. For the precision assessment, the coefficient of variation was above 10% for all groups, showing the printer's inability to reproduce the uniform internal gap within the same group.
Assuntos
Desenho Assistido por Computador , Coroas , Adaptação Marginal Dentária , Planejamento de Prótese Dentária/instrumentação , Impressão Tridimensional , Desenho Assistido por Computador/normas , Coroas/normas , Humanos , Processamento de Imagem Assistida por Computador/métodos , Teste de Materiais , Modelos Dentários , Impressão Tridimensional/normas , Distribuição Aleatória , Cimentos de Resina/química , Propriedades de Superfície , Preparo Prostodôntico do Dente/instrumentaçãoRESUMO
STATEMENT OF PROBLEM: Little peer-reviewed information is available regarding the accuracy and reproducibility of digitally fabricated casts compared to conventional nondigital methods. PURPOSE: The purpose of this in vitro study was to compare the accuracy and reproducibility of a digital impression and cast fabrication with a conventional impression and cast fabrication. MATERIAL AND METHODS: Conventional impressions were made via a 1-step single viscosity technique with vinyl siloxanether material of a typodont master model, and conventional casts were cast from dental stone. Digital impressions were obtained with a digital scanner, and digital stereolithographic models were printed. The typodont and fabricated casts were digitized with a structured light scanner and saved in surface tessellation language (STL) format. All STL records were superimposed via a best-fit method. The digital impression and cast fabrication method was compared with the conventional impression and cast fabrication method for discrepancy, accuracy, and reproducibility. The Levene test was used to determine equality of variances, and a 1-way ANOVA was conducted to assess the overall statistical significance of differences among the groups (n=5, α=.05). RESULTS: No significant statistical difference was found between the digital cast and conventional casts in the internal area or finish line area (P>.05). In addition, there was no statistically significant difference between these 2 techniques for a fixed dental prosthesis or single crown (P>.05). However, statistically significant differences were observed for overall areas of the casts in terms of accuracy (P<.01) and reproducibility (P<.001). Digital impression and cast fabrication were less accurate and reproducible than conventional impression and cast fabrication methods. CONCLUSIONS: No statistically significant difference was found between the digital cast and conventional cast groups in the internal and finish line areas. However, in terms of the reproducibility and accuracy of the entire cast area, the conventional cast was significantly better than the digital cast.