RESUMO
Bio-derived materials are becoming increasingly sought-after as a sustainable alternative to petrochemical-derived polymers. In the present pilot-scale study, a hemicellulose-rich compression screw pressate, obtained from the pre-heating stage of thermo-mechanical pulping (TMP) of radiata pine, was purified by treatment with adsorbent resin (XAD7), then ultrafiltered and diafiltered at 10 kDa to isolate the high-molecular weight (MW) hemicellulose fraction (yield 18.4% on pressate solids), and, finally, reacted with butyl glycidyl ether to plasticise the hemicelluloses. The resulting light brown hemicellulose ethers (yield 102% on the isolated hemicelluloses) contained ca. 0.5 butoxy-hydroxypropyl side chains per pyranose unit and had weight- and number-average MWs of 13,000 Da and 7200 Da, respectively. The hemicellulose ethers may serve as raw material for bio-based products such as barrier films.
RESUMO
The mechanical performance of composites made from isotactic polypropylene reinforced with natural fibres depends on the interface between fibre and matrix, as well as matrix crystallinity. Sizing the fibre surface with nucleating agents to promote transcrystallinity is a potential route to improve the mechanical properties. The sizing of thermo-mechanical pulp and regenerated cellulose (Tencel™) fibres with α- and ß-nucleating agents, to improve tensile strength and impact strength respectively, was assessed in this study. Polarised microscopy, electron microscopy and differential scanning calorimetry (DSC) showed that transcrystallinity was achieved and that the bulk crystallinity of the matrix was affected during processing (compounding and injection moulding). However, despite substantial changes in crystal structure in the final composite, the sizing method used did not lead to significant changes regarding the overall composite mechanical performance.