Effectiveness of Cyanoacrylate in the Treatment of Dentin Hypersensitivity: A Systematic Review.

Objective: To compare the effectiveness of cyanoacrylate to other treatments or placebo in the management of dentin hypersensitivity (DH). Materials and Methods: The present review was organized based on the preferred reporting items for systematic reviews and meta-analysis (PRISMA) guidelines. The search aimed to answer the following question: is cyanoacrylate effective in the treatment of DH when compared to other treatments or placebo? The following databases were used: PubMed/MEDLINE, Scopus, BVS, Web of Science, Cochrane, Clinicaltrials.gov, Portal Periódicos Capes, Google Scholar, and manual search. The evaluation process started with the information collected from the selected articles according to the Consolidated Standards of Reporting Trials (CONSORT). Results: Two randomized and five nonrandomized clinical trials were analyzed in the qualitative synthesis. The studies presented different cyanoacrylate formulations, different scales for evaluating pain, and different methods for provoking a painful stimulus. Cyanoacrylate-based products reduce DH in shorter follow-up periods and this reduction persisted throughout the study. The results varied according to the methods used to stimulate the pain. Only two articles showed a low risk of bias and a high level of scientific evidence. Conclusion: Although there is a limited number of studies in the scientific literature with appropriate methodological quality, the available evidence proves the effectiveness of cyanoacrylate in the treatment of DH. Clinical Relevance. Cyanoacrylate is easy to access, effective, easily applicable, and a low-cost product with satisfactory results.

Composite resin reinforced with silk nanoparticles from Bombyx mori cocoon for dental applications.

The objective of this work was to evaluate the mechanical performance of Z350 resin composite modified with Bombyx mori cocoons silk nanoparticles for dental applications. Four experimental groups were analyzed G0% = Filtek Z350 resin composite (control); G1% = Filtek Z350 with 1% of silk nanoparticles; G3% = Filtek Z350 with 3% of silk nanoparticles; G5% = Filtek Z350 with 5% of silk nanoparticles. It was employed scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, 3-point flexural strength test, Knoop hardness test, and surface roughness. From 3-point flexural strength tests the control group presented the best results G0% = 113.33 MPa (±23.73). The higher flexural modulus was shown by groups G3% = 29.150 GPa (±5.191) and G5% = 34.101 GPa (±7.940), which are statistically similar. The Knoop microhardness test has shown statistical difference only among the G3% group between the top 80.78 (± 3.00) and bottom 68.80 (±3.62) and no difference between the groups. The roughness test presented no statistical difference between the groups. The incorporation of silk nanoparticles reduced the flexural strength of Z350 resin composite. The surface roughness and microhardness tests showed no changes in any of the groups studied.

Composite resin reinforced with silk nanoparticles from Bombyx mori cocoon for dental applications

Abstract The objective of this work was to evaluate the mechanical performance of Z350 resin composite modified with Bombyx mori cocoons silk nanoparticles for dental applications. Four experimental groups were analyzed G0% = Filtek Z350 resin composite (control); G1% = Filtek Z350 with 1% of silk nanoparticles; G3% = Filtek Z350 with 3% of silk nanoparticles; G5% = Filtek Z350 with 5% of silk nanoparticles. It was employed scanning electron microscopy, energy dispersive X-ray spectroscopy, X-ray diffraction, 3-point flexural strength test, Knoop hardness test, and surface roughness. From 3-point flexural strength tests the control group presented the best results G0% = 113.33 MPa (±23.73). The higher flexural modulus was shown by groups G3% = 29.150 GPa (±5.191) and G5% = 34.101 GPa (±7.940), which are statistically similar. The Knoop microhardness test has shown statistical difference only among the G3% group between the top 80.78 (± 3.00) and bottom 68.80 (±3.62) and no difference between the groups. The roughness test presented no statistical difference between the groups. The incorporation of silk nanoparticles reduced the flexural strength of Z350 resin composite. The surface roughness and microhardness tests showed no changes in any of the groups studied.

Resumo O objetivo deste trabalho foi avaliar o desempenho mecânico da resina composta Z350 modificada com nanopartículas de seda Bombyx mori cocoons para aplicações odontológicas. Quatro grupos experimentais foram analisados: G0%) Resina Z350 apenas (grupo controle); G1%) Reforço com 1% de nanopartículas de seda; G3%) Reforço com 3% de nanopartículas de seda; e G5%) Reforço com 5% de nanopartículas de seda. Foi empregado microscopia eletrônica de varredura, espectroscopia de energia dispersiva de raios X, difração de raios X, teste de resistência à flexão de 3 pontos, teste de dureza Knoop e rugosidade superficial. Nos testes de resistência à flexão de 3 pontos o grupo controle apresentou melhores resultados G0% = 0.113 GPa (±0.024). O maior módulo de flexão foi demonstrado pelos grupos G3% = 29.151GPa (±5.191) e G5% = 34.102 GPa (±7.94), que são estatisticamente semelhantes. O teste de microdureza Knoop mostrou diferença estatística apenas entre o grupo G3% entre os 80.78 superiores (± 3.00) e os 68.80 inferiores (±3.62). Não há diferença entre os grupos. O teste de rugosidade não apresentou diferença estatística entre os grupos. A incorporação de nanopartículas de seda reduziu a resistência à flexão da resina composta Z350. Os testes de rugosidade superficial e microdureza não apresentaram alterações em nenhum dos grupos estudados.