Effect of Co-Surfactants on Properties and Bactericidal Activity of Cu2 O and Hybrid Cu2 O/Ag Particles.

Nanomaterials based on metal oxides, especially Cu2 O, have received much attention in recent years due to the many unique properties of the surface plasmon resonance they provide. The report presented the co-precipitation method, a simple preparation method to produce Cu2 O oxide particles. In addition, to improve the unique antibacterial properties of Cu2 O, a proposed method is to attach Ag nanoparticles to the surface of Cu2 O particles. The Cu2 O and Cu2 O-Ag particles were synthesized based on redox reactions using ascorbic acid (LAA) as a reducing agent. Moreover, in this experiment, two surfactants, polyethylene glycol 6000 (PEG 6000) and sodium dodecyl sulfate (SDS), were added during the manufacturing process to create particle samples and particle combinations with better properties than the original sample. Changes in the characteristics and properties of particle samples are determined by many different physical and chemical methods such as ultraviolet-visible spectroscopy (UV-Vis), infrared spectroscopy (IR), noise X-ray radiation (XRD), scanning electron microscope (SEM), dynamic light scattering (DLS), energy dispersive X-ray spectroscopy (EDS), and transmission electron microscopy (TEM). Finally, the activity against bacteria, including E. coli and S. aureus, was also tested using the agar well diffusion method to determine the zone of inhibition. The results improved the particle size value, which decreased by half to 200 nm when two additional surfactants, PEG and SDS, were added. In addition, the antibacterial ability has also been shown to increase significantly when the diameter of the bacterial inhibition zone increased significantly, reaching values of 20 mm (Cu2 O/Ag/SDS) and 32 mm (Cu2 O/Ag/PEG) for the E. coli bacterial strain. The initial test sample was only about 14 mm in size. The S. aureus bacterial strain also had a similar improvement trend after adding Ag to the Cu2 O surface with the appearance of two surfactants, SDS and PEG. The inhibition zone diameter values reached the optimal value at 36 mm in the Cu2 O/Ag/PEG particle combination sample compared to only the initial 26 mm in the Cu2 O particle sample. Finally, the particle samples are added to the acrylic emulsion paint film to evaluate the changes. Positive results were obtained, such as improvement in adhesion (1.22 MPa), relative hardness (240/425), and sand drop resistance (100 L/mil) in the Cu2 O/Ag/PEG particle combination sample, which showed the correctness and accuracy of the research.

Polypyrrole-based nanocomposites doped with both salicylate/molybdate and graphene oxide for enhanced corrosion resistance on low-carbon steel.

In this work, polypyrrole-based nanocomposites doped with graphene oxide, molybdate, and salicylate (PPy/GO/Mo/Sal) were synthesized via in situ electrochemical polymerization to enhance the anti-corrosion protection performance of polymer coatings. The morphology and structures of the coatings were characterized by SEM, EDX, FTIR, Raman spectroscopy, and XRD. The protection abilities of coatings against corrosion were investigated in 0.1 M NaCl solution with EIS potentiodynamic polarization, salt spray test, and open-circuit potential (OCP) measurements. The results showed that with the presence of both molybdate/salicylate and GO in the PPy matrix, the nanocomposite coating exhibited an excellent protection ability against corrosion for low-carbon steel, better than that with only GO as filler. Compared to the nanocomposites doped with only salicylate or salicylate/GO, the one doped with both molybdate/salicylate and GO exhibited the longest protection plateau (ca. 100 h) on the OCP-time curves with some fluctuation points known as the self-healing action of molybdate dopant. It also resulted in a decrease in the corrosion current (Tafel plots), a higher impedance (Bode plot), and a better protection performance in salt spray tests. In this case, the anti-corrosion ability of the coatings was provided through a barrier and self-healing mechanism.