Embrittlement Fracture Behavior and Mechanical Properties in Heat-Affected Zone of Welded Maraging Steel.

In welded maraging steels, mechanical properties, particularly ductility and toughness, are often compromised in the heat-affected zone (HAZ). This study focuses on 300-grade maraging steel bars, solution annealed at 1123 K for 1.5 h (5.4 ks) and welded using gas tungsten arc welding, followed by a post-weld heat treatment at 753 K for 13.33 h (48 ks). In situ observations during three-point bending tests on HAZ samples featuring coarsened prior austenite grain sizes were conducted to examine damage behavior and the crack path near the crack tip. The main crack initiated at the peak applied load during the bending test and, upon further loading, exhibited significant deflection and extension accompanied by numerous microcracks and localized crack branching. Distinctive damage features, such as transgranular cracking across block regions, intense intergranular cracking along packet boundaries with a pronounced shear component, and crowding of microcracks ahead of the crack tip, were observed in the HAZ sample during the in situ test. The interaction between the main crack tip and microcracks and its influence on the local crack propagation driving force was discussed using fracture mechanics. Experimental results, including tensile fracture surface observations and in situ images, along with analysis of the stress anti-shielding effect by microcracks, suggest that the HAZ sample exhibits embrittlement fracture behavior with lower ductility and toughness compared to the base metal sample.

Tensile Examination and Strength Evaluation of Latewood in Japanese Cedar.

With the crisis awareness of global warming and natural disasters, utilization of local wood has drawn increasing attention in achieving the Sustainable Development Goals (SDGs). It is necessary to investigate the deformation and fracture of the structural tissue in wood in order to improve the safety and reliability of wood application. However, deformation and fracture mechanisms of the structural tissue in each annual ring are unknown. The mechanical characteristics of wood are reflected in the properties of earlywood and latewood. In the present study, microstructural observation and tensile tests were conducted to examine the relationship between the mechanical properties and fracture behavior of latewood in the growth direction in Japanese cedar. Brittle fracture behavior of the latewood specimen was confirmed based on the tensile stress-strain curve and features of the fracture surface. Moreover, two fracture modes, tensile fracture and shear fracture, were recognized. Weibull analysis of tensile strength in each fracture mode was performed to evaluate the reliability and utility of brittle latewood. Lastly, two fracture mechanisms were discussed based on the failure observation findings by a scanning electron microscope.