BACKGROUND: We aimed to investigate the effectiveness of docosahexaenoic acid (DHA) as a treatment for Achilles tendinopathy (AT) induced with type-I collagenase in rats and compare it with collagen. METHODS: The AT model was induced with type I collagenase, and animals were randomly assigned to groups. Group 1:AT, Group 2: Collagen (7.2 mg/kg/day), Group 3:DHA (300 mg/kg/day), and Group 4:DHA (100 mg/kg/day). Right tendons of Group1 were used as a healthy control (HC). Oral treatments were applied for eight weeks. Serum tumor necrosis factor-alpha(TNF-α), matrix metalloproteinase-13 (MMP-13), and interleukin-1 beta(IL-1ß) concentrations were determined by ELISA. Tendon samples were taken for histopathological evaluation and examined immunohistochemically with antibodies specific for Col1A1, TNF-α, MMP-13, IL-1ß, and nitric oxide synthase-2(NOS-2). The ultimate tensile force (UTF) yield force(YF) and stiffness were measured by biomechanical assessments. RESULTS: UTF,YF and stiffness values were increased in all treatment groups compared to the AT control, a significant increase was found in Group 2 (p < 0.05). There was severe degeneration of tendon cells in the AT control. The tendon cells in samples from Groups 2-3 were less degraded, and this was statistically significant (p < 0.05). TNF-α, MMP-13, IL-1ß, and NOS-2 expressions were significantly higher in the AT control compared to the HC. In all treatment groups, their concentrations were lower than in the AT control. Serum TNF-α, MMP-13, and IL-1ß levels were lower in all treatment groups (Especially in Group3 (p < 0.001)) compared to Group1. CONCLUSION: The efficacy of high-dose DHA as a treatment for AT was investigated from biochemical, histopathological, and biomechanical perspectives. The results showed that DHA could be an alternative treatment compound to collagen.

The effect of TiO2 coating on biological NiTi alloys after micro-arc oxidation treatment for corrosion resistance.

NiTi alloys exhibit good properties, such as shape memory behavior, high corrosion resistant, having the closest elasticity modulus of a human bone and superior biocompatibility properties. However, the surface problems that arise during the use of this alloy limit the usage in the industry and health sector. In recent years, micro-arc oxidation method is used to improve the surface properties and increase the usage of these alloys. In this study, the TiO2 coatings were deposited on the NiTi substrates. The surface topography, morphology, crystallographic structure, and thickness of the coatings were determined using scanning electron microscopy and X-ray diffraction. The corrosion properties were investigated using potentiostat test unit in two different media such as NaCl solution and simulated body fluid. The results show that the coated samples have higher corrosion resistance than uncoated samples in the two different media.